Method for preparing and spaying anticorrosion coating for western wind farm tower

A technology for anti-corrosion coatings and wind farms, applied in anti-corrosion coatings, epoxy resin coatings, devices for coating liquids on the surface, etc., can solve the problem of lack of anti-corrosion coatings and related materials for the towers of western wind farms, and achieve good interlayer Adhesion, Wind Power Cost Reduction, Corrosion Rate Reduction Effects

Active Publication Date: 2014-08-13
洛阳双瑞防腐工程技术有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004]With the continuous investment of wind power generation funds in western China, there is an urgent need for a high-performance tower anti-corrosion coating to meet the long-term anti-corrosion requirements, but up to now, domestic There are no anti-corrosion coatings and related materials dedicated to the towers of western wind farms

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing and spaying anticorrosion coating for western wind farm tower
  • Method for preparing and spaying anticorrosion coating for western wind farm tower
  • Method for preparing and spaying anticorrosion coating for western wind farm tower

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0074] Weigh 35.0g of GF-630A elastic epoxy resin, 18g of mixed solvent (xylene: n-butanol: cyclohexanone = 1:1:1), 0.08g of BYK-4510, 0.4g of BYK-306 and mix Together and disperse and stir evenly, then add 23g of zinc powder and 0.5g of BYK-A530 for re-dispersion and stirring, after dispersing and stirring evenly, put them together in a sand mill for grinding until the fineness reaches 80μm, when the viscosity reaches 80 ~ After 110 seconds, the primer group A was prepared for use. Before spraying, 0.7 parts by weight of GF-630B was put into the primer group A of 10.0 parts by weight and fully dispersed and stirred to obtain the primer, that is, the Primer A group: said primer B group=10g:0.7g.

[0075]Weigh 30g of PUASTOMER-2804 ultra-linear elastic resin, 30.0g of shielding impermeability material (the ratio of mica iron oxide: glass flakes: mica powder in the 30.0g parts by weight = 2:1:1), 15g of Mix the solvent (xylene: butyl acetate: PMA=1:1:1) and disperse and stir ev...

Embodiment 2

[0079] Weigh 30.0g of GF-630A elastic epoxy resin, 15g of mixed solvent (xylene: n-butanol: cyclohexanone = 1:1:1), 0.05g of BYK-4511, 0.3g of BYK-306 and mix Together, disperse and stir evenly, then add 20g of zinc powder and 0.3g of EFKA-2035 for re-dispersion and stirring, after dispersing and stirring evenly, put them together in a sand mill for grinding until the fineness reaches 80μm, when the viscosity reaches 80 ~ After 110 seconds, the primer group A was prepared for use. Before spraying, 0.82 parts by weight of GF-630B was put into the primer group A of 10.0 parts by weight and fully dispersed and stirred to obtain the primer, that is, the Primer A group: said primer B group=10g:0.82g.

[0080] Weigh 35g of PUASTOMER-2804 ultra-linear elastic resin, 33.0g of shielding and anti-seepage material (the ratio of mica iron oxide: glass flakes: mica powder in the 33.0g parts by weight = 2:1:1), 18g of Mix the solvent (xylene: butyl acetate: PMA=1:1:1) and disperse and stir...

Embodiment 3

[0085] Weigh 40.0g of GF-630A elastic epoxy resin, 20g of mixed solvent (xylene: n-butanol: cyclohexanone = 1:1:1), 0.1g of BYK-4511, 0.5g of BYK-306 and mix Together, disperse and stir evenly, then add 25g of zinc powder and 0.7g of EFKA-2035 for re-dispersion and stirring, after dispersing and stirring evenly, put them together in a sand mill for grinding until the fineness reaches 80μm, when the viscosity reaches 80 ~ After 110 seconds, the primer group A was prepared for use. Before spraying, 0.81 parts by weight of GF-630B was put into 10.0 parts by weight of the primer group A and fully dispersed and stirred evenly to obtain the primer, that is, the Primer A group: said primer B group=10g:0.81g.

[0086] Weigh 40g of PUASTOMER-2804 ultra-linear elastic resin, 35.0g of shielding and anti-seepage material (the ratio of mica iron oxide: glass flakes: mica powder in the 35.0g parts by weight = 2:1:1), 20g of The mixed solvent (xylene: butyl acetate: PMA=1:1:1) is mixed toge...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

A preparation and spraying method of an anti-corrosion paint for towers of western wind farms. The anti-corrosion paint is composed of primer + intermediate paint + top coat, and the primer contains elastic resin A, zinc powder, mixed solvent, adhesion promoter, base material lubricant Wetting agent, defoamer and curing agent A, intermediate paint contains elastic resin B, shielding and anti-seepage material, mixed solvent, defoamer and curing agent B, topcoat contains elastic resin C, weather-resistant and anti-corrosion material, mixed solvent, defoaming agent, wetting and dispersing agent, leveling agent and curing agent C. The primer can weaken and absorb the impact stress caused by wind and sand on the paint film. The intermediate paint can weaken the impact stress from the topcoat and improve the elastic deformation capacity of the entire coating. In addition to good weather resistance, the topcoat also has good High elasticity, high wear resistance, high elongation at break, high tensile strength, and strong ability to withstand wind and sand impact, etc., according to the preparation and spraying method of the present invention, the main performance indicators of the anti-corrosion coating meet the use requirements of the towers of the western wind farm .

Description

technical field [0001] The invention belongs to the technical field of anti-corrosion coatings, and in particular relates to a method for preparing and spraying anti-corrosion coatings for wind farm towers in western China. Background technique [0002] Most of the wind farms in western China are located in areas with perennial drought and little rain, strong ultraviolet rays, strong and frequent wind and sand, and large temperature differences between day and night. Therefore, the anti-corrosion coating of the towers of the western wind farms is also affected by the above harsh conditions all the year round. The anti-corrosion coating on the near-ground part and the main windward side of the tower will be completely eroded, causing the exposed metal surface of the tower to be corroded, causing the main structure of the tower to be damaged, corroded, and even collapsed, causing serious safety hazards. [0003] According to GB / T 9072-2003 "Wind Turbine Generating Sets-Tower",...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/00C09D179/08C09D5/10C09D5/08C09D7/14B05D7/24C09D7/80
Inventor 卫小星张乐显陈华山
Owner 洛阳双瑞防腐工程技术有限公司