Welding method for low-carbon high-strength steel

A high-strength steel and welding method technology, applied in the field of plate welding, can solve the problems of low welding quality and achieve the effects of improving welding quality, uniform penetration depth, and good weld shape

Active Publication Date: 2013-04-03
青岛中车四方轨道车辆有限公司
View PDF10 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is: provide a welding method for low-carbon high-strength steel, solve the defect of low welding quality of low-carbon high-strength steel in the prior art, and realize the improvement of welding quality of low-carbon high-strength steel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Welding method for low-carbon high-strength steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] In order to make the purpose, technical solutions and advantages of the embodiments of the present invention clearer, the technical solutions in the embodiments of the present invention will be clearly and completely described below in conjunction with the drawings in the embodiments of the present invention. Obviously, the described embodiments It is a part of embodiments of the present invention, but not all embodiments. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without creative efforts fall within the protection scope of the present invention.

[0017] Such as figure 1 As shown, the welding method of low-carbon high-strength steel in this embodiment includes:

[0018] Step 1. A welding groove is formed on the low-carbon high-strength steel 1 by using a laser blanking method, and a weld seam is formed between the welding grooves of the two low-carbon high-strength steel 1 to be welded. S...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a welding method for low-carbon high-strength steel. The welding method for the low-carbon high-strength steel comprises the following steps of: 1) forming a welding groove on the low-carbon high-strength steel with a laser blanking method, and forming a welding line between the welding grooves of two pieces of low-carbon high-strength steel to be welded; and 2) welding the welding line by consumable electrode mixed gas metal arc welding, filling a welding wire in the welding process, and ensuring that the welding environment temperature is higher than 5DEG C. Specifically, the step 2) comprises the following steps of: 21) carrying out backing weld to the welding line by non-pulse consumable electrode mixed gas metal arc welding, forming a backing weld layer on the bottom of the welding line, and filling the welding wire in the welding process; and 22) carrying out cosmetic welding to the welding line by pulse consumable electrode mixed gas metal arc welding, forming a plurality of cosmetic layers above the backing weld layer, ensuring that two adjacent cosmetic layers are provided with overlay regions, and filling welding wire in the welding process. According to the welding method for the low-carbon high-strength steel, the stress concentration is lowered, and the welding quality of the low-carbon high-strength steel is improved.

Description

technical field [0001] The invention relates to the field of plate welding, in particular to a welding method for low-carbon high-strength steel. Background technique [0002] At present, low-carbon high-strength steel, with high strength, low expansion coefficient and stable elastic modulus, is an ideal material for high-strength products such as shipbuilding, pressure vessels, locomotive manufacturing, and engineering machinery. Low-carbon high-strength steel (for example: HG785D low-carbon quenched and tempered steel) has a low carbon content, generally no more than 0.12. Its high strength and good comprehensive mechanical properties are achieved by adding a variety of hardenability on the basis of low carbon. Alloying elements and quenching and tempering treatment to obtain low-carbon lath martensite and granular bainite with high strength and good toughness. During the welding process, low-carbon high-strength steel has a large tendency to harden, strong sensitivity to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23K9/173B23K9/235B23K26/38
Inventor 郭宝军张泽代夫华于鹏
Owner 青岛中车四方轨道车辆有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap