High-heat-conductivity ternary rubber

A EPDM rubber, high thermal conductivity technology, applied in the field of new nanomaterials, can solve the problems of poor thermal conductivity, high production cost, and decreased mechanical properties.

Inactive Publication Date: 2013-04-17
深圳桐源科技有限公司
View PDF6 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, most of the research on filling thermally conductive rubber adopts the method of physical fillin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-heat-conductivity ternary rubber
  • High-heat-conductivity ternary rubber
  • High-heat-conductivity ternary rubber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] Embodiment 1: In this embodiment, the high thermal conductivity nanometer rapid vulcanization composite EPDM rubber, the content ratio of each raw material component is as follows in parts by weight:

[0047] EPDM rubber 180-220 parts,

[0048] Anti-aging agent 2-3 parts,

[0049] 50-90 parts of carbon black,

[0050] 1-3 parts of sulfur,

[0051] Accelerator 1-3 parts,

[0052] 6-10 parts of plasticizer,

[0053] 40-80 parts of paraffin oil,

[0054] 8-16 parts of inorganic active agent,

[0055] 1-4 parts of dispersant.

[0056] And it is prepared by the following steps:

[0057] The first step, synthetic rubber: the above raw materials are synthesized into rubber through an internal mixer;

[0058] The second step, molding: the synthetic rubber is molded by an open mill;

[0059] The third step, vulcanization: Put the formed rubber into the mold in the vulcanizer, and the pressure range is 150-210kgf / ㎝ 2 , heating up to 220-230°C for 80-100 seconds for vulc...

Embodiment 2

[0060] Embodiment 2: The rubber dispersant is a reagent that promotes the uniform dispersion of material particles in the rubber medium to form a stable suspension. The rubber dispersant used in the embodiments of the present invention is one or more of the following reagents: triethylhexyl phosphoric acid, sodium lauryl sulfate, methyl amyl alcohol, cellulose derivatives, polyacrylamide, ancient Er gum, fatty acid polyethylene glycol ester.

Embodiment 3

[0062] The anti-aging agent used in one embodiment of the present invention is: 6-ethoxy-2,2,4-trimethyl-1,2-dihydroquinoline. Its trade name is antiaging agent AW. Antiaging agent AW is a brown viscous liquid, and the pure product is a light brown viscous liquid. Non-toxic, the specific gravity is 1.029~1.030 (25°C), and the boiling point is 169°C. Soluble in benzene, acetone, dioxyethane, carbon tetrachloride, solvent gasoline and ethanol; insoluble in water. Stable in storage. It is a special anti-ozone anti-aging agent, and it also has a protective effect on flex cracking and thermal oxygen aging. Especially suitable for products used under dynamic conditions. No frost, polluting, not suitable for light-colored products. When the amount is 1-2 parts, it has little effect on vulcanization, and when it is increased to 3 parts, it will significantly promote vulcanization, and the amount of promotion should be appropriately reduced during use.

[0063] The anti-aging age...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Softening pointaaaaaaaaaa
Freezing pointaaaaaaaaaa
Boiling pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses high-heat-conductivity ternary rubber. An anti-aging agent is one type or more types of the following reagents: N-phenyl-alpha-aniline, N-phenyl-beta-naphthylamine, N-phenyl-N'-cyclohexyl p-phenylenediamine, N-phenyl-N'-isopropyl-p-phenylenediamine and N-N'-diphenyl-p-phenylenediamine. An accelerant is one type or more types of the following reagents: an accelerant T, N,N-tetramethyl dithio-dithiocarbonyl amine, tetramethylthiuram disulfide, thiram, a vulcanization accelerant TMTD and tetramethylthiuram disulfide. By adoption of mixed fillers, the heat conductivity of the composite material is greatly improved. Granules and crystal whiskers with a certain length-diameter ratio form continuous heat-conducting network chain; combination of fillers with different grain size is selected, so high filling density is achieved; and the interface of the fillers and a matrix is improved by a coupling agent, so the heat resistance at the interface is reduced.

Description

technical field [0001] The invention relates to the technical field of new nanometer materials, in particular to a high thermal conductivity ternary rubber. Background technique [0002] Now, as electronic products tend to be more and more miniaturized, composite rubber substrates that are easy to integrate and miniaturize and have good flexibility are widely used, but because of the high integration of integrated circuits and the multilayering of laminates, there will inevitably be Therefore, the requirements for the thermal conductivity of these materials have become a top priority. [0003] Ethylene-propylene-diene rubber (EPDM) is a terpolymer of ethylene, propylene and diene monomers. The introduction of diene is to realize vulcanization. The types of diene are: dicyclopentadiene (DCPD), 1,4 Hexadiene. EPDM is tougher than ordinary ethylene propylene rubber. [0004] In recent years, people have filled polymers with non-conductive metal oxides and other compounds, wh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/16C08K13/02C08K3/22C08K3/34C08K3/38C08K3/28C08K3/30C08J3/24
Inventor 杨高林孙向红江志鑫
Owner 深圳桐源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap