High-impact PVC (polyvinyl chloride)/ABS (poly(acrylonitrile butadiene styrene)) tubing and preparation method thereof

A high-impact, pipe technology, applied in the direction of pipes/pipe joints/fittings, pipes, rigid pipes, etc., can solve the problems of difficult flowability and poor impact resistance of PVC melt processing, and achieve the improvement of tensile strength and Elongation at break, improved impact resistance, improved fluidity

Active Publication Date: 2013-02-06
河北鹏博通信设备有限公司
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

PVC pipes have the advantages of acid resistance, alkali resistance, corrosion resistance, and high strength. However, the impact resistance of PVC pipes produced by major manufactu

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0029] The preparation method of high-impact PVC / ABS pipe comprises the following steps:

[0030] The first step: preparation of material A

[0031] Take the following raw materials in parts by weight: polyvinyl chloride SG-5 55, polyvinyl chloride recycled material 45, active calcium 20, chlorinated polyethylene 15, titanium dioxide 5, calcium stearate 4, azobisisobutyronitrile 0.3, Impact modifier ACR 8, N-(β-aminoethyl)-γ-aminopropyltrimethoxysilane 0.4, antioxidant 1076 0.5, 2,4 dihydroxybenzophenone 0.3, glycerin stearate Grease 0.5, ditetradecyl alcohol ester 0.2, modified nano powder 8,

[0032] Among them, the modified nano-powder is prepared by the following method: after mixing barite powder, sepiolite powder, and limestone powder in equal proportions, burning at 700°C for 5 hours, then grinding into nano-powder, mixing with 4% bis(dioctyloxypyrophosphate) ethylene titanate was stirred evenly, dried, and pulverized into powder,

[0033] Put the weighed raw materi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-impact PVC (polyvinyl chloride)/ABS (poly(acrylonitrile butadiene styrene)) tubing and a preparation method thereof. The tubing is prepared from a material A and a material B by steps of proportionally mixing, extruding and granulating. Since a formula is optimized further, dispersing of organic packing can be improved during processing of the PVC tubing, fluidity of PVC melt can be improved, tensile strength and elongation at break can be improved, and the defect of good ductility but low hardness of polyethylene products produced by the aid of chlorinated polyethylene is overcome. In addition, since components such as impact modifiers ACR, ACM (poly(acrylic acid ester rubber)), MBS (methacrylate butadiene styrene) and ABS resin are utilized in the formula, cold bending performance and impact resistance of the tubing produced according to the formula are improved.

Description

technical field [0001] The invention relates to the field of PVC pipe production, in particular to a high-impact PVC / ABS pipe and a preparation method thereof. Background technique [0002] The main component of PVC pipe is polyvinyl chloride, and plasticizers, anti-aging agents and other auxiliary materials are added to increase its heat resistance, toughness, ductility, etc. PVC is a well-loved, popular and widely used synthetic material in the world today. PVC pipe is a mature pipe, mainly used in water supply and drainage projects. PVC pipes have the advantages of acid resistance, alkali resistance, corrosion resistance, and high strength. However, the impact resistance of PVC pipes produced by major manufacturers is not good, especially in the plasticization process in the processing of PVC products. The dispersion and processing fluidity of PVC melt have always been a difficult problem. Contents of the invention [0003] The purpose of the present invention is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08L55/02C08L23/28C08L51/00C08K13/06C08K3/22C08K5/098C08K5/544C08K3/34C08K5/523B29C47/92F16L9/12B29C48/92
CPCB29C48/04B29C48/09B29C48/40B29C48/92B29C2948/9259B29C2948/92704B29C2948/92885B29C2948/92895B29C2948/92904
Inventor 林传忍
Owner 河北鹏博通信设备有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap