Resin-based composite material for cable bracket or fixture and preparation method of resin-based composite material

A technology of cable support and composite materials, which is applied in the direction of pipeline supports, mechanical equipment, pipes/pipe joints/pipe fittings, etc., which can solve the problems of immature research and application of special polymer composite materials, and overcome easy corrosion and low material cost Effect

Inactive Publication Date: 2013-01-23
乌鲁木齐心愿圣峰工贸有限公司
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the research and application of special polymer composite materials for wire and cable brackets or fixtures at home and abroad are still immature.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A fiber-reinforced resin-based composite material for cable supports or clamps, the raw material components and the mass percentages of each component are as follows:

[0026] 191 Resin 13%

[0027] Styrene 3.5%

[0028] Butyl peroxyacetate 0.2%

[0029] Zinc Stearate 1%

[0030] Calcium powder 72%

[0031] Magnesium Oxide 0.15%

[0032] Calcium Oxide 0.15%

[0033] Glass Fiber 10%

[0034] The preparation method of the special fiber-reinforced resin-based composite material for the cable support or the clamp is as follows:

[0035] (1) Weigh the corresponding weight of 191 resin and glass fiber according to the ratio of the raw material formula, add it to the container, control the temperature at 80 degrees, and stir at 1000r / min until the reinforcing fiber is evenly dispersed;

[0036] (2) Take fillers, lubricants, and anti-aging agents of corresponding weights according to the ratio of the raw material formula, add them to the mixture obtained in step (1), con...

Embodiment 2

[0040] A fiber-reinforced resin-based composite material for cable supports or clamps, the raw material components and the mass percentages of each component are as follows:

[0041] 191 Resin 20%

[0042] Styrene 5%

[0043] Tert-butyl peroxybenzoate 0.2%

[0044] Zinc Stearate 0.7%

[0045] Sodium Humate 0.7%

[0046] Calcium powder 65%

[0047] Magnesium Oxide 0.2%

[0048] Calcium Oxide 0.2%

[0049] Glass Fiber 8%

[0050] The preparation method of the special fiber-reinforced resin-based composite material for the cable support or the clamp is as follows:

[0051] (1) Weigh the corresponding weight of 191 resin and glass fiber according to the ratio of the raw material formula, add it to the container, control the temperature at 70 degrees, and stir at 1000r / min until the reinforcing fiber is evenly dispersed;

[0052] (2) Take fillers, lubricants, and anti-aging agents of corresponding weights according to the ratio of the raw material formula, add them to the m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a resin-based composite material for a cable bracket or a fixture and a preparation method of the resin-based composite material. The resin-based composite material is characterized by being prepared from the following raw materials in percentage by weight: 10-30% of 191 resin, 6-20% of styrene, 0.1-0.8% of initiator, 0.5-3% of lubricant, 60-85% of filler, 0.1-1% of antiager and 8-16% of reinforcement fibers. The preparation method is as follows: weighing the raw materials according to the weight ratio; adding the raw materials into a container according to a feeding sequence of (1) the 191 resin and the reinforcement fibers, (2) the filler, the lubricant and the antiager, (3) the styrene and the initiator, maintaining the temperature at 60-100 DEG C and the rotating speed at 800-2000 r/min (revolutions per minute), and mixing the raw materials; discharging; and pouring and curing. A special resin-based composite material for cable bracket or fixture is designed and prepared through advanced and reasonable materials in the invention, and the composite material is excellent in corrosion resistance, mechanical property and electric property and low in material cost and has less possibility of being stolen, so that the composite material can be used for preparing cable brackets or fixtures meeting various environmental demands.

Description

technical field [0001] The invention belongs to the field of cable materials, and in particular relates to a resin-based composite material for cable supports or clamps and a preparation method. Background technique [0002] The cable bracket or clamp is a special bracket or clamp used to fix the cable after laying and installing the cable, so that the cable occupies the correct position and prevents the cable from moving due to external force or self-weight. It is also called a cable fixing bracket or clamp. Cable brackets or clamps are widely used in the fixing of building branch cables, flame-retardant cables, fire-resistant cables, tunnel cables, mine cables, high-voltage transmission and distribution cables and wiring. [0003] Cable brackets or clamps are important components for cable laying and have been used and researched for a long time. Traditionally, people use alloy materials to prepare cable brackets or clamps, but the cable brackets or clamps made of such ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L51/08C08K13/04C08K7/14C08K3/26C08K3/22C08F283/01F16L3/00
Inventor 宿新泰武荣兰冯聚广燕青芝徐娜
Owner 乌鲁木齐心愿圣峰工贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap