Low-smoke-intensity and high-sulfur fixation adhesion agent

A technology of binder and consolidating agent, applied in the field of chemical industry, can solve problems such as deficiencies, and achieve the effects of good mechanical properties, good waterproofness, and high cold and hot strength

Inactive Publication Date: 2013-07-24
徐祥兵
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these schemes have various deficiencies in terms of production cost, strength of briquette and water resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-smoke-intensity and high-sulfur fixation adhesion agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A binder with low smoke and high sulfur-fixing performance, which is composed of the following components in parts by weight: 40 parts of magnesium oxychloride cement, 10 parts of bentonite, 20 parts of waste furnace slag from steelmaking furnace, 5 parts of graphite tailings, phosphoric acid 2 parts of trisodium, 8 parts of sodium silicate, 3 parts of magnesite, 7 parts of magnesium chloride, and 5 parts of polyethylene glycol; each component was mixed by weight, stirred for 48 hours, and after being powdery, the It can be obtained by pressing and forming under pressure.

Embodiment 2

[0014] A binder with low smoke and high sulfur-fixing performance, which is composed of the following components in parts by weight: 30 parts of magnesium oxychloride cement, 20 parts of bentonite, 20 parts of waste furnace slag from steelmaking furnace, 5 parts of graphite tailings, phosphoric acid 2 parts of trisodium, 8 parts of sodium silicate, 3 parts of magnesite, 7 parts of magnesium chloride, and 5 parts of polyethylene glycol; each component was mixed by weight, stirred for 48 hours, and after being powdery, the It can be obtained by pressing and forming under pressure.

Embodiment 3

[0016] A binder with low smoke and high sulfur-fixing performance, which is composed of the following components in parts by weight: 35 parts of magnesium oxychloride cement, 15 parts of bentonite, 20 parts of waste furnace slag from steelmaking furnaces, 5 parts of graphite tailings, phosphoric acid 2 parts of trisodium, 8 parts of sodium silicate, 3 parts of magnesite, 7 parts of magnesium chloride, and 5 parts of polyethylene glycol; each component was mixed by weight, stirred for 48 hours, and after being powdery, the It can be obtained by pressing and forming under pressure.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a low-smoke-intensity and high-sulfur fixation adhesion agent. The adhesion agent consists of the following components in parts by weight: 30-40 parts of magnesium oxychloride cement, 10-20 parts of bentonite, 20 parts of steel furnace waste slag, 5 parts of graphite gangue, 2 parts of trisodium phosphate, 8 parts of sodium silicate, 3 parts of a solidification agent, 7 parts of a hardening agent and 5 parts of polyethylene glycol. The low-smoke-intensity and high-sulfur fixation adhesion agent provided by the invention has the advantages of low smoke blackness and good sulfur fixation performance; moreover, combustion performance of briquette coal cannot be changed, no calorific value is not reduced, briquette coal has good waterproofness, cold and hot strength is high and mechanical performance is good.

Description

technical field [0001] The invention relates to the field of chemical industry, in particular to a binder. Background technique [0002] The gasification industrial briquettes currently produced in China have many defects, such as briquettes are not waterproof, need to be dried, high cost, low heat and cold intensity, poor gasification effect, black heart, poor reducibility, low gasification rate, oxygen High content, low carbon monoxide output, low calorific value of gas. Not suitable for mass production and cannot be transported over long distances. There are many kinds of binders used at home and abroad, such as coal tar, asphalt, papermaking waste liquid, animal blood (blood meal), biochemical sludge, cement, calcium carbide and so on. But these schemes or on the production cost, or on the briquette strength, water resistance, there are deficiencies in varying degrees. Contents of the invention [0003] In order to solve the deficiencies of the prior art, the object...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C10L5/10
Inventor 徐祥兵
Owner 徐祥兵
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap