Refractory wall plate material and production method thereof

A production method and wall panel technology, which is applied in fire protection and building components, etc., can solve the problems of poor thermal insulation and heat insulation performance of external walls, low resource recycling rate, high production energy consumption, etc., to achieve simple construction and improve decoration efficiency , good compatibility effect

Active Publication Date: 2012-09-12
吴涛
View PDF7 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, 90% of my country's wallboard materials are solid clay bricks. Compared with similar foreign wallboard materials, its production energy consumption is about twice as high on average, but the thermal insulation and heat insulation performance of the external wall is 4 to 5 times

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0025] Example 1: The body board material of the firewall is made of three mixtures of A component, B component, and C component and bamboo sticks:

[0026] The A component is a mixed liquid of magnesium chloride, bamboo root water, ferrous sulfate and thickener; the weight ratio of each component: magnesium chloride 88kg, bamboo root water 5kg, ferrous sulfate 5kg, cement thickener 2kg; add water Prepared into a mixed solution with a weight concentration of 30%; component B is heavy magnesia; component C is a filler, composed of dry and crushed plant straw, fly ash or slag, and foam particles; weight ratio of component C For; plant straw 40kg, fly ash 50kg, foam particles 10kg. The bamboo skewers should be soaked in anti-insect and anti-mildew syrup (such as phosphoric acid and magnesium oxide mixture) for 2-5 hours; the radial size of the bamboo skewers is 6-10mm, and the length of the skewers is the same as the length of the board.

[0027] In the three-component mixture, the w...

Example Embodiment

[0047] Example 2: Component A: the weight ratio of each component: 96.5kg of magnesium chloride, 2kg of bamboo root water, 1kg of ferrous sulfate, 0.5kg of cement thickener; add water to prepare a mixture with a weight concentration of 30%;

[0048] B component: industrial magnesium oxide;

[0049] C component: 90kg slag, 10kg foam particles.

[0050] In the three-component mixture, the weight ratio of the A component, the B component, and the C component is 1:1.5:2; the bamboo sticks are evenly placed in the three-component mixture to form a solid board.

[0051] The curing time is 10 hours. I the same implementation 1.

[0052] The specific requirements for various raw materials are also the same as in Example 1.

[0053] The product of this example was tested according to the method specified in GB / T5464-1999, the temperature rise in the furnace was 5℃ (standard≤30℃), the continuous combustion time was 0 seconds (standard is 0 seconds), and the mass loss rate was 40.2% (standard≤50%)...

Example Embodiment

[0061] Example 3:

[0062] Component A: the weight ratio of its components, 92kg of magnesium chloride, 3.5kg of bamboo root water, 3kg of ferrous sulfate, 1.5kg of cement thickener; add water to prepare a mixture with a weight concentration of 40%;

[0063] B component: industrial magnesium oxide;

[0064] C component: 70kg of plant straw, 10kg of fly ash, 20kg of foam particles;

[0065] In the three-component mixture, the weight ratio of the A component, the B component, and the C component is 1:1.3:1.5; bamboo sticks are evenly placed in the three-component mixture to form a solid board.

[0066] Hardening time is 20 hours. I the same implementation 1.

[0067] The specific requirements for various raw materials are also the same as in Example 1.

[0068] No anti-halogen phenomenon occurred in the products of Examples 1, 2, and 3 during the production process.

[0069] The products of Examples 1, 2, and 3 did not produce anti-halogen phenomenon due to environmental degradation during ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a refractory wall plate material and a production method thereof. The refractory wall plate material comprises component A, component B and component C, wherein the component A is a mixed solution of magnesium chloride, bamboo root water, ferrous sulfate and thickening agent, the component B is magnesium oxide, and the component C is a mixed material of plant straws, pulverized coal ash, cinder and foam particles; the component A, the component B and the component C are mixed in a ratio of 1:(1-1.5):(1-2.0), and bamboo stickers are added to produce the material; and thebamboo stickers are soaked with insect-proofing mould-proofing liquid, the radial size of each bamboo sticker is between 6 and 10mm, the length of each bamboo sticker is the same as that of the plate, and the bamboo stickers are arranged in the plate at an interval of between 8 and 12cm. The refractory wall plate material and the wall plate have good fire-proofing, water-proofing and anti-corrosion performance, no anti-brine phenomenon, safety and environmental friendliness, no toxic or odor, can be mixed with conventional decoration materials, has high integration degree, good compatibility and lower cost.

Description

technical field [0001] The invention relates to a fire wall body board material, which is mainly used as a wall body. At the same time, it relates to a production method of the fire wall body plate material. Background technique [0002] At present, 90% of my country's wallboard materials are solid clay bricks. Compared with similar foreign wallboard materials, its production energy consumption is about twice as high on average, but the thermal insulation and heat insulation performance of the external wall is 4 to 5 times different. Heating energy consumption is about three times that of developed countries under the same conditions. At the same time, various walls generally have defects such as weak sealing performance, poor thermal insulation performance, high resource consumption, and low resource recycling rate. my country is a country that consumes a lot of energy, and it is also a country that is relatively poor and short of energy, and the waste of resources is serio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/32E04B1/94
Inventor 吴涛吴明贡彭正清
Owner 吴涛
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology