Water hose for firefighting and preparation method thereof

A technology for fire-fighting water and hoses, which is used in the laying and maintenance of mechanical equipment, hoses, pipes, etc., can solve problems such as the unsatisfactory performance of fire-fighting hoses, and achieve the effects of not easy peeling, high adhesion strength, and long service life.

Active Publication Date: 2012-05-02
QUANZHOU SANXING FIRE FIGHTING EQUIP
View PDF6 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a fire hose and its preparation method, to overcome the defects that the performance of the existing fire hose is not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The fire hose includes an outer cylindrical braid and a rubber lining, and the rubber lining is made of the following raw materials in parts by weight:

[0026] Polyvinyl chloride 60 parts acrylate rubber 5 parts composite stabilizer 3 parts titanium dioxide 0.8 parts paraffin 0.5 parts white carbon black 15 parts activator 4 parts light calcium carbonate 45 parts plasticizer 19 parts binder 7.5 parts vulcanizing agent 3.5 2 parts of antioxidant.

[0027] Wherein, the composite stabilizer is a calcium-zinc composite stabilizer, the activator is stearic acid, the plasticizer is tributyl citrate, the vulcanizing agent is dicumyl peroxide, and the adhesive is adhesive A , the anti-aging agent is RD.

[0028] The preparation steps are as follows: first weave the cylindrical braided layer, and then make the rubber hose from the raw materials for preparing the rubber lining: first mix the other raw materials except the vulcanizing agent, put them into the internal mixer and ...

Embodiment 2

[0030] Polyvinyl chloride 50 parts acrylate rubber 4 parts composite stabilizer 2 parts titanium dioxide 0.5 parts paraffin 0.1 parts white carbon black 10 parts activator 3 parts light calcium carbonate 40 parts plasticizer 12 parts adhesive 5 parts vulcanizing agent 2 1 part antioxidant.

[0031] The composite stabilizer is a calcium-zinc composite stabilizer, the activator is organic zinc, the plasticizer is rubber plasticizer A, the vulcanizing agent is TMTD, the adhesive is adhesive A, and the anti-aging agent is NBC / octamine. (mass ratio 1:1).

[0032] The preparation steps are as follows: first weave the cylindrical braided layer, and then make the rubber hose from the raw materials for preparing the rubber lining: first mix the other raw materials except the vulcanizing agent, put them into the internal mixer and knead for 1min, then put in the vulcanizing agent and continue mixing Knead for 0.5min at a mixing temperature of 100°C. After the material is discharged fro...

Embodiment 3

[0034] Polyvinyl chloride 70 parts acrylate rubber 6 parts composite stabilizer 4 parts titanium dioxide 1.0 parts paraffin wax 1 part white carbon black 20 parts activator 5 parts light calcium carbonate 50 parts plasticizer 25 parts binder 10 parts vulcanizing agent 5 3 parts of antioxidant.

[0035] The composite stabilizer is a calcium-zinc composite stabilizer, the activator is a mixture of zinc oxide and zinc stearate with a mass ratio of 1:1, the plasticizer is ATBC, the vulcanizing agent is sulfur, and the adhesive is an adhesive A, Antiaging agent is BLE.

[0036] The preparation steps are as follows: first weave the cylindrical braided layer, and then make the rubber hose from the raw materials for preparing the rubber lining: first mix the other raw materials except the vulcanizing agent, put them into the internal mixer and knead for 3 minutes, then put in the vulcanizing agent and continue mixing After mixing for 1 minute, the mixing temperature is 130°C. After t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a water hose for firefighting and a preparation method thereof. The water hose for the firefighting comprises a cylindrical weaving layer at the outer layer and a rubber liner, wherein the rubber liner is prepared by the following raw materials: polyvinyl chloride, acrylic rubber, a compound stabilizer, titanium oxide powder, paraffin wax, white carbon black, an activator, light calcium carbonate, a plasticizer, a binder, a vulcanizing agent and an antioxidant. The water hose for firefighting, provided by the invention, has the advantages that: the high temperature resistance and high pressure resistance are achieved; the adhesive strength of the liner and the outer weaving layer is high so that the liner and the outer weaving layer are not easy to strip, aging resistance is provided; and the service life is long.

Description

technical field [0001] The invention relates to a fire hose and a preparation method thereof. Background technique [0002] With the awakening of people's safety awareness in daily life and the increase of safety accidents, fire fighting equipment is becoming more and more popular. Among them, the fire hose is a kind of hose used in fire fighting equipment to transport water or foam mixture for fire extinguishing. It uses high-strength synthetic fiber as the outer braided layer and rubber as the inner lining. Its performance is mainly determined by the rubber inner lining. . At present, there are mainly three kinds of materials for the rubber lining, natural rubber, ethylene propylene rubber and polyurethane rubber, each of which has advantages, but also has some shortcomings. Therefore, research and development a kind of corrosion-resistant, wear-resistant, high pressure-resistant, aging-resistant fire hose could adapt to the demand of the market. Contents of the inven...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): F16L11/08F16L1/12C08L27/06C08L33/04C08K13/02C08K3/22C08K3/36C08K3/26C08K3/06C08K5/14B29B7/02B29B7/30B29C35/06
Inventor 肖君岩
Owner QUANZHOU SANXING FIRE FIGHTING EQUIP
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com