Preparation method of CoMn spinel coating on SOFC (Solid Oxide Fuel Cell) metal connector surface
A technology of spinel coating and metal connector, which is applied in the direction of metal material coating process, coating, fuel cell, etc., and can solve the problems of complex equipment, high cost, poor bonding strength between coating and metal substrate, etc. , to achieve the effect of simple process method, improved preparation efficiency and low cost
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0029] 1) Metal surface pretreatment: use 400-1200 # Grind the sample step by step with a suitable sandpaper, put the sample in an acetone solution for ultrasonic-assisted degreasing and cleaning for 3 to 5 minutes, then rinse with deionized water, and dry it for later use.
[0030] 2) Deposition electrode surface pretreatment: the selected pure Co (purity greater than 99.9wt.%, the same as the following examples) and pure Mn (purity greater than 99.9wt.%, the same as the following examples) electrode rods (both diameters are 2mm) ) into acetone solution for ultrasonic-assisted degreasing for 3 to 5 minutes, then rinsed with deionized water, and dried for later use.
[0031] 3) Alloy coating formation process: use the selected metal sample as the base material, as the cathode in the deposition process, connect the cathode of the power supply equipment, select the first good Mn electrode as the deposition electrode, adjust the process parameters, and set the deposition process ...
Embodiment 2
[0033] 1) Metal surface pretreatment: use 400-1200 # Grind the sample step by step with a suitable sandpaper, put the sample in an acetone solution for ultrasonic-assisted degreasing and cleaning for 3 to 5 minutes, then rinse with deionized water, and dry it for later use.
[0034] 2) Surface pretreatment of the deposition electrode: put the selected pure Co and pure Mn electrode rods (both with a diameter of 1.5mm) into the acetone solution for ultrasonic-assisted degreasing and cleaning for 3-5 minutes, then rinse with deionized water, and dry them for later use .
[0035]3) Alloy coating formation process: use the selected metal sample as the base material, as the cathode in the deposition process, connect the cathode of the power supply equipment, select the processed Mn electrode as the deposition electrode, adjust the process parameters, and set the deposition Process parameters, the deposition voltage is 100V, the frequency is 400hz, the pulse width is 200μs, the powe...
Embodiment 3
[0037] 1) Metal surface pretreatment: use 400-1200 # Grind the sample step by step with a suitable sandpaper, put the sample in an acetone solution for ultrasonic-assisted degreasing and cleaning for 3 to 5 minutes, then rinse with deionized water, and dry it for later use.
[0038] 2) Surface pretreatment of the deposition electrode: put the selected pure Co and pure Mn electrode rods (0.5mm in diameter) into the acetone solution for ultrasonic-assisted degreasing and cleaning for 3-5 minutes, then rinse with deionized water, and dry them for later use .
[0039] 3) Alloy coating formation process: use the selected metal sample as the base material, as the cathode in the deposition process, connect the cathode of the power supply equipment, select the processed Mn electrode as the deposition electrode, adjust the process parameters, and set the deposition process Parameters, the deposition voltage is 80V, the frequency is 400hz, the pulse width is 200μs, the argon flow rate ...
PUM
Property | Measurement | Unit |
---|---|---|
diameter | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com