Environmentally-friendly laminating coating for aluminum capacitor shell and preparation method thereof

A green and environmentally friendly capacitor technology, applied in capacitors, coatings, electrical components, etc., can solve the problems of poor temperature resistance and high production costs, and achieve the effects of reasonable formula, increased service life, and heat resistance and wear resistance.

Inactive Publication Date: 2012-04-18
TONGLING XINTAI ELECTRIC APP & CAPACITOR
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In fact, this method only reduces the secondary pollution of chlorine-containing coating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] Example 1: Green environment-friendly capacitor aluminum shell film coating, the weight parts of its constituent raw materials are: comprise composition A and composition B, described composition A: 60 parts of polyethylene resins, 20 parts of ketones, 5 parts of polyethylene waxes, 15 parts of isopropanol and 10 parts of attapulgite; the composition B: 20 ​​parts of phenolic resin, 5 parts of polydimethylsiloxane, 5 parts of silane coupling agent, 5 parts of stearic acid, 5 parts of graphite powder Parts and 5 parts of tetramethylsilane.

[0012] The preparation method of green environment-friendly capacitor aluminum shell film coating comprises the following steps:

[0013] (1) Weigh each raw material according to the weight of the constituent raw materials, add polyethylene resin, ketone, polyethylene wax, isopropanol and attapulgite into the mixer, stir at room temperature for 30-45 minutes, and mix well to obtain composition A , then add phenolic resin, polydimet...

Embodiment 2

[0016] Example 2: Green environment-friendly capacitor aluminum shell film coating, the weight parts of its raw materials are: including composition A and composition B, the composition A: 70 parts of polyethylene resin, 30 parts of ketone, 10 parts of polyethylene wax, 25 parts of isopropanol and 15 parts of attapulgite; the composition B: 30 parts of phenolic resin, 10 parts of polydimethylsiloxane, 10 parts of silane coupling agent, 10 parts of stearic acid, 10 parts of graphite powder Parts and 10 parts of tetramethylsilane.

[0017] The preparation method of green environment-friendly capacitor aluminum shell film coating comprises the following steps:

[0018] (1) Weigh each raw material according to the weight of the constituent raw materials, add polyethylene resin, ketone, polyethylene wax, isopropanol and attapulgite into the mixer, stir at room temperature for 30-45 minutes, and mix well to obtain composition A , then add phenolic resin, polydimethylsiloxane, sil...

Embodiment 3

[0021] Example 3: Be coated with embodiment 1 and embodiment 2 green environment-friendly capacitor aluminum casing film-coated paint, wherein curing temperature, time and the capacitor film-coated aluminum casing technical index that gained film-coated aluminum casing are made are:

[0022] Example 1 Example 2 Curing temperature (°C) 206 215 Curing time (s) 60 60 Requirement index conform to conform to aspect ratio 2.7:1 3.1:1

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an environmentally-friendly laminating coating for an aluminum capacitor shell and a preparation method thereof. The environmentally-friendly laminating coating is mainly obtained by mixing and stirring a composition A and a composition B in composition raw materials in part by weight, wherein the composition A consists of polyethylene resin, ketone, polyethylene wax, isopropanol and attapulgite; and the composition B consists of phenolic resin, polydimethylsiloxane, a silane coupling agent, stearic acid, graphite powder and tetramethylsilane. The environmentally-friendly laminating coating has a reasonable formula, a simple preparation method and a good curing effect on the aluminum capacitor shell; a capacitor is protected effectively; and the obtained laminating coating has heat resistance and wear resistance performance, and contributes to prolonging the service life of the capacitor.

Description

technical field [0001] The invention relates to a capacitor casing and a chemical composition, in particular to a green and environment-friendly capacitor aluminum casing coating and a preparation method thereof. Background technique [0002] With the advancement of technology in the electronics industry, the manufacturing technology of electronic circuit boards has also made great progress. In order to reduce the size of electronic products and reduce consumption, electrolytic capacitors, as one of the general components on electronic circuit boards, are not only important for their temperature resistance, The requirements for breakdown resistance are getting higher and higher, and the smaller the occupied area, the better. The occupied area of ​​electrolytic capacitors should be small. First, the aluminum case of the capacitor should have a high aspect ratio, and the occupied area should be small if the diameter of the capacitor is small; It is easy to be damaged and the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D123/06C09D161/06C09D183/04C09D7/12H01G2/10
Inventor 孔祥新
Owner TONGLING XINTAI ELECTRIC APP & CAPACITOR
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap