Water-based white sealed primer and preparation method thereof

A sealing primer, white technology, applied in the direction of coating, etc., can solve the problems of not mentioning the sealing effect of wood coatings, not mentioning the effect of barium metaborate against tannic acid, etc., to achieve good sealing, excellent water resistance, environmental protection and the effect of less harm to humans and animals

Inactive Publication Date: 2012-04-18
BEIJING ZHANCHEN CHEM +2
View PDF7 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The Chinese patent publication number is CN1073701A, and the title is "acrylic acid (ester) powder coating". In the "nano anti-radon antibacterial latex paint", nano barium metaborate is used as an antibacterial additive; patent publication number CN101705039A discloses a high temperature resistant flame retardant antirust paint and its preparation method. The patent uses barium metaborate as a flame retardant A kind of antirust agent, none of the above patents mentions the anti-tannic acid effect of barium metaborate in the primer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based white sealed primer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] Example 1: Water-based white sealing primer A with anti-tannin properties

[0059] 1. Composition:

[0060] Element

Weight (kg)

CRAYMUL 2711

490

Busan 11-M1

80

DALPAD TM D.

25

Preventol D7F

2

Preventol A 21-D

5

BYK024

7

TEGO Dispers 760W

8

TS 6200

150

CC1500 calcium carbonate

120

BYK345

3

Ammonia

4

PUR62

2

Thixol 53L

1

Deionized water

103

[0061] 2. Preparation method:

[0062] 1) First mix 95kg deionized water with DALPAD TM D. PreventolD7F, PreventolA21-D, BYK024, TEGO Dispers 760W were weighed into the dispersing tank, and started stirring at a medium speed;

[0063] 2) Add TS 6200, CC1500 calcium carbonate and Busan 11-M1 under medium speed stirring (800 rpm, abbreviated as 800 rpm), and disperse at 1200 rpm for 15 minutes;

[0064] 3) Reduce the speed to 80...

Embodiment 2

[0066] Example 2: Water-based white blocking primer B with anti-tannin properties

[0067] 1. Composition:

[0068] Element

Weight (kg)

CRAYMUL 2711

450

Busan 11-M1

80

DALPAD TM D.

22

Preventol BIT 20N

2

Preventol A 14-D

5

TEGO810

6

TEGO Dispers 740W

9

R-706

150

CC1500 calcium carbonate

150

BYK345

3

Deionized water

116

Ammonia

3

PUR62

4

[0069] 2. Preparation method:

[0070] 1) First mix 105kg deionized water, DALPAD TM D. Weigh Preventol BIT 20N, Preventol A14-D, TEGO810, and TEGO Dispers 740W into the dispersing tank, and start stirring at a medium speed;

[0071] 2) Add R-706, CC1500 calcium carbonate and Busan 11-M1 under medium-speed stirring (850 rpm), and disperse for 15 minutes at 1200 rpm;

[0072] 3) Reduce the speed to 800 rpm, add CRAYMUL 2711 and BYK345 in turn, and...

Embodiment 3

[0074] Example 3: Waterborne White Sealing Primer C with Anti-Tannic Acid Properties

[0075] Preparation process is with embodiment 1, and difference is that each component of the water-based white sealing primer of the present embodiment is as follows:

[0076] Element

[0077] Adjust the pH to 9.6.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a water-based white sealed primer and a preparation method thereof. The water-based white sealed primer comprises the following components in part by weight: 350 to 600 parts of water-based resin and 50 to 100 parts of modified barium metaborate. The water-based white sealed primer provided by the invention has performance of sealing wood tannic acid and has a durable and good sealing effect after construction on the base material containing the tannic acid, nicotine blot and water-based pigment. Water-based white wood coating is coated on the primer, so the water-based white wood coating is not polluted by the pollutants and is not discolored, and the primer has high rubbing property, covering power and corrosion resistance and can prevent wood from being rotten and deteriorated.

Description

technical field [0001] The invention relates to the field of paint chemical industry, in particular to a water-based white sealing primer and a preparation method thereof. Background technique [0002] At present, white paint and white-based light-colored coating effects on the market have been recognized by consumers and have become the mainstream style in the decorative coating industry. White gives people the impression of purity, frankness and softness, and can remind people of holiness and innocence. White furniture, pure and elegant, reflects the distinctive style of the times, and white is the expression of a life philosophy. [0003] There are three kinds of conventional solvent-based paints commonly used at present: ordinary alkyd paint, polyurethane (PU) paint and nitro (NC) paint. Ordinary alkyd paints are prone to aging, cracking, and peeling off; polyurethane paints tend to turn yellow, and the decoration effect cannot last; while NC paints have low solid cont...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/00C09D7/12
Inventor 陈寿生王德华罗先平
Owner BEIJING ZHANCHEN CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com