Fire extinguishing agent and preparation method thereof

A technology of fire extinguishing agent and surfactant, which is applied in the field of fire extinguishing agent and its preparation, can solve the problems of long dispersion time, affecting the preparation efficiency of fire extinguishing agent, high dispersing rotation speed, etc., so as to improve preparation efficiency, high extinguishing efficiency, and reduce dispersing rotation speed. Effect

Active Publication Date: 2013-04-03
广州神州安防科技有限公司
View PDF11 Cites 88 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the preparation of the fire extinguishing agent in the above-mentioned patent requires a higher dispersion speed and a longer dispersion time, which affects the preparation efficiency of the fire extinguishing agent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The fire extinguishing agent in this embodiment is made of the following raw materials in parts by weight: 1 part of hydrophilic solid powder, 0.08 part of water-soluble surfactant, 2 parts of hydrophobic solid particles, and 100 parts of aqueous solution; the mass percentage of solute in the aqueous solution The content is 10%; the hydrophobic solid particles are solid particles with a contact angle of 110° after hydrophobic modification; the solid particles are magnesium hydroxide particles, silicon dioxide particles, calcium carbonate particles, talc particles, oxidized Aluminum particles, aluminum hydroxide particles, zinc borate particles, zinc oxide particles, zinc carbonate particles, calcium carbonate particles, iron oxide particles, titanium dioxide particles, montmorillonite particles, hydrotalcite particles, hydrotalcite-like particles, fly ash particles, One or more of diatomite particles, mica particles, attapulgite particles and zeolite particles; the water...

Embodiment 2

[0024]The fire extinguishing agent in this embodiment is made of the following raw materials in parts by weight: 25 parts of hydrophilic solid powder, 0.5 part of water-soluble surfactant, 10 parts of hydrophobic solid particles, and 100 parts of aqueous solution; the mass percentage of solute in the aqueous solution The content is 5%; the hydrophobic solid particles are solid particles with a contact angle of 110° after hydrophobic modification; the solid particles are magnesium hydroxide particles, silicon dioxide particles, calcium carbonate particles, talc particles, oxidized Aluminum particles, aluminum hydroxide particles, zinc borate particles, zinc oxide particles, zinc carbonate particles, calcium carbonate particles, iron oxide particles, titanium dioxide particles, montmorillonite particles, hydrotalcite particles, hydrotalcite-like particles, fly ash particles, One or more of diatomite particles, mica particles, attapulgite particles and zeolite particles; the water...

Embodiment 3

[0028] The fire extinguishing agent in this embodiment is made of the following raw materials in parts by weight: 12 parts of hydrophilic solid powder, 1 part of water-soluble surfactant, 50 parts of hydrophobic solid particles, and 100 parts of aqueous solution; the mass percentage of solute in the aqueous solution The content is 1%; the hydrophobic solid particles are solid particles with a contact angle of 120° after hydrophobic modification; the solid particles are magnesium hydroxide particles, silicon dioxide particles, calcium carbonate particles, talc particles, oxidized Aluminum particles, aluminum hydroxide particles, zinc borate particles, zinc oxide particles, zinc carbonate particles, calcium carbonate particles, iron oxide particles, titanium dioxide particles, montmorillonite particles, hydrotalcite particles, hydrotalcite-like particles, fly ash particles, One or more of diatomite particles, mica particles, attapulgite particles and zeolite particles; the water-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a fire extinguishing agent. The fire extinguishing agent is prepared by evenly mixing 1-25 parts of hydrophilic solid powder and 100 parts of water or water solution, and then adding 0.001-2 parts of surfactant for evenly mixing; and then adding 2-100 parts of hydrophobic solid particles. The invention provides a preparation method of the fire extinguishing agent. Compared with the existing fire extinguishing agent, the fire extinguishing agent can simultaneously play stifling, cooling and chemical inhibition roles, and the fire extinguishing efficiency is high; according to the fire extinguishing agent, due to addition of the surfactant in the water phase, the dispersion of rotating speed in preparation process can be lowered, the dispersion time can be shortened, and the preparation efficiency can be improved; and with the fire extinguishing agent, the adhesion property of solid gas interface and liquid gas interface can be greatly improved, the usage amount for extinguishing fire can be greatly reduced, and the fire extinguishing property can be obviously improved.

Description

technical field [0001] The invention belongs to the technical field of fire extinguishing materials, and in particular relates to a fire extinguishing agent and a preparation method thereof. Background technique [0002] Water is a frequently used extinguishing agent whose thermal properties make it useful in the extinguishing process for most types of fires. However, the fluidity of water is very strong, and most of the water used for fire extinguishing is lost before it can take effect under normal circumstances, resulting in a low utilization rate of water fire extinguishing, and it is easy to cause secondary losses and environmental pollution. Chinese patent 201110316520.X provides a fire extinguishing agent, the fire extinguishing agent effectively restricts the free flow of water by binding water in a solid shell, and has a certain accumulation, while reducing the amount of fire extinguishing agent and improving the fire extinguishing effect, Significantly reduces the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A62D1/00
Inventor 贺拥军
Owner 广州神州安防科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap