Titaniferous-spinel-added gunning mix for steel converter
A steel-making converter and spinel technology, which is applied in the field of gunning materials and gunning materials for steel-making converters, can solve the problems of poor corrosion resistance and erosion resistance, low use efficiency, and short service life, and achieve improved Anti-erosion and erosion resistance, improved production efficiency, and reduced production costs
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0064] Example 1
[0065] According to the performance index and particle size requirements of the raw materials, according to weight percentage, 50% magnesia, 5% titanium-containing spinel as aggregate, 10% titanium-containing spinel as matrix material, 21% magnesia fire clay, and cement 1.5%, silica powder 2%, clay 3%, sodium tripolyphosphate 0.5%, sodium hexametaphosphate 4%, borax 3%, add magnesia and titanium-containing spinel to the mixing equipment, and then sieve the borax Then add it together with the magnesium fire clay, and finally add sodium hexametaphosphate, sodium tripolyphosphate, cement, silica powder and clay powder. After fully mixing, the finished gunning material for steelmaking converter can be obtained after inspection and packaging.
Example Embodiment
[0066] Example 2
[0067] According to the performance index and particle size requirements of the raw materials, in weight percentage, 60% magnesia, 4% titanium-containing spinel as aggregate, 6% titanium-containing spinel as matrix material, 20% magnesia fire mud, cement 2%, silica powder 3%, clay 1%, sodium tripolyphosphate 1%, sodium hexametaphosphate 1%, borax 2%, first add magnesia and titanium-containing spinel to the mixing equipment, and then sieve the borax Then add it together with the magnesium fire clay, and finally add sodium hexametaphosphate, sodium tripolyphosphate, cement, silica powder and clay powder. After fully mixing, the finished gunning material for steelmaking converter can be obtained after inspection and packaging.
Example Embodiment
[0068] Example 3
[0069] According to the performance indicators and particle size requirements of the raw materials, in weight percentage, 53% magnesia, 6% titanium-containing spinel as aggregate, 8% titanium-containing spinel as matrix material, 20% magnesia fire clay, and cement 1.4%, silica powder 4%, clay 1.5%, sodium tripolyphosphate 0.1%, sodium hexametaphosphate 2%, borax 4%, first add magnesia, titanium-containing spinel to the mixing equipment, and then sieve the borax Then add it together with the magnesium fire clay, and finally add sodium hexametaphosphate, sodium tripolyphosphate, cement, silica powder and clay powder. After fully mixing, the finished gunning material for steelmaking converter can be obtained after inspection and packaging.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap