Transparent high-hardness impact-resistant acrylonitrile butadiene styrene (ABS) plastic alloy composition

A technology of ABS plastic and high hardness, which is applied in the field of high-strength, transparent, impact-resistant ABS plastic alloy composition and ABS plastic alloy composition, which can solve the problems of transparency, impact resistance and heat resistance, and product Single performance, complex process and other problems, to achieve the effect of omitting surface coating, good toughness and good flow performance

Active Publication Date: 2012-07-04
SHANGHAI PRET COMPOSITES
View PDF2 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the disadvantages of these methods of producing transparent ABS by polymerization are that the process is complex, the process is long, and the product performance is single, which cannot effectively solve the contradiction between transparency, impact resistance and heat resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-4 and comparative example 1

[0031] Mix the dried SAN resin, PMMA resin, acrylate graft rubber and other additives according to the composition ratio in Table 1, and then add them to the twin-screw extruder (screw diameter 35mm, length-diameter ratio L / D=36) host in the barrel. The temperature control of each section of the main barrel (from the feeding port to the nozzle outlet) is 200°C, 220°C, 230°C, 230°C, 230°C respectively, and the twin-screw speed is 300 rpm. pellets to obtain the product. Above-mentioned product is injection molded into standard spline with plastic injection molding machine after being dried at 80 ℃ for 5 hours in blast oven, and injection molding temperature is 230 ℃. The injection-molded strips were placed at 50% relative humidity at 23°C for at least 24 hours before performance testing. The actual test results are shown in Table 1.

[0032] Table 1:

[0033] composition

[0034] As can be seen from Table 1, compared with the transparent ABS material (comparative e...

Embodiment 5-8 and comparative example 2

[0036] Mix the dried SAN resin, PMMA resin, acrylate graft rubber and other additives according to the composition ratio in Table 1, and then add them to the twin-screw extruder (screw diameter 35mm, length-diameter ratio L / D=36) host in the barrel. The temperature control of each section of the main barrel (from the feeding port to the nozzle outlet) is 200°C, 220°C, 230°C, 230°C, 230°C respectively, and the twin-screw speed is 300 rpm. pellets to obtain the product. Above-mentioned product is injection molded into standard spline with plastic injection molding machine after being dried at 80 ℃ for 5 hours in blast oven, and injection molding temperature is 230 ℃. The injection-molded strips were placed at 50% relative humidity at 23°C for at least 24 hours before performance testing. The actual test results are shown in Table 2.

[0037] Table 2:

[0038] composition

[0039] As seen from Table 2, when adopting the SAN (comparative example 2) that acrylonitrile...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
transmittivityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a transparent high-hardness impact-resistant acrylonitrile butadiene styrene (ABS) plastic alloy composition. The transparent high-hardness impact-resistant ABS plastic alloy composition comprises 30 to 50 weight parts of styrene-acrylonitrile resin, 30 to 50 weight parts of polymethacrylate resin and 10 to 30 weight parts of acrylic ester elastomer. The ABS plastic alloy composition prepared by the technical scheme has the advantages that: the ABS plastic alloy composition is transparent and has high toughness and high surface hardness; 2, the ABS plastic alloy composition is transparent and has high impact resistance and surface hardness, so surface coating can be saved; and 3, the ABS plastic alloy composition has high flowability, so filling formation of a large-sized die is facilitated. The ABS plastic alloy composition can be applied to shells of mobile phones, mobile digital video disc (DVD) electronic products, domestic appliances such as televisions, liquid crystal displays and the like and automobile instrument displays and the like.

Description

technical field [0001] The invention relates to an ABS plastic alloy composition, in particular to a transparent, high-strength, impact-resistant ABS plastic alloy composition, which belongs to the field of polymer materials. Background technique [0002] The light transmittance of the transparent ABS material can reach more than 85%, and its mechanical strength exceeds that of the same transparent MBS resin. At the same time, transparent ABS has excellent impact strength and notched impact strength, and even low temperature impact resistance is also very good; it also has high bending strength and surface hardness. Compared with other transparent resins (such as the fluidity of PC, the chemical stability of PMMA, and the impact resistance of SAN), transparent ABS has obvious advantages, so that transparent ABS is unique in new application fields. [0003] At present, the production process of transparent ABS is mainly emulsion grafting or bulk polymerization method, that i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L25/12C08L33/04C08L33/12C08L33/10C08L51/00
Inventor 陈永东纪效均张祥福周文
Owner SHANGHAI PRET COMPOSITES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com