Steel 18MnMoNbR for pressure vessel and process for producing 18MnMoNbR steel plate with thickness of 100mm
A pressure vessel and production process technology, applied in the field of pressure vessel steel 18MnMoNbR and its 100mm thick plate production process, can solve the problems of difficult production and high production cost
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0019] Example 1:
[0020] A pressure vessel steel 18MnMoNbR, containing the following mass percentages of chemical composition (unit, wt%): C: 0.16, Si: 0.25, Mn: 1.35, Mo: 0.5, P≤0.015, S≤0.005, Als: 0.015, Nb : 0.030, Ti: 0.010, the others are Fe and residual elements.
[0021] The carbon equivalent of the chemical composition is ≤0.40.
[0022] The pressure vessel steel 18MnMoNbR has 90% tempered bainite and 10% ferrite.
[0023] Further, a production process for producing a 100mm pressure vessel steel 18MnMoNbR thick plate is provided, which includes the following steps:
[0024] a. KR hot metal pretreatment: the molten iron at the station must be stripped of the front slag and the back slag to ensure that the thickness of the slag layer is ≤20mm. After the molten iron is stirred and desulfurized by KR, the molten iron S is ≤0.005%, and the desulfurization cycle is 15min and the temperature drop is 15 ℃;
[0025] b. Converter smelting: molten iron S≤0.003%, P≤0.080%, molten ...
Example Embodiment
[0043] Example 2:
[0044] A pressure vessel steel 18MnMoNbR, containing the following mass percentages of chemical composition (unit, wt%): C: 0.18, Si: 0.35, Mn: 1.40, Mo: 0.55, P≤0.015, S≤0.005, Als: 0.025, Nb : 0.035, Ti: 0.015, the others are Fe and residual elements.
[0045] The carbon equivalent of the chemical composition is ≤0.40.
[0046] The pressure vessel steel 18MnMoNbR has 90% tempered bainite and 10% ferrite.
[0047] Further, a production process for producing a 100mm pressure vessel steel 18MnMoNbR thick plate is provided, which includes the following steps:
[0048] a. KR hot metal pretreatment: the molten iron at the station must be stripped of the front slag and the back slag to ensure that the thickness of the slag layer is ≤20mm. After the molten iron is stirred and desulfurized by KR, the molten iron S is ≤0.005%. ℃;
[0049] b. Converter smelting: molten iron S≤0.003%, P≤0.080%, molten iron temperature 1290℃, molten iron loading error is controlled by ±1...
Example Embodiment
[0067] Example 3:
[0068] A pressure vessel steel 18MnMoNbR, containing the following mass percentages of chemical composition (unit, wt%): C: 0.20, Si: 0.45, Mn: 1.45, Mo: 0.6, P≤0.015, S≤0.005, Als: 0.040, Nb : 0.040, Ti: 0.020, the others are Fe and residual elements.
[0069] The carbon equivalent of the chemical composition is ≤0.40.
[0070] The pressure vessel steel 18MnMoNbR has 90% tempered bainite and 10% ferrite.
[0071] Further, a production process for producing a 100mm pressure vessel steel 18MnMoNbR thick plate is provided, which includes the following steps:
[0072] a. KR hot metal pretreatment: the molten iron at the station must be stripped of the front slag and the back slag to ensure that the thickness of the slag layer is ≤20mm. After the molten iron is stirred and desulfurized by KR, the molten iron S is ≤0.005%. ℃;
[0073] b. Converter smelting: molten iron entering the furnace S≤0.003%, P≤0.080%, molten iron temperature 1310℃, molten iron loading error i...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap