A 1.10mm, oil shale technology, used in coke ovens, petroleum industry, preparation of liquid hydrocarbon mixtures, etc., can solve problems such as inability to handle small particle oil shale, waste of oil shale resources, and inability to use for oil refining, etc. Achieve the effect of high comprehensive utilization, less pollutant discharge, and significant economy

Inactive Publication Date: 2012-08-01
于炳正
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main reason is that most retort furnaces cannot process oil shale with small grains below 10mm, and are only suitable for processing shale with grains above 10mm. waste
However, some methods of refining small-grained oil shale below 10 mm in size by heating with solid heat carrier have complex processes, huge investment, and unstable operation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A. Preparation of oil shale cold-pressed balls:

[0023] a. Adhesive preparation:

[0024] Add 949.5‰ water into the iron stirring container according to the weight percentage. When the water temperature is 25°C-35°C, add 10‰ calcium humate, 40‰ kaolin, and 0.5‰ magnesium phosphate respectively, and heat up while stirring, and the temperature rises to 85 Between -95°C, react for 1-2 hours to prepare the adhesive;

[0025] b. Pressure ball forming:

[0026] Add 920kg of small grain oil shale below 10mm and 80kg of the above-mentioned binder into the stirred tank, stir evenly, enter into a briquette machine for pressing and molding, after molding, dry and dehydrate in a dryer (temperature 125°C-135°C, time 5 hours -7 hours) to make oil shale cold-pressed balls; the dried oil shale cold-pressed balls can withstand high temperature up to 1200℃, the diameter of cold-pressed balls is 20-150mm, and the strength is 80-180kg / cm2;

[0027] B. Oil shale cold-pressed ball refini...

Embodiment 2

[0034] A. Preparation of oil shale cold-pressed balls:

[0035] a. Adhesive preparation:

[0036] Add 949‰ water into the iron stirring container according to the weight percentage. When the water temperature is 25°C-35°C, add 30‰ calcium humate, 20‰ kaolin, and 1‰ magnesium phosphate respectively, and heat up while stirring, and the temperature rises to 85 Between -95°C, react for 1-2 hours to prepare the adhesive;

[0037] b. Pressure ball forming:

[0038]Add 850kg of small grain oil shale below 10mm and 150kg of the above-mentioned binder into the stirred tank, stir evenly and enter into a briquette machine for pressing and forming, and after forming, dry and dehydrate in a dryer (temperature 125°C-135°C, time 5 hours -7 hours) to make oil shale cold-pressed balls; the dried oil shale cold-pressed balls can withstand a high temperature of 1200°C, the diameter of cold-pressed balls is 20-150mm, and the strength is 80-180kg / cm2;

[0039] B. Oil shale cold-pressed ball ref...

Embodiment 3

[0041] A. Preparation of oil shale cold-pressed balls:

[0042] a. Adhesive preparation:

[0043] Add 949.2‰ water into the iron stirring container according to the weight percentage. When the water temperature is 25°C-35°C, add 20‰ calcium humate, 30‰ kaolin, and 0.8‰ magnesium phosphate respectively, and heat up while stirring, and the temperature rises to 85 Between -95°C, react for 1-2 hours to prepare the adhesive;

[0044] b. Pressure ball forming:

[0045] Add 900kg of small grain oil shale below 10mm and 100kg of the above-mentioned binder into the stirred tank, stir evenly, enter into the ball press machine for pressing and molding, after molding, dry and dehydrate in the dryer (temperature 125°C-135°C, time 5 hours -7 hours) to make oil shale cold-pressed balls; the dried oil shale cold-pressed balls can withstand a high temperature of 1200°C, the diameter of cold-pressed balls is 20-150mm, and the strength is 80-180kg / cm2;

[0046] B. Oil shale cold-pressed ball ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a 10mm-below granular oil shale cold-pressing sphere and a method for oil refining by adopting the same. The oil shale cold-pressing sphere is prepared by adding adhesives with weight percentage of 8-15 percent into 10mm-below granular oil shale, wherein the adhesives comprise the following components in percentage by weight: 10-30 thousandth of humic acid calcium, 20-40 thousandth of kaolin, 0.5-1 thousandth of magnesium phosphate, and the balance water. The method comprises the following steps of: feeding the oil shale cold-pressing sphere into a gas retort, cushioning and falling through two layers of baffles, increasing steps of heat supplying carried out by a central heat supply device in the gas retort and the like so as to carry out dry distillation to obtain an oil gas mixture, and carrying out oil refining through an oil recovery system and the like. The oil shale cold-pressing sphere has good resistance to high temperature and high mechanical strength, and is not easy to crush; the production period of the gas retort is effectively prolonged, and the working efficiency is improved; and the cold-pressing sphere is adopted for oil refining, so that the co-combustion amount is high, the heat stability is good, the hot and cold strength is high, the dry distillation effect is good, the oil extraction rate is higher, the pollutant emission is less, the space is saved, the secondary pollution is avoided, and the cost is low.

Description

[0001] Technical field: [0002] The invention relates to small-grained oil shale cold-pressed balls less than 10 mm in size and a method for refining oil using the same, and belongs to the technical field of comprehensive utilization of oil shale. Background technique: [0003] At present, most of the small-grained oil shale below 10mm is used as a low calorific value fuel for coal blending for combustion and power generation, and there is no use of small-grained oil shale below 10mm for carbonization and refining. The main reason is that most retort furnaces cannot process oil shale with small grains below 10mm, and are only suitable for processing shale with grains above 10mm. waste. However, some methods of refining small-grained oil shale below 10mm in size by heating with a solid heat carrier have complex processes, huge investment, and unstable operation. Invention content: [0004] The object of the present invention is to overcome the deficiencies of the above-m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C10B53/06C10B53/08C10B57/04C10G1/00
Inventor 于昊于炳正
Owner 于炳正
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap