Preparation method of compound zirconium oxide

A technology of zirconia and zirconia oxychloride, which is applied in the field of preparation of chemical materials, can solve the problems of poor mixing uniformity of composite zirconia materials and difficult control of crystal structure, and achieve excellent mechanical properties, controllable crystal structure, and uniform mixing good sex effect

Active Publication Date: 2014-04-16
GUANGDONG FENGHUA ADVANCED TECH HLDG
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the above technical problems, the technical problem solved by the present invention is to solve the problems of poor mixing uniformity and difficult control of crystal structure of composite zirconia materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of compound zirconium oxide
  • Preparation method of compound zirconium oxide
  • Preparation method of compound zirconium oxide

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] a. Control the concentration of the zirconium oxychloride solution before feeding to 0.3mol / L, and the concentration of ammonia to: 1.6mol / L;

[0011] b. Add ammonia droplets to the zirconium oxide solution to react, control the molar ratio of ammonia water to zirconium oxychloride to 2.0:1, control the reaction temperature to 55°C, control the flow rate to 1800L / h, and then keep the temperature constant for 1hr after the dripping of ammonia water, After the reaction is completed, zirconium hydroxide hydrogel is generated;

[0012] c. Wash the zirconium hydroxide hydrogel with deionized water, and obtain zirconium hydroxide colloid by pressure filtration;

[0013] d. Dry the zirconium hydroxide gel at 200 ℃, and then powder to obtain powdery zirconium oxide;

[0014] e. Mix powdered zirconia, yttrium oxide, and small materials, where the addition amount of yttrium oxide is 4.5%, the addition amount of small materials is 0.2%, and the mixing time is 5h;

[0015] f. After mixing, ...

Embodiment 2

[0018] a. Control the concentration of the zirconium oxychloride solution before feeding to 0.7mol / L, and the concentration of ammonia to: 2.4mol / L

[0019] b. Add ammonia droplets to the zirconium oxide solution to react, control the molar ratio of ammonia water to zirconium oxychloride to 3.0:1, control the reaction temperature to 70°C, control the flow rate to 2500L / h, and then keep the temperature constant for 2hr after the dripping of ammonia water, After the reaction is completed, zirconium hydroxide hydrogel is generated;

[0020] c. Wash the zirconium hydroxide hydrogel with deionized water, and obtain zirconium hydroxide colloid by pressure filtration;

[0021] d. Dry the zirconium hydroxide gel at 500 ℃, and then powder to obtain powdered zirconium oxide;

[0022] e. Mix powdered zirconia, yttrium oxide, and small materials, wherein the addition amount of yttrium oxide is 6.5%, the addition amount of small materials is 0.6%, and the mixing time is 10h;

[0023] f. After mixin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of compound zirconium oxide. The method comprises the following steps that: A, ammonia water is dripped into zirconium oxychloride solution for reaction, and zirconium hydroxide water sol is generated after the reaction completion; B, deionized water is used for washing the zirconium hydroxide water sol, and zirconium hydroxide colloid is obtained after press filtering; C, the zirconium hydroxide colloid is dried, and then, powdery zirconium hydroxide is obtained through powdery processing; D, yttrium oxide and auxiliary materials (one kind of materials or several kinds of materials from aluminum oxide, magnesium oxide and calcium oxide) are added into the powdery zirconium oxide to be mixed (through ball mill or stirring tank mixing), and after the mixing completion, the mixed materials are roasted for 2 to 3 hours at 950 to 1050 DEG C, and compound zirconium oxide powder is obtained. The method has the advantages that the scaled production method of high-performance compound zirconium oxide materials is obtained, the produced compound zirconium oxide materials have good uniformity, the specific surface area of products is controllable, and the crystal phase structure is controllable.

Description

technical field [0001] The invention relates to a method for preparing chemical materials, more specifically, the invention relates to a method for preparing composite zirconia. Background technique [0002] High-performance composite zirconia powder is the basic raw material for making zirconia special ceramics, optical communication devices, advanced refractory materials, and new energy materials. At present, the production capacity of domestic composite zirconia is low, and due to the large gap between quality indicators and imported products, it can only be used in relatively low-end industrial fields. [0003] Currently widely used composite zirconia ceramics generally adopt solid-phase sintering and liquid-phase mixed reaction processes. The former consumes a lot of energy and requires high equipment, while the latter is slightly lacking in the uniformity of mixing between the product zirconium and yttrium. Chinese patent application CN101100379A discloses a preparat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/48C04B35/626
Inventor 赵兴国蒋训莎刘艳丽林滟新聂晓明
Owner GUANGDONG FENGHUA ADVANCED TECH HLDG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com