Water-based environmentally-friendly antirust agent used before electrical steel decarburization and preparation method thereof
A technology for electrical steel and rust inhibitor, which is applied in the field of water-based environmental protection rust inhibitor before decarburization of electrical steel and its preparation field, and achieves the effects of excellent rust resistance, good corrosion resistance and environmental friendliness
Inactive Publication Date: 2013-04-03
段辉
View PDF2 Cites 6 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0003] The present invention aims at overcoming the defects of complex process of removing anti-rust oil or anti-rust agent before decarburization of existing electrical steel, and aims to provide an electrical steel with env
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0009] 10wt% salicylhydroxamic acid, 10wt% ethanol, 20wt% urea, 20wt% ammonia water, 10wt% urotropine, 10wt% ammonium carbonate and 20wt% deionized water were mixed.
Embodiment 2
[0011] 10wt% salicylhydroxamic acid, 5wt% ethanol, 20wt% urea, 20wt% ammonia, 10wt% urotropine, 10wt% ammonium carbonate and 25wt% deionized water were mixed.
Embodiment 3
[0013] 5wt% salicylhydroxamic acid, 10wt% ethanol, 20wt% urea, 20wt% ammonia water, 10wt% urotropine, 5wt% ammonium carbonate and 30wt% deionized water were mixed.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Login to view more
Abstract
The invention specifically relates to a water-based environmentally-friendly antirust agent used before electrical steel decarburization and a preparation method thereof. The technical scheme of the preparation method is as follows: mixing 0-10wt % of salicylhydroxamic acid, 0-10wt % of ethanol, 0-20wt % of urea, 0-20wt % of ammonia water, 0-10wt % of methenamine, 0-10wt % of ammonium carbonate and 20-80wt % of deionized water, uniformly dispersing in a stirrer, and packaging. The components of the water-based environmentally-friendly antirust agent do not contain chromate, nitrite and toxic and harmful ingredients so that the water-based environmentally-friendly antirust agent is environmentally-friendly; the prepared antirust agent is coated on the surface of the electrical steel and forms a protective layer on the metallic surface after dried by cold air or aired, thus inhibiting the corrosion of metal; when decarburization is carried out at above 750 DEG C, the surface layer gradually sublimes or breaks up into volatile gas; and the decarburization of the electrical steel is not affected under the condition that surface treatment is omitted before decarburization.
Description
technical field [0001] The invention belongs to the technical field of antirust agents for electrical steel. In particular, it relates to a water-based environment-friendly antirust agent for electrical steel before decarburization and a preparation method thereof. Background technique [0002] Electrical steel is a magnetic material widely used in electrical products such as engines, generators and transformers. Because silicon is easily oxidized, the electrical steel sheet is rusted and corroded. There are various anti-rust oils and anti-rust agents used in the process of electrical steel sheets and the anti-rust of finished products, but because a small amount of carbon content in steel will also affect the movement of magnetic domains and increase hysteresis loss, therefore, the steel must be The carbon content is reduced to below 50ppm. Decarburization generally occurs at N 2 —H 2 —H 2 It is carried out in an O atmosphere, or in a humid or high dew point exotherm...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more
IPC IPC(8): C23F11/00C21D3/04C21D1/68
Inventor 段辉
Owner 段辉
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap