Ceramic adhesive

An adhesive, ceramic technology, applied in the directions of wax adhesive, adhesive type, rosin adhesive, etc., to achieve the effect of strong cohesion, convenient operation and low cost

Inactive Publication Date: 2012-11-07
占协琼
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, there are many types of ceramic adhesives on the market, but most of them contain harmful substances, and their production process is complicated and the production cost is high
In addition, the existing ceramic adhesives still have defects such as weak cohesion and poor leakage.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A ceramic adhesive comprising the following components in parts by weight:

[0019] 8 parts of crystalline sodium carbonate

[0020] Rosin 30 parts

[0021] 10 parts white wax

[0022] 20 parts of magnesium chloride

[0023] 1 part borax

[0024] 10 parts of polyvinyl alcohol.

[0025]

Embodiment 2

[0027] A ceramic adhesive comprising the following components in parts by weight:

[0028] 10 parts of crystalline sodium carbonate

[0029] Rosin 40 parts

[0030] 20 parts white wax

[0031] 30 parts of magnesium chloride

[0032] Borax 5 parts

[0033] 20 parts of polyvinyl alcohol.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a ceramic adhesive. The ceramic adhesive comprises, by weight, 8-10 parts of crystal carbonate, 30-40 parts of rosin, 10-20 parts of white wax, 20-30 parts of magnesium chloride, 1-5 parts of borax and 10-20 parts of polyvinyl alcohol. The ceramic adhesive is available in raw materials, simple in preparation, low in cost, convenient to operate when used and has the advantages of no toxicity, innocuousness, high adhesive property and fine permeability.

Description

technical field [0001] The invention relates to an adhesive, in particular to a ceramic adhesive. Background technique [0002] There are many types of ceramic adhesives on the market, but most of them contain harmful substances, and their production process is complicated and the production cost is high. In addition, the existing ceramic adhesives still have defects such as weak cohesive force and poor leakage. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a ceramic adhesive with strong cohesive force, good leakage, simple manufacturing process and low production cost. [0004] In order to solve the problems of the technologies described above, the technical scheme adopted in the present invention is as follows: [0005] A ceramic adhesive, which comprises the following components by weight: [0006] 8~10 parts of crystalline sodium carbonate [0007] Rosin 30~40 parts [0008] White wax 10~20 parts ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J193/04C09J191/06C09J129/04C09J11/04
Inventor 占协琼
Owner 占协琼