Photosensitive dry film and detection method thereof

A technology of photosensitive dry film and photosensitive resin, which is applied in the direction of optics, photomechanical equipment, and weighing by removing certain components, can solve problems that affect the health of employees, unpleasant odors, air pollution, etc., and achieve a clear environment Benefits and social benefits, reducing air pollution, and improving the working environment

Active Publication Date: 2013-08-07
湖南五江高科技材料有限公司
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The photosensitive resin is in a semi-dry state, and the photosensitive resin used in the photosensitive dry film in the prior art will emit an extremely unpleasant odor, which has a relatively large impact on the working environment, thereby seriously affecting the health of employees; at the same time, this odor Odor is also an unfavorable factor causing air pollution
At present, some manufacturers of photosensitive dry film also try to add some substances similar to industrial flavors in the photosensitive resin composition, but the effect is not good, and the odor of photosensitive dry film that plagues the industry has not been solved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] (1) Weigh 45 parts of hydrogenated polydecene PAO6, 20 parts of polyoxyethylene lauryl (lauryl) ether, and 15 parts of diisooctyl succinate according to the weight ratio of the deodorant components. Sodium ester sulfonate, 3 parts of eugenol, and then mixed to obtain a deodorant.

[0040] (2) Prepare an alkali-soluble resin, which is synthesized from styrene, methyl methacrylate, and hydroxyethyl acrylate under the action of the catalyst azobisisobutyronitrile. This preparation process is a known technology, so it will not be described in detail.

[0041] (3) Prepare a photopolymerizable compound. The photopolymerizable compound in this example is composed of ethoxylated bisphenol A diacrylate and polyethylene glycol dimethacrylate with a molecular weight of 1000. 100 parts by weight of the polymerizable compound is taken as the basis for measurement, and 20 parts of ethoxylated bisphenol A diacrylate and 80 parts of polyethylene glycol dimethacrylate with a molecular ...

Embodiment 2

[0045] (1) Weigh 50 parts of hydrogenated polydecene PAO6, 25 parts of polyoxyethylene lauryl (lauryl) ether, and 20 parts of diisooctyl succinate according to the weight ratio of the deodorant components. Sodium ester sulfonate, 5 parts of eugenol, then mix to obtain deodorant.

[0046] (2) Prepare an alkali-soluble resin, which is synthesized from styrene, ethyl methacrylate, and hydroxybutyl acrylate under the action of the catalyst cumene hydroperoxide. This preparation process is a known technology, so it will not be described in detail.

[0047] (3) Prepare a photopolymerizable compound. The photopolymerizable compound in this example is composed of ethoxylated bisphenol A diacrylate and polyethylene glycol dimethacrylate with a molecular weight of 1500. 100 parts by weight of the polymerizable compound is taken as the basis for measurement, and 45 parts of ethoxylated bisphenol A diacrylate and 55 parts of polyethylene glycol dimethacrylate with a molecular weight of 1...

Embodiment 3

[0051] (1) Weigh 55 parts of hydrogenated polydecene PAO6, 30 parts of polyoxyethylene lauryl (lauryl) ether, and 25 parts of diisooctyl succinate according to the weight ratio of the deodorant components. Sodium ester sulfonate, 7 parts of eugenol, then mixed to obtain a deodorant.

[0052] (2) Prepare an alkali-soluble resin, which is synthesized from styrene, butyl methacrylate, and isooctyl acrylate under the action of a catalyst called tert-butyl hydroperoxide. This preparation process is a known technology, so it will not be described in detail.

[0053] (3) Prepare a photopolymerizable compound. The photopolymerizable compound in this example is composed of ethoxylated bisphenol A diacrylate and polyethylene glycol dimethacrylate with a molecular weight of 2000. 100 parts by weight of the polymerizable compound is taken as the basis for measurement, and 70 parts of ethoxylated bisphenol A diacrylate and 30 parts of polyethylene glycol dimethacrylate with a molecular we...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a photosensitive dry film which sequentially comprises a PET (Polyethylene Terephthalate) support film layer, a photosensitive resin layer and a PE (Polyethylene) protective film layer, wherein the photosensitive resin layer mainly comprises the following materials in parts by weight: 60-70 parts of alkali-soluble resin, 15-25 parts of a polymerizability compound with at least one ethylene unsaturated base, 1-2 parts of a photopolymerization initiator and 0.01-0.1 parts of deodorant. The deodorant can exert a solubilizing function on a low polymer in the photosensitive resin layer, and can inhibit volatilization of the low polymer, so that the photosensitive dry film can inhibit or eliminate the original distinctive odor in the photosensitive resin layer. After the deodorant is added, the performances, such as photosensitiveness, mechanical strength and resolving power of the photosensitive dry film are not affected.

Description

technical field [0001] The invention relates to a photosensitive dry film, in particular to a photosensitive dry film with suppressed or eliminated special odor; the invention also relates to a detection method of the photosensitive dry film. Background technique [0002] With the improvement of people's health awareness, more and more attention is paid to the requirements of the working environment. As we all know, in the production process of printed circuit boards, a photosensitive dry film is used to form a circuit pattern, and the photosensitive dry film includes a supporting base film, a photosensitive resin and a protective film. The photosensitive resin is in a semi-dry state, and the photosensitive resin used in the photosensitive dry film in the prior art will emit an extremely unpleasant odor, which has a relatively large impact on the working environment, thereby seriously affecting the health of employees; at the same time, this odor Odor is also an unfavorab...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G03F7/11G03F7/027G03F7/004G01N5/04
Inventor 肖志义王爱军
Owner 湖南五江高科技材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com