Transparent environment-friendly calcium zinc stabilizer and preparation method thereof

A calcium-zinc stabilizer and main stabilizer technology, applied in the field of transparent environment-friendly calcium-zinc stabilizer and its preparation, to achieve the effects of good heat resistance stability, simple preparation method, and good printability

Active Publication Date: 2012-01-18
嘉兴若天新材料科技有限公司
View PDF3 Cites 41 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it is difficult for most calcium-zinc composite stabilizer...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Transparent environment-friendly calcium zinc stabilizer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0062] First take 20Kg magnesium-aluminum binary hydrotalcite (MgO / AL in magnesium-aluminum binary hydrotalcite 2 o 3 The molar ratio is 4.0:1) and 20Kg zinc-magnesium-aluminum ternary hydrotalcite (ZnO / MgO / AL in zinc-magnesium-aluminum ternary hydrotalcite 2 o 3 The molar ratio is 2:4:2) into the high-speed mixer, the speed of the high-speed mixer is 1000 r / min, stirring at 55 ° C for 5 min; then continue to add 10Kg calcium stearate, 10Kg calcium benzoate, 10Kg stearin Zinc acid zinc, 10Kg zinc benzoate and 10Kg butyl stearate were stirred for 10 min at a speed of 1000 r / min and a temperature of 55°C; finally, 5Kg of β-(3,5-di-tert-butyl- 4-Hydroxyphenyl) n-octadecyl propionate, 2Kg dibenzoylmethane, 1Kg ethyl acetoacetate and 2Kg ultraviolet absorber UV-9, wherein the speed of the high-speed mixer is 1000 r / min, at 55 ℃ Stir for 15 min, and obtain a transparent and environmentally friendly calcium-zinc stabilizer after cooling.

Embodiment 2

[0064] First take 30Kg magnesium-aluminum binary hydrotalcite (MgO / AL in magnesium-aluminum binary hydrotalcite 2 o 3 The molar ratio is 4.5:1) and 20Kg zinc-magnesium-aluminum ternary hydrotalcite (ZnO / MgO / AL in zinc-magnesium-aluminum ternary hydrotalcite 2 o 3 The molar ratio is 4:2:2) into the high-speed mixer, the speed of the high-speed mixer is 1250 r / min, stirred at 60 ° C for 10 min; then continue to add 5Kg calcium benzoate, 5Kg pentacarbon fatty acid calcium, 5Kg laurel Zinc benzoate, 5Kg zinc benzoate, 5Kg butyl monostearate and 10Kg liquid paraffin, stirred for 10 min under the conditions of rotating speed 1250 r / min and temperature 60°C; finally added 5Kg tris[2.4-ditert- Butylphenyl] phosphite, 2Kg stearoylbenzoylmethane, 3Kg dehydroacetic acid and 5Kg ultraviolet absorber UV-327, wherein the speed of the high-speed mixer is 1250 r / min, stirring at 60 ° C for 10 min, After cooling, a transparent and environmentally friendly calcium-zinc stabilizer is obtained...

Embodiment 3

[0066] First take 20Kg magnesium-aluminum binary hydrotalcite (MgO / AL in magnesium-aluminum binary hydrotalcite 2 o 3 The molar ratio is 4.2:1) and 10Kg zinc-magnesium-aluminum ternary hydrotalcite (ZnO / MgO / AL in zinc-magnesium-aluminum ternary hydrotalcite 2 o 3 The molar ratio is 3:3:2) into the high-speed mixer, the speed of the high-speed mixer is 1500 r / min, stirring at 65 ° C for 5 min; then continue to add 20Kg heptadecanoic acid calcium, 10Kg dodecylbenzene calcium dodecylbenzenesulfonate, 5Kg zinc dodecylbenzenesulfonate, 15Kg zinc stearate, 5Kg glyceryl monostearate and 5Kg paraffin wax, stirring for 5 min at a speed of 1500 r / min and a temperature of 65°C; Finally, add 3Kg of tetra[β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester, 1Kg of acetylacetone, 1Kg of 2,3-pentanedione, and 2Kg of ultraviolet absorber UV-P and 3Kg ultraviolet absorber UV-320, wherein the rotating speed of the high-speed mixer is 1500 r / min, stirred at 65°C for 20 min...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of chemical stabilizers, in particular to a transparent environment-friendly calcium zinc stabilizer and a preparation method thereof. The transparent environment-friendly calcium zinc stabilizer is prepared from the following raw materials in percentage by mass: 10 to 30 percent of calcium salt main stabilizer, 10 to 30 percent of zinc salt main stabilizer, 30 to 50 percent of hydrotalcite, 10 to 20 percent of lubricant, 1 to 5 percent of antioxidant, 1 to 5 percent of ultraviolet absorber and 1 to 5 percent of auxiliary stabilizer. The preparation method for the transparent environment-friendly calcium zinc stabilizer comprises the following steps of: adding the raw materials into a high speed stirrer in three stages, jointly stirring at the temperature of between 55 and 56DEG C for 30 minutes, and making the rotating speed of the stirrer 1,000-1,500r/min. The prepared transparent environment-friendly calcium zinc stabilizer has high heatresistance, high transparency and copper rust resistance.

Description

technical field [0001] The invention relates to the technical field of chemical stabilizers, in particular to a transparent and environment-friendly calcium-zinc stabilizer and a preparation method thereof. Background technique [0002] Known heat stabilizers in the PVC industry mainly include lead salts, metal soaps, organotin, rare earth and Ca / Zn stabilizers, but the most widely used heat stabilizers are lead salts and metal soaps. Lead salt stabilizers are cheap and have good thermal stability effects, but they are highly toxic, seriously endangering human health and polluting the environment, and lead salt stabilizers have the disadvantage of being opaque. Organotin stabilizers not only have good transparency and thermal stability, but also have low toxicity. They are widely used in high-transparency polyvinyl chloride sheets, sheets, food, and pharmaceutical packaging, but they are expensive, and some products are more toxic in terms of toxicity. The control is comple...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08K13/02C08K5/098C08K5/42C08K3/22
Inventor 赖文华袁援卓
Owner 嘉兴若天新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap