Novel mineral reflective thermal insulation coating for architecture and preparation method thereof

A technology for reflective thermal insulation coatings and buildings, applied in reflective/signal coatings, coatings, etc., can solve problems such as fading of coating functions, and achieve the effects of preventing cracks, good environmental protection, and easy to make

Active Publication Date: 2014-07-09
PANJIN AOMA PAINT
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This kind of coating can only withstand the low temperature of 250°C, and the organic binder will volatilize or carbonize above 400°C, the coating film will be destroyed, and the function of the coating will also fade.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel mineral reflective thermal insulation coating for architecture and preparation method thereof
  • Novel mineral reflective thermal insulation coating for architecture and preparation method thereof
  • Novel mineral reflective thermal insulation coating for architecture and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0063] (1) pulping

[0064] Add water 178.0g, Natrosol250MHR (purchased from Hercules, USA) 2.0g successively in the dispersing tank, stir until completely dissolved; then add 2.0g of Inocot610 (purchased from Germany Fanbairou Silicate Products Company), Lopon826 (purchased from German Baker Gilini Company) 2.0g, Lopon ST (purchased from German Beck Gilini Company) 5.0g, continue to stir until uniform; then add titanium dioxide R-706 (purchased from DuPont Company) 150.0g, particle size is 1.1 μm of heavy calcium (purchased from Liaoning Haicheng Heshan Company) 100.0g, particle size of 10 μm heavy calcium (purchased from Liaoning Haicheng Heshan Company) 40.0g, particle size of 12 μm wollastonite (purchased from Jilin Pear Wollastonite Co., Ltd.) 60.0g in the mixed solution; after adding, use 15.0g of reserved water to clean the material sticking to the dispersion shaft and the cylinder wall into the cylinder; under the condition that the stirring speed is 1400-2000 rpm Nex...

Embodiment 2

[0070] (1) pulping

[0071] Add 185.6 g of water and 2.4 g of hydroxyethyl cellulose (purchased from Clariant, Germany) with a viscosity of HS30000yp in the dispersion tank, and stir until completely dissolved; ) 2.0g, Lopon895 (purchased from German Becker Gilini Company) 2.0g, Lopon ST (purchased from German Becker Gilini Company) 5.0g, continue to stir until uniform; then add titanium dioxide CR-501 (purchased from Jinzhou Titanium White Powder Co., Ltd.) 120.0g, calcite with a particle size of 0.7 μm (purchased from Liaoning Haicheng Heshan Company) 150.0 g, 77.0 g of calcite with a particle size of 5 μm (purchased from Liaoning Haicheng Heshan Company), with a particle size of 38 μm 1g of mica powder (purchased from Chuzhou Gerui Company) in the mixed solution; after adding, use 10.0g of reserved water to wash the material sticking to the dispersion shaft and the cylinder wall into the cylinder; when the stirring speed is 1400-200 rpm Disperse at high speed for 20 minute...

Embodiment 3

[0076] Embodiment 3 coating performance test

[0077] The China Academy of Building Research and the China Academy of Space Technology jointly tested Embodiment 1, and the results are shown in Table 3. All performances of Embodiment 1 are better than national technical indicators.

[0078] table 3

[0079]

[0080]

[0081] The coating prepared in the pilot test of the formula of Example 1 is used in the X-ray perspective room of Xinglongtai District Center for Disease Control and Prevention, Panjin City. The building is 15.24 meters long, 4.64 meters wide and 3.2 meters high. The roof is made of dark blue curved color steel plate, and the facade is made of light gray old latex paint. The total painting area of ​​the top and facade is about 260㎡. Roller coating is used for construction. Firstly, one coat of sealing primer is applied. After drying (about 20 minutes), the pilot product of the formula in Example 1 is used for roller coating once, and the second coat of r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
viscosityaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a novel mineral reflective thermal insulation coating for architecture and a preparation method thereof. The coating comprises, by weight, 0.1-0.6% of a thickener, 0.2-1.2% of an antifoaming agent, 0.1-0.5% of a dispersing agent, 0.5-1.0% of a stabilizer, 6.0-20.0% of functional pigments, 5.0-27.0% of fillers, 4.0-10.0% of a modified emulsion with a concentration of 46-50wt%, 15.0-23.0% of potassium silicate with a concentration of 28-32wt%, 1.0-5.0% of a water repellent agent, 6.0-10.0% of ceramic microbeads, 0-1.5% of a rheological agent and the balance water. According to the coating and the preparation method thereof, defects of latex type reflective thermal insulation coatings are overcome, national standards are accorded with, and the advantages of being energy-saving, economical, environment-friendly, low-carbon, flame retardant, high temperature resistant, good anti-aging and anti-contamination performances and the like of inorganic coatings are maintained.

Description

Technical field: [0001] The invention relates to a paint and a preparation method thereof, more specifically, to a mineral reflective heat-insulating paint for building and a preparation method thereof. Background technique: [0002] With the introduction of various national building energy-saving policies, the public security department has increased the fire protection requirements for building external insulation materials. Traditional building energy-saving materials such as thermal insulation mortar and EPS external insulation systems are becoming more and more disadvantageous due to flammability, cracking, leakage, and falling off. Obviously, and the construction is cumbersome, the cost is high, and it is not suitable for the construction of special-shaped complex structures. A large number of plate gaps form thermal bridges, which makes it difficult to further improve the energy-saving effect of the system. [0003] As a new type of green and environment-friendly bui...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D1/00C09D125/14C09D133/04C09D5/33C09D7/12
Inventor 宋振芳崔洪斌马丰
Owner PANJIN AOMA PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com