A kind of aramid fiber reinforced resin-based stab-resistant composite material

A technology for reinforcing resin-based and aramid fibers, applied in the field of stab-resistant composite materials, can solve the problems of high porosity, poor wettability of aramid fibers, affecting the consistency of material quality, etc., achieving high strength and hardness, and good stab resistance. , the effect of strong design

Active Publication Date: 2016-03-23
SHANDONG NON METALLIC MATERIAL RES INST +1
View PDF6 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the poor wettability of the aramid fiber, the resin content of the anti-stab composite material prepared by this method is not uniform, there are white spots on the surface and inside of the material, and the inside of the material has a high void ratio, which affects the quality consistency of the material.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The area density is 200g / m 2 The aramid fiber plain weave was used as the reinforcing material, and the urethane-modified vinyl ester was used as the matrix material. The fiber content was 40%, and the tensile strength and shear strength were 434.6 and 225.6 MPa, respectively.

[0019] 12 layers of sheets of the same size are superimposed and constrained around the periphery to obtain the stab-resistant composite material with a laminated structure involved in the present invention, with an areal density of 4440g / m 2 , can effectively protect the puncture of 12J standard tool.

Embodiment 2

[0021] The area density is 300g / m 2 The aramid fiber plain weave fabric was used as the reinforcing material, and bisphenol A epoxy vinyl ester was used as the matrix material, the fiber content was 44.5%, and the tensile strength and shear strength were 411.5 and 223.2 MPa, respectively.

[0022] 9 layers of sheets of the same size are superimposed and constrained around the periphery to obtain the stab-resistant composite material with a laminated structure involved in the present invention, with an areal density of 6840g / m 2 , can effectively protect the puncture of 18J standard tool.

Embodiment 3

[0024] The area density is 410g / m 2 The aramid fiber wrinkle-free woven cloth is used as the reinforcing material, and the brominated modified vinyl ester is used as the matrix material. The fiber content is 47.8%, and the tensile strength and shear strength are 427.6 and 245.3 MPa, respectively.

[0025] 12 layers of the same size sheets are superimposed and constrained around the periphery to obtain the stab-resistant composite material with a laminated structure involved in the present invention, with an areal density of 8880g / m 2 , can effectively protect the puncture of 24J standard tool.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
shear strengthaaaaaaaaaa
shear strengthaaaaaaaaaa
shear strengthaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of an armored protecting material and relates to a human body protecting material technology, in particular to an anti-puncturing compound material. High strength and high modulus of aramid fiber plain cloth and high hardness of modified vinyl ester resin are utilized to resist the puncturing of a cutting tool. The aramid fiber reinforced resin based anti-puncturing compound material provided by the invention has an n-layer superposed structure of modified vinyl ester resin impregnated aramid fiber fabric sheet, wherein n is a natural number from 12-100; the surface density of the superposed structure is 4440-19000g / m<2>; the structure strength and hardness are high; the anti-puncturing property is excellent; the weight is light; the designability is strong; a shellproof effect is achieved; and the compound material is suitable for the field of human body protection and armoring protection.

Description

technical field [0001] The invention belongs to the technical field of armor protection materials, relates to the technology of human body protection materials, and particularly relates to a stab-resistant composite material. Background technique [0002] In the field of human protection, in addition to bulletproof requirements, it is also necessary to have protective functions for various knives, so it is necessary to use materials that have effective protective functions for various knives to design protective clothing. [0003] Materials with effective protection function for knives include metal plates, including steel plates, aluminum plates, titanium alloy plates and other metal alloy plates. [0004] Due to the large weight of the metal alloy plate, it is not easy to deform, and the wearing comfort is poor. The United States also invented a metal scale stab-proof material similar to fish scales, which has good conformability and significantly improved wearing comfort...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B32B27/04F41H1/02
Inventor 王慧军金子明李英建丁笑晖惠林海刘发杰李华曲英章杜国源
Owner SHANDONG NON METALLIC MATERIAL RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap