Dust-proof anti-aging black high-gloss ABS (acrylonitrile-butadiene-styrene) alloy and preparation method thereof

An anti-aging, ABS resin technology, which is applied in the field of dust-proof and aging-resistant black high-gloss ABS alloy and its preparation, can solve the problems of large amount of carrier resin and dispersing lubricant, high consumption of energy processing aids, uneven powder dispersion, etc. Achieve good anti-dust pollution performance, good anti-scratch performance, and reduce surface resistance

Active Publication Date: 2012-12-19
NANHUA UNIV +1
View PDF11 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The processing technology containing powder not only has uneven dispersion of powder, but also has the disadvantage of polluting the production environment; while the processing technology of single masterbatch has the disadvantages of large amount of carrier resin and dispersing lubricant, high energy and processing aid consumption in the processing process, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dust-proof anti-aging black high-gloss ABS (acrylonitrile-butadiene-styrene) alloy and preparation method thereof
  • Dust-proof anti-aging black high-gloss ABS (acrylonitrile-butadiene-styrene) alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Embodiment 1. A dust-proof and aging-resistant black high-gloss ABS alloy, the weight percentage of each component is: ABS resin: 60%; PMMA resin: 22%; compatibilizer: 12%; dust-proof and aging-resistant high-gloss black masterbatch Grains: 4%.

[0038] The ABS resin is a ternary copolymerization resin of acrylonitrile, butadiene and styrene, and the weight percentages of its components are: acrylonitrile: 10-30%, butadiene: 5-30%, styrene: 40-30%. 70%;

[0039] The PMMA resin is a transparent resin with a light transmittance ≥ 90%;

[0040] Described compatibilizer is the resin that MBS resin and AS resin are mixed by weight ratio 1:1, and MBS resin is the ternary copolymerization resin of methyl methacrylate, butadiene, styrene, and MBS resin is transparent resin, light-transmitting Rate ≥ 85%, AS resin is acrylonitrile, styrene copolymer resin, AS resin is transparent resin, light transmittance ≥ 85%.

[0041] The weight percent of each component of the dust-proof...

Embodiment 2

[0051] Embodiment 2. A dust-proof and aging-resistant black high-gloss ABS alloy, the weight percentage of each component is: ABS resin grade is ABS-GP22: 48%; PMMA resin: 30%; compatibilizer: 18%; dustproof Anti-aging high-gloss black masterbatch: 6%.

[0052] The ABS resin is a ternary copolymerization resin of acrylonitrile, butadiene and styrene, and the weight percentages of its components are: acrylonitrile: 10-30%, butadiene: 5-30%, styrene: 40-30%. 70%.

[0053] The PMMA resin is a transparent resin with a light transmittance ≥ 90%.

[0054] Described compatibilizer is the resin that MBS resin and AS resin are mixed by weight ratio 1:2, and MBS resin is the ternary copolymerization resin of methyl methacrylate, butadiene, styrene, and MBS resin is transparent resin, light-transmitting Rate ≥ 85%, AS resin is acrylonitrile, styrene copolymer resin, AS resin is transparent resin, light transmittance ≥ 85%.

[0055] The weight percent of each component of the dust-proo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
transmittivityaaaaaaaaaa
transmittivityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a dust-proof anti-aging black high-gloss ABS (acrylonitrile-butadiene-styrene) alloy which comprises the following components in percentage by weight: 48-60% of ABS resin, 22-30% of PMMA (polymethyl methacrylate) resin, 12-18% of compatilizer and 4-6% of dust-proof anti-aging high-gloss black master batch. The anti-aging agent and pigment carbon black in the dust-proof anti-aging high-gloss black master batch constitute an anti-aging system; and the carbon nanotubes, pigment carbon black and lauryl amine polyoxyethylene (2) ether constitute a dust-proof system, thereby effectively preventing aging of ABS, and satisfying the requirements of the high-gloss ABS alloy for coloration, color protection, gloss protection and dust-proofing. The preparation method comprises the following steps: preparing the dust-proof anti-aging high-gloss black master batch, and preparing the dust-proof anti-aging black high-gloss ABS alloy by using the master batch. The multifunctional master batch technique provided by the invention eliminates environmental pollution of dust, implements green clean production of the ABS resin and alloy, has the characteristics of low consumption of carrier resin and lubricating dispersant and low consumption of master batch processing energy and processing assistants, and can be widely applicable to formation processing of the ABS and alloy.

Description

technical field [0001] The invention relates to the technical field of polymer alloys, in particular to a dust-proof and aging-resistant black high-gloss ABS alloy and a preparation method thereof. Background technique [0002] ABS resin obtained by ternary copolymerization of acrylonitrile, butadiene, and styrene is widely used in the electronics and electrical industries due to its excellent comprehensive properties. High-gloss ABS alloys occupy a large share in high-gloss plastics. The high-gloss ABS alloy realizes the ABS spray-free process, which is a new technology for energy saving and environmental protection in the electronic and electrical industry. [0003] The main chain of ABS resin contains double bonds, which is one of the most prominent plastics with aging problems. Poor aging resistance is one of the biggest shortcomings of ABS. The earliest aging phenomenon during product use is loss of gloss (loss of gloss), so it is particularly important for gloss reten...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L33/12C08L51/04C08L25/12C08K13/04C08K7/00C08K3/04C08J3/22
Inventor 刘芝芳王宏青袁小斌龙泽海宋红光廖云
Owner NANHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap