Lightweight plastic-wood composite sheet and preparation method thereof

A wood-plastic composite material and board technology, which is applied in the field of light-weight plastic-wood composite board and its preparation, can solve the problems of inability to absorb toxic and harmful gases, inconvenient transportation, installation and maintenance, and high density of plastic-wood composite materials. The effect of light weight, low cost and low production cost

Inactive Publication Date: 2013-12-04
江苏森诺塑胶科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, conventional wood-plastic composite materials are dense, heavy, and inconvenient for transportation, installation, and maintenance. At the same time, they cannot absorb toxic and harmful gases in the environment. They are generally only used for outdoor flooring. The use of the place has been greatly limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] PVC plastic particles 100kg, wood flour (80 mesh) 35kg,

[0053] LDPE-g-GMA 10kg, hollow glass beads (120 mesh) 4kg,

[0054] Baking soda 4kg, Citric acid 2kg,

[0055] Chlorinated polyethylene 3kg, tribasic lead sulfate 6kg,

[0056] Ethylene bis stearic acid amide 2kg, butyl stearate 1.5kg,

[0057]A kind of preparation method of light plastic-wood composite material board of the present invention, it comprises the following steps:

[0058] (1) Weigh each raw material according to the formula quantity;

[0059] (2) Add polyvinyl chloride plastic particles and tribasic lead sulfate into the stirring tank, and mix mechanically at 80°C for 15 minutes;

[0060] (3) Add wood powder, LDPE-g-GMA, hollow glass beads, chlorinated polyethylene, ethylene bisstearic acid amide and butyl stearate to the above stirring tank, heat up to 125°C, and stir After 15 minutes, the temperature of the stirred tank was lowered to 40°C, and the mixture was taken out from the stirred tank;...

Embodiment 2

[0063] PVC plastic particles 100kg, wood flour (60 mesh) 30kg,

[0064] LDPE-g-GMA 5kg, hollow glass beads (100 mesh) 2kg,

[0065] Baking soda 2kg, citric acid 1kg,

[0066] Chlorinated polyethylene 2kg, tribasic lead sulfate 4kg,

[0067] Ethylene bis stearic acid amide 1kg, butyl stearate 1kg,

[0068] A kind of preparation method of light plastic-wood composite material board of the present invention, it comprises the following steps:

[0069] (1) Weigh each raw material according to the formula quantity;

[0070] (2) Add polyvinyl chloride plastic particles and tribasic lead sulfate into the stirring tank, and mix mechanically at 70°C for 10 minutes;

[0071] (3) Add wood powder, LDPE-g-GMA, hollow glass beads, chlorinated polyethylene, ethylene bisstearic acid amide and butyl stearate to the above stirring tank, raise the temperature to 115°C, and stir After 10 minutes, the temperature of the stirred tank was lowered to 30°C, and the mixture was taken out from the s...

Embodiment 3

[0074] PVC plastic particles 100kg, wood flour (100 mesh) 40kg,

[0075] LDPE-g-GMA 15kg, hollow glass beads (140 mesh) 6kg,

[0076] Baking soda 6kg, citric acid 3kg,

[0077] Chlorinated polyethylene 4kg, tribasic lead sulfate 8kg,

[0078] Ethylene bis stearic acid amide 3kg, butyl stearate 2kg,

[0079] A kind of preparation method of light plastic-wood composite material board of the present invention, it comprises the following steps:

[0080] A kind of preparation method of light plastic-wood composite material board of the present invention, it comprises the following steps:

[0081] (1) Weigh each raw material according to the formula quantity;

[0082] (2) Add polyvinyl chloride plastic particles and tribasic lead sulfate into the stirring tank, and mix mechanically at 90°C for 20 minutes;

[0083] (3) Add wood powder, LDPE-g-GMA, hollow glass beads, chlorinated polyethylene, ethylene bisstearic acid amide and butyl stearate to the above stirring tank, raise the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
densityaaaaaaaaaa
impact strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a lightweight plastic-wood composite sheet and a preparation method thereof. The preparation method comprises the following steps of: firstly stirring PVC particles and tribasic lead sulfate evenly in a stirred tank, and then adding wood flour, LDPE-g-GMA, hollow glass beads, chlorinated polyethylene, ethylene bisstearamide and hard fatty acid butyl ester to the tank, heating up and stirring evenly, cooling and taking out the mixture, and then stirring the mixture evenly with baking soda and citric acid at room temperature, extruding out and molding. The lightweight plastic-wood sheet has the advantages of convenient production and manufacture, high degree of mechanization in the production process, low production cost, low density, light weight, easy installation and maintenance, less use of timber and plastic, turning waste into treasure, being recyclable and not destroyed by insects, no aging and discoloration as well as cracking, no buckling deformation and high impact strength, with the function of adsorbing gas. The lightweight plastic-wood sheet can be applied to a plurality of occasions such as office buildings, hotels and home offices, can be made into products such as photo frames, picture frames, foot lines, and hoisting and fastening boards, and can also be used as suspended beams, pergolas, and the like.

Description

technical field [0001] The invention relates to a plastic-wood composite material, in particular to a light-weight plastic-wood composite material board and a preparation method thereof. Background technique [0002] In the fields or places such as decoration and garden corridors, various boards are often used in large quantities. Commonly used boards include wood, aluminum alloy, stainless steel, plastic, gypsum and other boards, but wooden boards are prone to moisture, mildew, and insects during use. or cracking, etc.; aluminum alloy plates are poorly modifiable, easy to deform, etc.; stainless steel plates are poorly modifiable, feel bad, bulky, expensive, etc.; plastic plates are prone to aging and discoloration, low strength, etc.; Reproducibility, etc. The existence of these defects often limits the use range and service life of these plates. [0003] Wood-plastic composite materials use hot-melt plastics, including polyethylene, polypropylene, polystyrene, etc., and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06C08L97/02C08L51/06C08L23/28C08K13/04C08K7/20C08K3/30C08K5/20C08K5/101
Inventor 不公告发明人
Owner 江苏森诺塑胶科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com