Normal-temperature color pavement cold paving material used in winter or high-cold areas and preparation technology thereof
A technology for cold feeding in alpine regions, applied in the field of cold feeding of colored pavement, to achieve the effect of not easy to fade, long storage time and easy to store
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0027] The raw materials used in the production of 106kg normal temperature cold patch material for winter or alpine regions are as follows:
[0028]
[0029] Its preparation process is as follows:
[0030] ① Preparation of material A: first clean up the stirring equipment, then add furfural extract oil with a weight of 2.23kg, styrene-butadiene-styrene block copolymer with a weight of 0.18kg, and a weight of 0.22kg Powder SBR, petroleum resin with a weight of 1.78kg, and pigment with a weight of 0.45kg. During the addition process, the stirring equipment kept stirring, and the above mixture was heated to 170°C, stirred at 170°C for 60 minutes and then sheared Prepare 4.86kg cementing material A material;
[0031] ② Preparation of material B: put solvent oil with a weight of 0.1104kg, Na with a weight of 0.006kg 2 SO 3 1-aminoethyl-2-heptadecyl imidazoline with a weight of 0.0036 is mixed and stirred to make 0.12kg modified solution B material, as a lubricant and a modif...
Embodiment 2
[0035] The raw materials used in the production of 106kg normal temperature cold patch material for winter or alpine regions are as follows:
[0036]
[0037] Its preparation process is as follows:
[0038]① Preparation of material A: first clean up the stirring equipment, then add furfural extract oil with a weight of 2.60kg, styrene-butadiene-styrene block copolymer with a weight of 0.14kg, and a weight of 0.15kg Powder SBR, petroleum resin with a weight of 1.56kg, and pigment with a weight of 0.38kg. During the addition process, the stirring equipment kept stirring, and the above mixture was heated to 170°C, stirred at 170°C for 60 minutes and then sheared Prepare 4.86kg cementing material A material;
[0039] ② Preparation of material B: put solvent oil with a weight of 0.1104kg, Na with a weight of 0.006kg 2 SO 3 1-aminoethyl-2-heptadecyl imidazoline with a weight of 0.0036 is mixed and stirred to make 0.12kg modified solution B material, as a lubricant and a modifi...
Embodiment 3
[0043] The raw materials used in the production of 106kg normal temperature cold patch material for winter or alpine regions are as follows:
[0044]
[0045] Its preparation process is as follows:
[0046] ① Preparation of material A: first clean up the stirring equipment, then add furfural extract oil with a weight of 2.45kg, styrene-butadiene-styrene block copolymer with a weight of 0.14kg, and a weight of 0.23kg Powder SBR, petroleum resin with a weight of 1.62kg, and pigment with a weight of 0.41kg. During the addition process, the stirring equipment kept stirring, and the above mixture was heated to 170°C, stirred at 170°C for 60 minutes and then sheared Prepare 4.86kg cementing material A material;
[0047] ② Preparation of material B: put solvent oil with a weight of 0.1104kg, Na with a weight of 0.006kg 2 SO 3 1-aminoethyl-2-heptadecyl imidazoline with a weight of 0.0036 is mixed and stirred to make 0.12kg modified solution B material, as a lubricant and a modif...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com