Hot melt adhesive for steel plastic composite pipeline and production method of hot melt adhesive

A technology of steel-plastic composite and hot-melt adhesive, which is applied in the bonding between steel and plastic, and in the field of hot-melt adhesive for steel-plastic composite pipes. advanced questions

Inactive Publication Date: 2012-04-04
SHANDONG DONGHONG PIPE IND
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the price of hot melt adhesive for steel-plastic composite pipes for steel belt reinforced polyethylene spiral corrugated pipes on the market is relatively high, and the production process is complicated, which is not conducive to operation, and some products cannot be used for p

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0015] Example 1: The weight percentage of raw material components contained in it are: 95.75% high-density polyethylene, 1% maleic anhydride, 0.05% peroxide, 3% acetone, and 0.2% antioxidant.

[0016] The above-mentioned production method of hot melt adhesive for steel-plastic composite pipes includes:

[0017] Step 1: Add high-density polyethylene and antioxidant to the mixer, heat the maleic anhydride and peroxide to melt at the same time, stir for 2-7 minutes, and control the temperature in the mixer to 35℃-40℃;

[0018] Step 2: The cooling material obtained in step 1 is pelletized with a medium-shear combined twin-screw extruder granulator at an extrusion temperature of 170-180°C and a die temperature of 190-200°C; the hot pelletizer extrudes the material through a strand The water cooling method is used to cut the pellets to ensure that there is no moisture on the surface of the pellets.

[0019] The plastic particles prepared by the above method are used to pass the steel belt ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a hot melt adhesive for a steel plastic composite pipeline and a production method of the hot melt adhesive. The hot melt adhesive comprises the following raw materials in percentage by weight: 95 to 98 percent of high-density polyethylene, 0.9 to 2.0 percent of maleic anhydride, 0.02 to 0.2 percent of peroxide, 0.09 to 0.5 percent of antioxidant and 0.9 to 4.0 percent of solvent. The production method comprises the following steps of: adding the high-density polyethylene and the antioxidant into a mixing machine; controlling the temperature of a stirring machine to be between 35 and 40 DEG C and stirring for 2 to 7 minutes; and granulating by using an intermediate-speed cutting combined double-screw extrusion granulator, wherein the extruding temperature is between 170 and 180 DEG C and the temperature of a machine head is between 190 and 200 DEG C. The hot melt adhesive is used for solving the bonding problem between a steel belt and plastic during production of the steel plastic composite pipeline. Based on detection required indexes according to the industrial standard CJ/T225-2006, the peeling strength meets the standard; the ring flexibility is qualified; and the product is qualified after passing a sunlight insolation test. All the indexes meet the industrial standard.

Description

technical field [0001] The invention relates to a steel-plastic composite adhesive, in particular to a hot-melt adhesive for a steel-plastic composite pipe and a production method, and is especially suitable for solving the bonding between steel and plastic in the production of steel-belt-reinforced polyethylene spiral corrugated pipe products. Background technique [0002] At present, the price of hot melt adhesive for steel-plastic composite pipes for steel belt reinforced polyethylene spiral corrugated pipes on the market is relatively high, and the production process is complicated, which is not conducive to operation, and some products cannot be used for pipes with specifications exceeding 1000mm, resulting in ring flexibility of pipes. If the indicators are not up to standard, there will be a problem of detachment between the reinforcing rib and the matrix, and the steel strip and the plastic layer will easily appear when the pipe is exposed to the sun. Contents of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J123/06C09J11/06
Inventor 倪立营鞠恒山付辉林丙海单汝钢
Owner SHANDONG DONGHONG PIPE IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap