Artificial sub-gloss high temperature resistant and tip winding resistant polyester hair and its preparation method

A technology of artificial hair and high temperature resistance, applied in the direction of single-component polyester rayon, rayon manufacturing, rayon heat treatment, etc., can solve the problems affecting the comfort and aesthetics of wigs, and the lack of high temperature resistance and anti-tail entanglement performance. and other problems, to achieve the effect of delicate and smooth hand feeling, good gloss and excellent curling.

Inactive Publication Date: 2012-10-17
POLY WELL NANTONG IND
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In modern life, the use of wigs is more and more accepted by fashion lovers. As the raw material of wigs, artificial hair directly affects the comfort and aesthetics of wigs; There is a certain guarantee, but its high temperature resistance and tail winding resistance are lacking

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] a. Dry the PET at 160°C, and control the moisture after drying at 40-50ppm; b. Dry the above-mentioned 100 (weight) parts of PET and 7 parts of PET matting masterbatch, 0.5 parts of titanium dioxide, and 1 part of vinyl Put bis stearamide and 0.15 parts of silicon dioxide in a closed mixing tank and mix well; c. Pass the uniformly mixed mixture in step b through a screw extruder and melt and extrude it at 250-300°C to form a spinning silk melt; d. the above-mentioned spinning melt enters the spinning box, and then is extruded through a metering pump and a 170-hole spinneret, and is cooled by side blowing in the wire passage; e. , after oiling and drafting 4 times to obtain the raw silk; f. After the raw silk drawn in step e is heat-set through a heat setting device, a matt type high temperature resistant and anti-tail tangle polyester artificial Hair; heat styling treatment temperature 200°C.

Embodiment 2

[0023] a. Dry PET and PBT separately at 160°C, and control the moisture after drying at 40-50ppm;

[0024] b. Put 70 (weight) parts of PET, 30 parts of PBT and 6 parts of PET matting master batches, 1.5 parts of titanium dioxide, 1 part of silicone resin, and 0.15 parts of magnesium hydroxide in a closed mixing tank after drying, and mix them well uniform;

[0025] c. Pass the homogeneously mixed mixture in step b through a screw extruder and melt and extrude it at 250-300°C to form a spinning melt; d. The above-mentioned spinning melt enters the spinning box, and then passes through a metering pump 1. The spinneret of 170 holes is extruded, and is cooled by side blowing in the wire passageway; e. the obtained step d is oiled and drawn 5 times to obtain the original silk; f. after step e is drawn After the raw silk is heat-set by a heat-setting device, a matte type of high-temperature-resistant and anti-tangle polyester artificial hair is obtained; the temperature of heat-set...

Embodiment 3

[0027] a. Dry PET and PBT separately at 180°C, and control the moisture after drying at 40-50ppm;

[0028] b. Put 60 (weight) parts of PET, 40 parts of PBT and 5 parts of PET matting master batches, 2.5 parts of titanium dioxide, 1.5 parts of dioctyl phthalate, and 0.15 parts of meerschaum after drying above into a closed mixing tank c. Pass the uniformly mixed mixture in step b through a screw extruder, and melt and extrude it at 250-300°C to form a spinning melt; d. The above spinning melt enters the spinning box body, then extruded through a metering pump and a spinneret with 170 holes, and cooled by side blowing in the wire passageway; e. the obtained in step d, oiled and drawn 4 times to obtain the original silk; f. After the raw silk drawn in step e is subjected to heat setting treatment by a heat setting device, a matt type high temperature resistant and anti-tangle polyester artificial hair is obtained; the temperature of the heat setting treatment is 220°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Artificial sub-gloss high temperature resistant and tip winding resistant polyester hair mainly comprises a polyester, a delustering agent, organic particles and inorganic particles. A production method of the artificial sub-gloss high temperature resistant and tip winding resistant polyester hair comprises the steps of slice drying, mixing, screw fusion extrusion, oiling, drafting, winding, high temperature heat shaping and the like. The delustering agent used in the invention is a mixture of PET delustring master batches and titanium dioxide.

Description

technical field [0001] The invention belongs to the field of artificial hair production, and in particular relates to a matt type high temperature resistant and anti-tangle polyester artificial hair and a preparation method thereof. Background technique [0002] In modern life, the use of wigs is more and more accepted by fashion lovers. As the raw material of wigs, artificial hair directly affects the comfort and aesthetics of wigs; There is a certain guarantee, but its high temperature resistance and tail entanglement resistance are lacking. Contents of the invention [0003] The purpose of the present invention is to provide a matte high temperature resistant and anti-tangle polyester artificial hair, which has good gloss, excellent curling property, high temperature resistance, light texture, fine and smooth hand feeling. [0004] Another object of the present invention is to provide a method for preparing matte high temperature resistant polyester artificial hair, sp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/92D01F1/10A41G3/00D01D1/04D01D5/12D01D10/02
Inventor 李珉世王建华王荃
Owner POLY WELL NANTONG IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap