A safety tire, high temperature resistance technology, applied in special tires, tire parts, rolling resistance optimization and other directions, can solve the problems of burning out of flame retardant components, tires without fire resistance and high temperature resistance, vehicle paralysis, etc., to achieve low cost and production technology Simple, fire-resistant effect
Inactive Publication Date: 2012-06-13
夏丽红
View PDF3 Cites 7 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
But at present, most of the fire trucks and special vehicles are equipped with tires that are basically not fire-resistant and high-temperature resistant, and can only be used for long-distance operations; some rubber has flame-retardant properties, but under the action of flames and high temperatures, its flame-retardant components If it burns out, the ordinary rubber material separated by it will be burned immediately, carbonized and smoked, and the vehicle will be paralyzed, seriously affecting personal life and environmental health and safety.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0008] The present invention is a material used for manufacturing fire-proof and high-temperature-resistant special safety tires, which consists of the following ingredients in parts by weight:
[0009]
[0010] A more preferred embodiment of the present invention is composed of the following components in parts by weight:
[0011]
[0012] The polyisoprene is selected from one of polyisoprene rubber IR565, IR LHIR70, IR560, and IR2200;
[0013] The silicone rubber is selected from one of GM300, GM500, 110-2, TSE270-7U, and 3150 in silicone rubber;
[0014] The white carbon black is selected from one of FINE-SIL365, FINE-SIL518, A130, and A150 in white carbon black;
[0015] The ceramic powder is selected from one of NAI, ZYBJ-1, JZA-103F, and XZS in ceramic powder;
[0016] The silicone oil is selected from one of 2294H, 201, 5036D, and KF-96-1000 in silicone oil; the antioxidant is compounds such as diphenylamine, p-phenylenediamine, and dihydroquinoline and derivati...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention discloses a material for manufacturing a fireproof and high temperature resistant special safety tire. The material comprises, by mass, 30-50 parts of polyisoprene, 20-30 parts of silicon rubber, 10-15 parts of white carbon black, 8-15 parts of ceramic powder, 8-10 parts of silicone oil, 0.5-2 parts of an antioxidant, and 0.5-2 parts of a toughening agent. According to the present invention, the material of the present invention is used for tire materials of special safety tires for fire fighting, fire scenes, and high temperature risk operations; the material of the present invention has characteristics of the ordinary tire rubber at the room temperature, and has characteristics of high temperature resistance, flame resistance, strong fire insulation, aging resistance and the like in the extremely hot environment; the preparation process of the material of the present invention is simple, the material can be recovered, and no pollution is generated.
Description
technical field [0001] The invention discloses a special material for manufacturing fireproof and high temperature resistant special safety tires. Background technique [0002] In some high-temperature environments such as fire scenes, expedition surveys, and even interstellar operations, people are more willing to conduct close-range and more effective surveys and operations without endangering their lives. However, most of the fire trucks and tires equipped with special vehicles basically do not have the characteristics of fire resistance and high temperature resistance, and can only work at long distances; Burn out, the common rubber material that is separated is burnt immediately carbonization smokes, and vehicle travels paralyzed, has a strong impact on personal life and environmental sanitation safety. Contents of the invention [0003] The object of the present invention is to invent a material for manufacturing fire-proof and high-temperature-resistant special saf...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/00C08L83/04C08L51/00C08K3/36B60C1/00
CPCY02T10/862
Inventor 夏华松夏康凯
Owner 夏丽红