Method for extracting vanadium from alkaline leaching solution containing vanadium stone coal

A technology of alkaline leaching solution and vanadium stone, applied in the direction of improving process efficiency, etc., can solve the problems of large acid, salt and energy consumption, long process flow, etc., and achieve the goal of improving vanadium extraction efficiency, simplifying process flow, and reducing environmental pollution Effect

Inactive Publication Date: 2012-01-18
NANTONG HANRUI IND
View PDF1 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This silicon removal method consumes a lot of acid, salt and energy
In order to increase the concentration of vanadium and re

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] 1. Crush the ore to 30 meshes, then make ore balls with a diameter of 8mm, and roast them at 850°C for 2 hours. The roasted ore balls are leached with NaOH solution (1mol / L) 0.8 times its mass to obtain leached ore pulp;

[0033] 2. Solid-liquid separation of ore pulp to obtain leaching liquid and leaching slag;

[0034] 3. The leaching solution obtained in the second step is pressed by the V contained in the solution. 2 o 5 Add 20% mass concentration of copper-iron reagent to 10 times the mass, fully stir, and place for ten minutes; the copper-iron reagent is N-nitroso-N-phenylhydroxylamine ammonium salt, molecular formula: C 6 h 9 N 3 o 2 ;

[0035] 4. The solution obtained in the third step is subjected to conventional solid-liquid separation, and the obtained precipitate is a vanadium compound, and the vanadium precipitation rate is 95%.

Embodiment 2

[0037] 1. Crush the ore to 60 meshes, then make ore balls with a diameter of 12mm, roast at 900°C for 2-3 hours, and leaching the roasted ore balls with NaOH solution (1.5mol / L) twice its mass to obtain leached pulp;

[0038] 2. Solid-liquid separation of ore pulp to obtain leaching liquid and leaching slag;

[0039] 3. The leaching solution obtained in the second step is pressed by the V contained in the solution. 2 o 5 Add 18% copper-iron reagent to 15 times the mass concentration, fully stir, and place for ten minutes; the copper-iron reagent is N-nitroso-N-phenylhydroxylamine ammonium salt, molecular formula: C 6 h 9 N 3 o 2 ;

[0040] 4. The solution obtained in the third step is subjected to conventional solid-liquid separation, and the obtained precipitate is a vanadium compound, and the vanadium precipitation rate is 96%.

Embodiment 3

[0042] 1. Crush the ore to 50 meshes, then make ore blocks with a diameter of 10mm, roast at 950°C for 2-3 hours, and leaching the roasted ore balls with NaOH solution (0.8mol / L) twice its mass to obtain leached ore pulp;

[0043] 2. Solid-liquid separation of ore pulp to obtain leaching liquid and leaching slag;

[0044] 3. The leaching solution obtained in the second step is pressed by the V contained in the solution. 2 o 5 Add 15% copper-iron reagent to 20 times the mass concentration, fully stir, and place for six minutes; the copper-iron reagent is N-nitroso-N-phenylhydroxylamine ammonium salt, molecular formula: C 6 h 9 N 3 o 2 ;

[0045] 4. The solution obtained in the third step is subjected to conventional solid-liquid separation, and the obtained precipitate is a vanadium compound, and the vanadium precipitation rate is 96%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a method for extracting vanadium from alkaline leaching solution containing vanadium stone coal. The method comprises the following steps of: smashing ore containing the vanadium stone coal, roasting at the temperature of 800-950 DEG C, leaching with alkaline solution with 0.7-2 times weight of the ore and mol concentration of 0.7-1.8mol/L after roasting is carried out, so as to obtain ore pulp; carrying out solid-liquid separation on the ore pulp to obtain leachate and leached slag; excessively adding cupferron with the mass concentration of 15-25% into the leachate obtained in the previous step, fully stirring, standing, and then carrying out solid-liquid separation on the obtained solution, wherein the obtained precipitate is namely vanadium compound. The method provided by the invention solves the problem of separating vanadium and silicon in the traditional alkaline method stone coal vanadium extracting leachate, two processes, namely silicon removal and ion exchange, in the traditional alkaline method vanadium extracting leachate are reduced, the alkaline method stone coal vanadium extracting process is greatly simplified, and vanadium precipitation rate is more than 95%, thus the method provided by the invention has a great market promotion prospect.

Description

technical field [0001] The invention relates to a process for extracting vanadium from vanadium-containing stone coal, which is suitable for all occasions where vanadium is directly extracted from vanadium-containing ores by using a blank roasting leaching solution. Background technique [0002] Vanadium extraction from stone coal usually refers to the industrial process of extracting vanadium compounds from vanadium-containing carbonaceous shale, vanadium-containing coal gangue, vanadium-containing clay ore, etc. [0003] In the past, the vanadium extraction process from stone coal was mainly divided into two major process routes, namely the roasting and leaching vanadium extraction process and the direct acid leaching vanadium extraction process. Roasting and leaching vanadium extraction process refers to the process in which the ore is oxidized and roasted at high temperature, and the low-valent vanadium is oxidized into pentavalent vanadium, and then wet leached to obtai...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22B3/12C22B3/44C22B1/02C22B34/22
CPCY02P10/20
Inventor 喻华葛广凯
Owner NANTONG HANRUI IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap