Method for decomposing stone coal vanadium ore by aging with sulfuric acid
A technology of stone coal vanadium and sulfuric acid, applied in the direction of improving process efficiency, can solve problems such as inability to carry out large-scale continuous production, difficult control of production process indicators, unstable product quality, etc., to save energy consumption and shorten leaching cycle. , the effect of pure leachate
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0032] Example 1:
[0033] See attached figure 1 , Take 1000g of stone coal vanadium ore from a certain place in Guizhou, finely grind it to 65% below 0.074mm, control the moisture content to 7%, mix in 50g sodium sulfate, then add 126ml 98% concentrated sulfuric acid and mix well. The temperature of the obtained material was raised to 161°C, and then the matured material was placed in a sealed box and stored for 24h. After being taken out, the matured material was broken into pieces, and the liquid-solid ratio ml / g 2:1 was used to soak in water at 95°C for 6h. According to the experiment, the leaching rate of vanadium is 84.37% (based on slag), and the rate of iron leaching is 3.12% (based on slag). The leaching solution contains 3.39g / L vanadium and 0.61g / L iron.
Example Embodiment
[0034] Example 2:
[0035] Take 1000g of stone coal vanadium ore from a certain place in Shaanxi, finely grind it to 70% below 0.074mm, control the moisture content to 5%, mix in 60g sodium sulfate, and then add 140ml 98% concentrated sulfuric acid to mix and mature. The temperature of the obtained material was raised to 168°C, and then the matured material was placed in a sealed box for 36h. After taking it out, the matured material was crushed, and the liquid-solid ratio was used to immerse in water at 90°C for 6h at a ratio of ml / g of 1.8:1. According to the experiment, the vanadium leaching rate was 80.06% (based on slag), and the iron leaching rate was 3.88% (based on slag). The leaching solution contained 4.23g / L vanadium and 0.44g / L iron.
Example Embodiment
[0036] Example 3:
[0037] Take 1000g of stone coal vanadium ore from a place in Shiyan, Hubei, finely grind it to 70% below 0.074mm, control the water content of the material to 5%, mix in 60g of sodium sulfate, and then add 82ml of 98% concentrated sulfuric acid and mix well. It was measured that the temperature of the material was raised to 155°C, and then the material was placed in a sealed box and cured for 48 hours. After taking it out, the clinker was broken into pieces, and the liquid-solid ratio ml / g 2:1 was used to immerse in water at 95°C for 6 hours. According to the experiment, the leaching rate of vanadium is 84.12% (based on slag), and the leaching rate of iron is 2.57% (based on slag). The leaching solution contains 3.12g / L vanadium and 0.65g / L iron.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap