Borax antioxidant and preparation method thereof

An anti-oxidant and borax technology, applied in the direction of additives, petroleum industry, lubricating compositions, etc., can solve the problems of clogged nozzles, poor anti-oxidation performance and lubricating effect, agglomeration, etc., to prevent secondary oxidation, excellent performance, reduce Effect of rolling pressure and energy consumption

Active Publication Date: 2012-10-03
HUNAN JINHUA SCI & TECH GRP
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to prevent the capillary from being oxidized, the existing domestic continuous pipe mills use the method of blowing nitrogen and borax into the capillary or using borax antioxidants from foreign companies. Due to the simple formula of borax antioxidants, the use performance and comprehensive technology of the product are not considered. performance, resulting in agglomeration of the product in actual production and application, clogged nozzle, poor oxidation resistance and lubrication effect, resulting in abnormal production, steel pipe product quality, production efficiency, and economic benefits are greatly affected

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Prepare 100kg borax antioxidant, the component and weight of this antioxidant are:

[0039] Powdered anhydrous borax 35kg,

[0040] Anhydrous sodium sulfate 30kg,

[0041] Sodium metaaluminate 10kg,

[0042] Magnesium oxide 20kg,

[0043] Sodium phosphate 5kg.

[0044] Its preparation process is:

[0045] At room temperature, add powdered anhydrous borax to the reaction kettle, start stirring, then add anhydrous sodium sulfate and sodium metaaluminate, stir for about five minutes, then add magnesium oxide and dispersant sodium phosphate, stir for about 20 minutes After 1 minute, stop stirring.

[0046] technical indicators

[0047] Particle size ≥ 95% through 16 mesh sieve;

[0048] Moisture ≤2.0%;

[0049] During the use of the borax antioxidant, anhydrous borax, sodium metaaluminate and magnesium oxide are fused first to form a liquid oxide film of metaborax salt and metaaluminate. Under the mixture of dispersant and anhydrous sodium sulfate, the liquid antio...

Embodiment 2

[0051] Prepare 100kg borax antioxidant, the component and weight of this antioxidant are:

[0052] Powdered anhydrous borax 40kg,

[0053] Anhydrous sodium sulfate 10kg,

[0054] Sodium metaaluminate 30kg,

[0055] Magnesium oxide 10kg,

[0056] Sodium phosphate 10kg.

[0057] Its preparation process is:

[0058] At room temperature, add powdered anhydrous borax to the reaction kettle, start stirring, then add anhydrous sodium sulfate and sodium metaaluminate, stir for about five minutes, then add magnesium oxide and dispersant, stir for about 20 minutes , stop stirring.

[0059] technical indicators

[0060] Particle size ≥ 95% through 16 mesh sieve

[0061] Moisture ≤1.0%

[0062] During the use of the borax antioxidant, anhydrous borax, sodium metaaluminate and magnesium oxide are fused first to form a liquid oxide film of metaborax salt and metaaluminate. Under the mixture of dispersant and anhydrous sodium sulfate, the liquid antioxidant film of metaborax salt an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a borax antioxidant. The borax antioxidant comprises the following components in weight percentage: 20 to 40% of powdery anhydrous borax, 15 to 30% of anhydrous sodium sulfate, 10 to 30% of sodium aluminate, 5 to 10% of MgO and 5 to 10% of dispersing agent. A preparation method of the borax antioxidant comprises the following steps: adding the powdery anhydrous borax into a reaction kettle at room temperature; stirring; adding the anhydrous sodium sulfate and the sodium aluminate; after stirring for about five minutes, adding the MgO and the dispersing agent; and stirring for about twenty minutes later, and stopping stirring. The borax antioxidant is suitable for rolling different materials and has the characteristics of no pollution, strong oxidation resistance and good chemical stability and physical stability.

Description

technical field [0001] The invention relates to a borax antioxidant and a preparation method thereof Background technique [0002] During the continuous (hot rolling) pipe rolling unit rolling seamless steel pipes at high temperature, the inner wall of the capillary tube will be oxidized after piercing and rolling, and the generated oxide scale will cause deep scratches on the inner wall of the steel pipe. In order to prevent the capillary from being oxidized, the existing domestic continuous pipe mills use the method of blowing nitrogen and borax into the capillary or using borax antioxidants from foreign companies. Due to the simple formula of borax antioxidants, the performance and comprehensive technology of the product are not considered. performance, resulting in the actual production and application of the product often agglomerated, clogging the nozzle, poor oxidation resistance and lubrication effect, resulting in abnormal production, steel pipe product quality, pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C10M125/00C10M125/26C10N30/10C10N30/06C10N40/24
Inventor 唐鹏飞
Owner HUNAN JINHUA SCI & TECH GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap