Low-smell rigid-tough high-performance polypropylene composite material and preparation method thereof

A composite material, polypropylene technology, applied in the field of rigid tough high performance polypropylene composite materials and its preparation, can solve the problems of not considering the balance of rigidity and toughness of modified PP, comprehensive odor control is not effective, etc., to achieve good deodorization Effect, improvement of rigidity, effect of low odor

Inactive Publication Date: 2012-07-04
CHINA PETROLEUM & CHEM CORP
View PDF10 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0013] Patent US6376741 proposes substrates with odor control compositions including silica and zeolites, however, conventional odor control compositions are less effective in demonstrating overall odor control
[0014] Since the odor of modified PP is the result of the interaction of multi-component odors, the above-mentioned single method cannot completely solve this problem. It needs multiple ways and methods to work at the same time to hope to completely eliminate the odor and meet the development needs of automobiles and home appliances. ; and the above-mentioned patents did not consider the technical problem of the balance of rigidity and toughness of modified PP while solving the problem of odor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-smell rigid-tough high-performance polypropylene composite material and preparation method thereof
  • Low-smell rigid-tough high-performance polypropylene composite material and preparation method thereof
  • Low-smell rigid-tough high-performance polypropylene composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] The low odor rigid high performance polypropylene composite material of the present invention is prepared according to the following steps

[0054] ①.Ingredient pre-mixing

[0055] According to the proposed formula, accurately weigh 72 parts by weight of polypropylene QP83N, 7.5 parts by weight of toughening agent 8150 produced by DuPont, compound odor suppression (compounded by attapulgite:diatomite:zeolite=1:33:33:33) into) 2 parts by weight,

[0056] Antioxidant 1010 0.2 parts by weight, lubricant AC 0.3 parts by weight, pre-mixed for 5-20 minutes;

[0057] ②.Dry mixing, melt extrusion granulation

[0058] Place the pre-mixed raw materials in step 1 in a twin-screw side feeder, add active wollastonite whiskers 1250 mesh and 18 parts by weight by side feeding, and dry mix for 5 to 20 minutes; then melt Extrusion and granulation; process conditions are as follows:

[0059]

Embodiment 1～ Embodiment 10

[0061] According to the methods and steps of the examples, and according to the formula in Table 1, the low-odor rigid and tough high-performance polypropylene composite material of the present invention was prepared

[0062] Table 1

[0063]

[0064]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
melt flow indexaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention is a low-smell rigid-tough high-performance polypropylene composite material and a preparation method thereof. The composite material of the invention belongs to a polypropylene composition without chemical post-processing. The composite material of the invention comprises the following raw materials by weight: 60-85 parts of polypropylene, 14-15 parts of toughening agents, 5-30 parts of active mineral fillers, 0.5-3 parts of composite smell inhibitors, and 0.1-2 parts of routine additives. By using low-smell rigid-tough balanced basic resin, through filling of wollastonite whiskers and compounding, matching and optimization of various smell adsorbents, the prepared polypropylene composite material has less smell and good balance between rigidity and toughness. Wollastonite whiskers are added in a mode of lateral feeding, which avoids the damage of the wollastonite long-needle shape caused by screw strong shearing, and thus the prepared polypropylene composite material not only has increased rigidity, but also has basically non-influenced toughness. The preparation process is simple, and the production cost is low. The composite material is suitable for the manufacturing of automobile bumpers, instrument panels, engine fans, washing machine inner drums, and refrigerator drawers.

Description

technical field [0001] The invention relates to a low-odor rigid and tough high-performance polypropylene composite material and a preparation method thereof. Belongs to polypropylene compositions that have not been chemically post-treated. Background technique [0002] With the rapid development of household appliances and automobile industries, environmental protection, lightweight and functionalization have become the main trends in the development of these industries, and plastics and their composite materials have become their important structural and decorative materials. Polypropylene (PP) has been widely used in the automobile and home appliance industries due to its low density, high cost performance, excellent heat resistance, rigidity, corrosion resistance and easy processing. The fastest variety. [0003] However, due to the shortcomings of general PP, such as high shrinkage rate, poor product dimensional stability, easy warping deformation, poor low temperatur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L53/00C08L23/08C08K13/04C08K3/34C08K3/36C08K7/26C08K5/132B29C47/92B29C48/92
CPCB29C48/92B29C48/875B29C2948/92514B29C2948/9259B29C2948/92704B29C2948/92885B29C2948/92895
Inventor 李伟李超芹李丽李延亮唐岩陈智能
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap