High-resistance polymer coating fluid

A high-molecular polymer, polymer technology, applied in the direction of starch derivative coatings, cellulose derivative coatings, coatings, etc., can solve the problems of difficult recycling and difficult processing of high-molecular materials, and reduce processing costs and preparation methods Simple, excellent oxygen barrier effect

Inactive Publication Date: 2012-03-21
GREATVIEW BEIJING TRADING CO LTD
View PDF2 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] For this reason, the technical problem to be solved by the present invention is that the existing polymer materials used as high barrier polymer coating solutions are difficult to process and difficult to recycle. Therefore, the present invention provides a mul...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] High barrier polymer coating solution includes the following components:

[0049] Polyvinyl alcohol PVOH 18wt%, its molecular weight is 13200, alcoholysis degree is 88wt%;

[0050] Nano silica 1wt%, specific surface area is 200m 2 / g;

[0051] Silane coupling agent KH-570 0.1%wt;

[0052] Acetic acid 0.32wt%;

[0053] Polyacrylic acid 0.32wt%, its molecular weight 5000;

[0054]Cross-linking agent 1.2wt%, described cross-linking agent is the mixture of boric acid and sodium borate, and its weight ratio is 1: 1;

[0055] Ethanol 5wt%;

[0056] Water 74.06wt%.

[0057] The preparation method of the above-mentioned high barrier polymer coating liquid is:

[0058] (1) Add 25 parts of PVOH with a molecular weight of 13200 and an alcoholysis degree of 88%wt to 75 parts of water at 92°C, stir at 500 rpm for 40 minutes to obtain a solution, cool to 30°C for use.

[0059] (2) The specific surface area of ​​25 parts is 200m 2 / g silicon dioxide, 2.5 parts of KH-570, 3.5 ...

Embodiment 2

[0063] High barrier polymer coating solution includes the following components:

[0064] Polyvinyl alcohol PVOH 10.5wt%, its molecular weight 75000, alcoholysis degree 99%wt;

[0065] Nano silicon dioxide 3.6wt%, specific surface area is 200m2 / g;

[0066] Silane coupling agent KH-570 0.05%wt;

[0067] Acetic acid 1.325wt%;

[0068] Polymethacrylic acid 1.2wt%, its molecular weight 5000;

[0069] Cross-linking agent 0.45wt%, described cross-linking agent is the mixture of boric acid and sodium borate, and its weight ratio is 1: 1;

[0070] Isopropanol 8wt%;

[0071] Water 74.875wt%.

[0072] The preparation method of the above-mentioned high barrier polymer coating liquid is:

[0073] (1) Add 20 parts of PVOH with a molecular weight of 75,000 and an alcoholysis degree of 99% wt to 80 parts of water at 92°C, stir at 800 rpm for 40 minutes to obtain a solution, cool to 30°C for later use;

[0074] (2) The specific surface area of ​​24 parts is 200m 2 / g silicon dioxide, 0...

Embodiment 3

[0078] High barrier polymer coating solution includes the following components:

[0079] Polyvinyl alcohol PVOH 10wt%, its molecular weight 75000, alcoholysis degree 99%wt;

[0080] Nano-alumina 7wt%, specific surface area is 200m 2 / g;

[0081] Acetic acid 1.18wt%;

[0082] Polymethacrylic acid 0.168wt%, its molecular weight 5000;

[0083] Cross-linking agent 0.5wt%, described cross-linking agent is the mixture of boric acid and sodium borate, and its weight ratio is 1: 3;

[0084] Isopropanol 11.72wt%;

[0085] Water 69.432wt%.

[0086] The preparation method of the above-mentioned high barrier polymer coating liquid is:

[0087] (1) Add 20 parts of PVOH with a molecular weight of 75000 and an alcoholysis degree of 99%wt to 80 parts of water at 95°C, stir at 800rpm for 40 minutes to obtain a solution, cool to 30°C for later use;

[0088] (2) The specific surface area of ​​25 parts is 200m 2 / g alumina, 3.5 parts of acetic acid, 0.6 part of 10000 molecular weight poly...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Specific surface areaaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-resistance polymer coating fluid which is prepared from the following components of: 6-18 percent by weight of water-soluble high polymer with high hydroxyl density, 0.45-1.2 percent by weight of cross-linking agent, 0-7 percent by weight of nano size metal oxide, 0.01-2.5 percent by weight of viscosity modifier, 0.1-6 percent by weight of polymer dispersant, 0-1.3 percent by weight of coupling agent, 1-28 percent by weight of drying regulator and 40-92.44 percent by weight of water. The multi-component environment-friendly coating fluid prepared in the invention has excellent oxygen resistant performance under the condition that a thinner coating is formed and simultaneously has the advantages of simple preparation process and stable performance.

Description

technical field [0001] The invention relates to a high-barrier polymer coating solution with high oxygen barrier properties after film formation. Background technique [0002] In the process of food storage and transportation, there are many factors that lead to food spoilage, among which the food spoilage is mainly caused by the contact between food and oxygen in the air. For liquid food, in order to improve the storage time and shelf life of the food, it is usually packaged with materials with high barrier properties to oxygen, and the package must have sufficient water resistance to prevent leakage of the contents. [0003] For water resistance, if you choose non-polar polymer materials such as polyolefins, including polyethylene, polypropylene, etc., a continuous mold with sufficient thickness can provide good water resistance; for oxygen with a small molecular diameter, you must use Strong polarity, high crystallinity, and high density materials can obtain low oxygen t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D129/04C09D103/02C09D103/04C09D101/02C09D101/08C09D7/12C09D5/00
Inventor 不公告发明人
Owner GREATVIEW BEIJING TRADING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager