Anti-crease finishing process of cotton fabric after dyeing

An anti-wrinkle finishing and cotton textile technology, which is applied in textiles and papermaking, fabric surface trimming, fiber treatment, etc., can solve the problems that are not easy to prevent, and achieve the effects of increased wrinkle recovery angle, soft hand feeling and excellent air permeability

Inactive Publication Date: 2012-10-24
SHAOXING UNIVERSITY
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Easing shrinkage can be slightly removed through relaxation treatment during fabric processing or continuous compression finishing in the final process, but it is not easy to prevent shrinkage caused by yarn bulking because it is the nature of cellulose fibers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] An anti-wrinkle finishing process for cotton textile fabrics after dyeing, comprising the following steps: drying the bad cloth after dyeing, first adding a specified amount of clear water into the reactor, then adding a finishing agent, stirring continuously, and adjusting the pH value to 5.5 , after the complete reaction, start sizing and rolling liquid, and then carry out crosslinking, baking, cleaning, softening, dehydration, smoothing and softening agent, tenter heat setting, inspection and packaging; the finishing agent is composed of citric acid, maleic anhydride, Nano-TiO 2 Configured, and citric acid, maleic anhydride, nano-TiO 2 The percentage by weight of each is 70%, 22%, and 8% respectively, and the percentage by weight of the finishing agent in clear water is 20%.

[0016] For the baking process, the baking temperature is controlled at 130-170°C, the baking time is 3-4min, the liquid extrusion rate is 80-90%, the speed is 10m / min, and the baking process i...

Embodiment 2

[0018] An anti-wrinkle finishing process for cotton textile fabrics after dyeing, comprising the following steps: drying the bad cloth after dyeing, first adding a specified amount of clear water into the reactor, then adding a finishing agent, stirring continuously, and adjusting the pH value to 5 , after the complete reaction, start sizing and rolling liquid, and then carry out crosslinking, baking, cleaning, softening, dehydration, smoothing and softening agent, tenter heat setting, inspection and packaging; the finishing agent is composed of citric acid, maleic anhydride, Nano-TiO 2 Configured, and citric acid, maleic anhydride, nano-TiO 2 The percentage by weight of each is 80%, 15%, and 5% respectively, and the percentage by weight of the finishing agent in clear water is 40%.

[0019] For the baking process, the baking temperature is controlled at 130-170°C, the baking time is 3-4min, the liquid extrusion rate is 80-90%, the speed is 12m / min, and the baking process is ...

Embodiment 3

[0021] An anti-wrinkle finishing process for cotton textile fabrics after dyeing, comprising the following steps: drying the bad cloth after dyeing, first adding a specified amount of clear water into the reactor, then adding a finishing agent, stirring continuously, and adjusting the pH value to 6 , after the complete reaction, start sizing and rolling liquid, and then carry out crosslinking, baking, cleaning, softening, dehydration, smoothing and softening agent, tenter heat setting, inspection and packaging; the finishing agent is composed of citric acid, maleic anhydride, Nano-TiO 2 Configured, and citric acid, maleic anhydride, nano-TiO 2 The percentage by weight of each is 75%, 20%, and 5% respectively, and the percentage by weight of the finishing agent in clear water is 30%.

[0022] For the baking process, the baking temperature is controlled at 130-170°C, the baking time is 3-4min, the liquid extrusion rate is 80-90%, the speed is 11m / min, and the baking process is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-crease finishing process of cotton fabric after dyeing, belonging to the technical field of a fabric dyeing and finishing process. The anti-crease finishing process comprises the steps of drying dyed grey fabric, adding clean a specified amount of water into a reactor, then adding a finishing agent, stirring continuously, adjusting the PH value to be 5-6, reacting completely, then sizing and rolling liquid, crosslinking, baking, cleaning, softening, dewatering, coating a smooth softening agent, stentering and hot-sizing, checking and packaging, wherein, the finishing agent is prepared from the following components by weight percent: 70-80% of citric acid, 15-25% of maleic anhydride and 5-8% of nano TiO2, and meanwhile, 20-40% of the finishing agent is contained in clean water. The cotton fabric processed by the anti-crease finishing process disclosed by the invention has soft handfeeling, is smooth, and extremely good in air permeability and has a strong anti-contraction and anti-crease capability.

Description

technical field [0001] The invention discloses an anti-wrinkle finishing process for dyed cotton fabrics, belonging to the technical field of dyeing and finishing processes for textile fabrics. Background technique [0002] Because cellulose fiber has excellent water absorption, hygroscopicity, moderate strength and easy dyeing, it is the main material for underwear and shirts, especially natural fibers such as cotton and hemp. But fabrics made from these natural fibers inevitably crease and shrink when washed. At the same time, the regenerated cellulose fiber that appeared in the early 20th century, due to its low wet strength and the shrinkage and wrinkles during washing exceeded the allowable limit, made the creases and shrinkage during washing more serious. To solve this problem, anti-wrinkle finishing has appeared for cotton knitted fabrics. [0003] Anti-wrinkle finishing, also known as easy care, durable press finishing, wrinkle resistance, washability, non-ironing,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M13/207D06M13/203D06M11/46D06C7/02D06M101/06
Inventor 张新华张若煜
Owner SHAOXING UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com