High-Q value nickel and zinc ferrite with initial permeability of 70 and preparation method thereof

A technology of nickel-zinc ferrite and magnetic permeability, which is applied in the field of high-Q value nickel-zinc ferrite and its preparation, can solve the problems of low Q value, large core heating, large loss, etc., and achieves high Q value and improved The effect of high frequency Q value and good high frequency and low loss characteristics

Active Publication Date: 2012-07-25
TDG HLDG CO LTD
View PDF6 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When power inductors are used at high frequencies, especially at 5MHz to 10MHz, the performance of the device is often deteriorated due to the low Q value, large loss, and large core heating.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-Q value nickel and zinc ferrite with initial permeability of 70 and preparation method thereof
  • High-Q value nickel and zinc ferrite with initial permeability of 70 and preparation method thereof
  • High-Q value nickel and zinc ferrite with initial permeability of 70 and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0030] The present invention will be described below based on specific examples, but the present invention is not limited to these examples.

[0031] The high-Q nickel-zinc ferrite with an initial magnetic permeability of 70 of the present invention is manufactured by a traditional oxide method, and the specific steps are as follows:

[0032] (1) Mixing: perform dry mixing according to the ratio of the main components described in Table 1 (Example and Comparative Example), and the mixing time is 60 to 90 minutes;

[0033] (2) Pre-burning: pre-fire the mixed materials in a pusher kiln, the pre-fire temperature is controlled at 860±20°C, and the pre-fire time is 240~300 minutes;

[0034] (3) Grinding: Add auxiliary components to the main component calcined material obtained in the previous step according to Table 1 (Example and Comparative Example) and perform wet grinding. The grinding time is 90 to 120 minutes. After grinding, the slurry particles The diameter is controlled a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Curie pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to high-Q value nickel and zinc ferrite with the initial permeability of 70 and a preparation method thereof, which are suitable for a power inductor. The nickel and zinc ferrite comprises the following main ingredients calculated by the oxide: 47.0-49.0mol% of Fe2O3, 25.1-28.5mol% of NiO, 16.3-20.5mol% of ZnO, 4.3-7.5mol% of CuO, and also comprises the following auxiliary components: 0.1-0.2wt% of CaCO3, 0.8-1.3wt% of SiO2, 2-7wt% of LiFe5O8, 0.3-0.6wt% of Co2O3 and 0.8-1.3wt% of Bi2O3. The high-Q value nickel and zinc ferrite is prepared with an oxide method and is sintered under certain condition. The sintered product has the characteristics of high Q value within the high-frequency range of 5-10MHz, and is suitable for the requirement of high frequency and low loss of the ferrite material by the power inductor.

Description

Technical field [0001] The present invention is the field of soft magnet oxygen technology, which involves a high Q value nickel -zinc iron oxygen body and its preparation method with a starting magnetic guidance rate of 70. Background technique [0002] Nickel -zinc iron oxygen has the characteristics of high resistivity, high frequency, etc., so that it can be widely used in the fields of anticroxer electromagnetic interference, SMD (Surface Mount Devices), MLCI (Multiplayer Chop Inuctors), electronic transformers, high -power synthesizers and other fields.,Market prospects. [0003] As the device develops towards a higher frequency, higher requirements have been put on the performance of nickel -zinc soft magnet oxygen.The power induction is used at high frequency, especially at 5MHz ~ 10MHz. Often, due to the low Q value, the loss of the loss, the magnetic heart is more fever, which causes the performance of the device to deteriorate.In order to correspond to the requirements...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/26C04B35/622
Inventor 聂敏徐方舟孙蒋平申志刚
Owner TDG HLDG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com