Novel water permeable material using desert sand as aggregate, and preparation method and application of novel water permeable material

A permeable material and a new type of technology, applied in the field of building materials, can solve the problems of inability to be widely promoted, high cost of permeable bricks, low compressive strength, etc., and achieve the effects of good water permeability, low price, and improved mechanical properties.

Active Publication Date: 2012-11-14
杭锦旗亿嘉环境治理有限公司
View PDF1 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Cement permeable bricks either have low water permeability or good water permeability, but the compressive strength is not high. It is difficult to balance the performance of these two aspects; the cost of using polymer binders and manual processing of sand permeable bricks is high and cannot be widely promoted

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel water permeable material using desert sand as aggregate, and preparation method and application of novel water permeable material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Accurately weigh raw materials (Kg): Kubuqi desert sand 85, Portland cement 5, water glass 5, water-based epoxy resin binder 3, polyvinyl acetate binder 1, coloring agent molybdenum chrome bright red 1.

[0025] Preparation:

[0026] (a) Add desert sand, inorganic binder and colorant to the cement mortar mixer and stir evenly;

[0027] (b) Add water-based polymer binder and stir evenly;

[0028] (c) injecting the stirred raw materials into the mould;

[0029] (d) Use the pressurized belt vibration forming process to ensure that the new water-permeable material is formed, maintain it at room temperature for 24 hours, and then demould.

[0030] The novel water-permeable material is used for preparing water-permeable pavement permeable bricks.

[0031] Water-based epoxy resin binder, preferably bisphenol A type epoxy resin, such as bisphenol A type epoxy resin E-44, E-42, E-35, E-31, E-20, E-14, E One of -12, E-06, E-03 or any combination thereof.

Embodiment 2

[0042] Accurately weigh raw materials (Kg): Kubuqi desert sand 80, water-based epoxy resin 3, Portland cement 2, water glass 1, medium chrome yellow 1.

[0043] Preparation:

[0044] (a) Add desert sand, portland cement, water glass and colorant to the cement mortar mixer and stir evenly;

[0045] (b) Add water-based polymer binder and stir evenly;

[0046] (c) injecting the stirred raw materials into the mould;

[0047] (d) Use the pressurized belt vibration forming process to ensure that the new water-permeable material is formed, maintain it at room temperature for 24 hours, and then demould.

[0048] The novel water-permeable material is used for preparing water-permeable pavement permeable bricks.

[0049] Water-based epoxy resin binder, preferably bisphenol A type epoxy resin, such as bisphenol A type epoxy resin E-44, E-42, E-35, E-31, E-20, E-14, E One of -12, E-06, E-03 or any combination thereof.

Embodiment 3

[0051] Accurately weigh raw materials (Kg): Kubuqi desert sand 90, water-based epoxy resin 3, polyvinyl acetate resin 3, Portland cement 8, molybdenum chromium scarlet 2.

[0052] Preparation:

[0053] (a) Add desert sand, portland cement and colorant to the cement mortar mixer and stir evenly;

[0054] (b) Add water-based epoxy resin and polyvinyl acetate resin and stir evenly;

[0055] (c) injecting the stirred raw materials into the mould;

[0056] (d) Use the pressurized belt vibration forming process to ensure that the new water-permeable material is formed, maintain it at room temperature for 24 hours, and then demould.

[0057] The novel water-permeable material is used for preparing water-permeable pavement permeable bricks.

[0058] Water-based epoxy resin binder, preferably bisphenol A type epoxy resin, such as bisphenol A type epoxy resin E-44, E-42, E-35, E-31, E-20, E-14, E One of -12, E-06, E-03 or any combination thereof.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a novel water permeable material using desert sand as aggregate, and a preparation method and application of the novel water permeable material. The material is characterized by comprising the following ingredients in parts by weight: 70-95 parts of desert sand, 1-10 parts of aqueous polymer binder, 2-10 parts of inorganic binder and 0-3 parts of colorant. The preparation method of the novel water permeable material comprises the following steps of uniformly stirring the desert sand, the inorganic binder, the colorant and the aqueous polymer binder, filling into a mold and using a pressurizing band vibration molding process to prepare water permeable road bricks and water permeable plates. According to the invention, the raw desert sand is utilized, so that the waste is changed into wealth; compared with a resin type water permeable brick, the material is low in price and good in water permeability; environment-friendly binders which are free of toxin, smell and pollution are utilized; the material is wide in application field; when being used for preparing water permeable bricks which are paved on sidewalks and roads in parks, residential areas and the like, the material is beneficial for underground water circulation.

Description

technical field [0001] The invention belongs to the field of building materials, and in particular relates to a novel water-permeable material using desert sand as an aggregate, a preparation method and application thereof. Background technique [0002] At present, due to the needs of the development of the urban ecological environment, the urban ground is gradually being covered by impermeable materials such as cement and asphalt to be covered by permeable pavement materials. The traditional method is composed of large particle skeleton and cement or artificially processed sand and polymer binder. Cement permeable bricks either have low water permeability or good water permeability but low compressive strength. It is difficult to balance the performance of these two aspects; the cost of using polymer binders and manual processing of sand permeable bricks is high and cannot be widely promoted. Desert sand is currently a waste that is difficult to use with high added value. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B28/26C04B14/06
Inventor 郝亮赵建军
Owner 杭锦旗亿嘉环境治理有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com