Stripping agent for stainless steel electroplating rack

An electroplating hanger and stripping agent technology, applied in the field of electroplating technology, can solve the problems of damage to the insulating glue, short service life of the insulating glue hanger, unable to maintain the performance and service life of the hanger, and achieve the effect of accelerating peeling and promoting peeling. Effect

Inactive Publication Date: 2013-01-16
DONGGUAN DAOGU ELECTRONICS MATERIAL TECH
View PDF3 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The former surface coating can not be removed, which will deform the hook and damage the insulating glue. The latter is easy to pollute the environment, has a hook that is easy to corrode, and damages the insulating glue. The service life of the hanger is short.
Later, mixed acid and corrosion inhib...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach

[0008] Embodiments of the present invention are as follows: a stripping agent for stainless steel electroplating racks, which is prepared from sodium nitrate, Rochell's salt, boric acid, triethanolamine, thiourea and water, and is characterized in that: the concentrated solution weight percentage ratio of the stripping agent For: sodium nitrate 6% - 30%, Rohrs' salt 0.1% - 8%, triethanolamine 5% - 10%, thiourea 0.01% - 0.05%, boric acid 1% - 4%, glacial acetic acid 0.1% - 2% , and the rest is water.

[0009] The sodium nitrate is a conductive salt, the Rohrs' salt is a surfactant, the triethanolamine is a gloss agent, the thiourea is a corrosion inhibitor, and the boric acid is a buffer buffer. The glacial acetic acid is an acidity regulator.

[0010] The use method is as follows: (1), according to claim 1, the weight percentage distribution ratio is: 20%-30%, the rest is the concentrated solution of the stripping agent of water, the hanger is an anode, and the cathode is a s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of electroplating processes, in particular to a stripping agent for a stainless steel electroplating rack. The stripping agent for the stainless steel electroplating rack is prepared from sodium nitrate, potassium sodium tartrate tetrahydrate, boric acid, triethanolamine, glacial acetic acid, thiourea and water and is characterized in that a concentrated solution of the stripping agent comprises the following components in percentage by weight: 6 to 30 percent of sodium nitrate, 0.1 to 8 percent of potassium sodium tartrate tetrahydrate, 5 to 10 percent of triethanolamine, 0.01 to 0.05 percent of thiourea, 1 to 4 percent of boric acid, 0.1 to 2 percent of glacial acetic acid and the balance of water. The process is advanced, and the combined concentrated solution of the stripping agent is colorless and tasteless. During use, the concentrated solution of the stripping agent and water are mixed. During operation, the rack is used as an anode, and a stainless steel plate is used as a cathode; the stripping voltage is 4 to 6V; the hooking and electroplating layer of the rack can be stripped completely in 3 to 5 minutes, harmful gas is not produced, and a hook point is not corroded; and after the rack is stripped completely, the hook point is bright, and limb insulating glue is not damaged.

Description

Technical field: [0001] The invention relates to the technical field of electroplating technology, in particular to a stripping agent for stainless steel electroplating racks. Background technique: [0002] In the field of electroplating technology, the hanging plating of the electroplating line generally uses a hanger (the main body of the hanger is copper metal, and the limbs and hooks are stainless steel. The main body and limbs use organic insulating glue). During electroplating, the current discharges between the hook tip of the hanger and the electroplated product to deposit the coating. Due to multi-layer electroplating, the hanger hook will deposit a layer of electroplating to affect the conductivity of the hanger hook and the electroplated product. Therefore, it must be stripped to make it conductive. There are two traditional stripping methods, one is to strip with manual pliers, and the other is to remove it by nitric acid corrosion. The former surface coating c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C25F5/00
Inventor 陈华棠
Owner DONGGUAN DAOGU ELECTRONICS MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap