Technology for producing poly(p-phenylene benzobisoxazole) (PBO) fibers

A technology of benzobisoxazole and polyparaphenylene, which is applied in fiber processing, fiber chemical characteristics, and single-component synthetic polymer rayon, etc., can solve the problem of complicated feeding procedures, difficult control, and long residence time. problems, to achieve the effect of overcoming difficult polymerization, improving production efficiency and enhancing stability

Active Publication Date: 2013-02-27
CHINA BLUESTAR CHENGRAND CO LTD +1
View PDF5 Cites 35 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] 1. The feeding procedure is complicated. Since terephthalic acid (TPA) is insoluble in polyphosphoric acid (PPA), 1-10% TPA is added during the polymerization after the slurry, making it difficult to control the ratio of the two monomers in the polymerization;
[0008] 2. To fully mix the TPA slurry into the pre-polymerized material, it needs to stay for too long (more than 5h);
[0009] 3. Pre-polymerization conditions are harsh, monomer salts are easily oxidized and difficult to control

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] A process for producing poly-p-phenylene benzobisoxazole PBO fibers, comprising the following process steps:

[0049] A. Degassing, pre-polymerization and defoaming

[0050] Heat the polyphosphoric acid at 80°C for 60 minutes, then enter the degassing kettle, add 4,6-diaminoresorcinol hydrochloride, terephthalic acid and phosphorus pentoxide, and degas it in the degassing kettle After the degassing is completed, enter the mixing tank for pre-polymerization and degassing to obtain the pre-polymerized material;

[0051] B. Post-polymerization, defoaming

[0052] After the pre-polymerization is completed, the temperature of the mixing tank is raised to 110°C, and the pre-polymer material is pressed into the storage tank, and then the pre-polymer material is pressed into the screw extruder through a hydraulic press capable of precise flow control. The hydraulic press controls the output speed to be 10ml / min. The pre-polymer material is post-polymerized in the screw extrud...

Embodiment 2

[0060] A process for producing poly-p-phenylene benzobisoxazole PBO fibers, comprising the following process steps:

[0061] A. Degassing, pre-polymerization and defoaming

[0062] Heat the polyphosphoric acid at 120°C for 180 minutes, then enter the degassing kettle, add 4,6-diaminoresorcinol hydrochloride, terephthalic acid and phosphorus pentoxide, and degas it in the degassing kettle After the degassing is completed, enter the mixing tank for pre-polymerization and degassing to obtain the pre-polymerized material;

[0063] B. Post-polymerization, defoaming

[0064] After the pre-polymerization is completed, the temperature of the mixing tank is raised to 200°C, and then the pre-polymer material is pressed into the storage tank, and then the pre-polymer material is pressed into the screw extruder through a hydraulic press capable of precise flow control. The hydraulic press controls the output speed to be 100ml / min. The pre-polymer material is post-polymerized in the scre...

Embodiment 3

[0072] A process for producing poly-p-phenylene benzobisoxazole PBO fibers, comprising the following process steps:

[0073] A. Degassing, pre-polymerization and defoaming

[0074] Heat the polyphosphoric acid at 100°C for 120 minutes, then enter the degassing kettle, add 4,6-diaminoresorcinol hydrochloride, terephthalic acid and phosphorus pentoxide, and degas it in the degassing kettle After the degassing is completed, enter the mixing tank for pre-polymerization and degassing to obtain the pre-polymerized material;

[0075] B. Post-polymerization, defoaming

[0076] After the pre-polymerization is completed, the temperature of the mixing tank is raised to 155° C., and the pre-polymer material is pressed into the storage tank, and then the pre-polymer material is pressed into the screw extruder through a hydraulic press capable of precise flow control. The hydraulic machine controls the output speed to be 55ml / min, and the pre-polymer material is subjected to a post-polyme...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a technology for producing poly(p-phenylene benzobisoxazole) (PBO) fibers, and belongs to the field of high performance fiber production. The technology comprises the steps: A, degassing, pre-polymerizing and defoaming; B, post-polymerizing and defoaming; C, spinning and solidifying; D, post-treating; and E, heat-treating and the like. Through optimizing equipment and controlling parameters, a plurality of problems of the prior art are solved. The technological process, equipment cooperation and parameter control of the basic technical scheme are taken as an integral system, are cooperated with each other and are dispensable, materials can be effectively transferred, the scale polymerizing and subsequent scale spinning of the PBO polymer are realized, and a high-quality PBO fiber product is obtained.

Description

technical field [0001] The invention relates to a production process of special fibers, more specifically, the invention relates to a process for producing poly-p-phenylene benzobisoxazole PBO fibers, belonging to the field of high-performance fiber production. Background technique [0002] PBO is the abbreviation of poly-p-phenylene benzobisoxazole. PBO fiber is a high-performance fiber made by spinning PBO polymer. Compared with other high-performance fibers, PBO fibers have higher specific strength, specific modulus, and heat-resistant and flame-retardant properties. They are known as "21st century super fibers" and are used to make high-performance composite materials, such as heat-resistant materials. , Anti-shock and anti-riot materials and structural stealth materials are widely used in high-tech fields such as aerospace, aviation and national defense. [0003] PBO polymers are usually prepared by polymerizing diaminoresorcinol hydrochloride (DAR) and terephthalic a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/94D01F1/10D01F11/08D01D1/02D01D1/10D01D5/06C08G73/22
Inventor 严家策范新年许伟郭玲赵亮钱军李欣欣
Owner CHINA BLUESTAR CHENGRAND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap