Wood-plastic material and production method thereof

A technology of wood-plastic materials and thermoplastics, which is applied in the field of wood-plastic materials, can solve the problems that cement materials and wood materials cannot meet the requirements of outdoor use, such as durability and beauty, and achieve the effects of beautiful appearance, reduced environmental pollution, and stable quality

Inactive Publication Date: 2013-08-28
QINGDAO ENVIRONMENTAL PROTECTION MATERIAL WOOD RHINE
View PDF3 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problem that cement materials and wood materials in the prior art cannot meet the durability and beauty of outdoor use, the present invention provides a wood-plastic material with wood patterns, beautiful and durable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] 1) Grinding 30kg polyvinyl chloride material into 10-50 mesh plastic powder;

[0022] 2) Put plastic powder, 35kg wood flour, 35kg bran powder, 0.3kg antioxidant 1010, 0.15kg phenyl phthalate, 1kg polyethylene wax, 0.5kg silane coupling agent, 2.5kg stearic acid in a mixer Keep the temperature at 45°C and mix for 6 hours;

[0023] 3) Put the uniformly mixed material into a screw extruder, control the temperature at 140°C, and mix for 6 hours;

[0024] 4) Extrude the profile according to the shape of the mold, draw it after vacuum setting, cooling, and then divide it into the required size.

Embodiment 2

[0026] 1) Grinding 28kg of polyethylene material into 10-50 mesh plastic powder;

[0027] 2) Mix plastic powder with 33kg wood powder, 37kg bran powder, 0.2kg antioxidant DLTP, 0.1kg resorcinol monobenzoate, 1.5kg polyethylene wax, 0.25kg titanate coupling agent, 3.5kg hard Fatty acid was kept at a temperature of 30°C in the mixer, and mixed for 10 hours;

[0028] 3) Put the uniformly mixed material into a screw extruder, control the temperature at 80°C, and mix for 10 hours;

[0029] 4) Extrude the profile according to the shape of the mold, draw it after vacuum setting, cooling, and then divide it into the required size.

Embodiment 3

[0031] 1) Grinding 32kg polystyrene material into 10-50 mesh plastic powder;

[0032] 2) Mix plastic powder with 37kg wood powder, 33kg bran powder, 0.4kg antioxidant 264, 0.2kg2-hydroxy-4-methoxybenzophenone, 0.5kg polyethylene wax, 0.75kg titanate coupling agent 1.5kg of stearic acid was kept in the mixer at a temperature of 60°C and mixed for 2 hours;

[0033] 3) Put the uniformly mixed material into a screw extruder, control the temperature at 150°C, and mix for 2 hours;

[0034] 4) Extrude the profile according to the shape of the mold, draw it after vacuum setting, cooling, and then divide it into the required size.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
impact strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a wood-plastic material and a production method thereof. The wood-plastic material comprises the following components in parts by weight: 28-32 parts of thermoplastic, 33-37 parts of wood meal, 33-37 parts of bran powder, 0.2-0.4 part of antioxidant, 0.1-0.2 part of anti-ultraviolet agent, 0.5-1.5 parts of polyethylene wax, 0.25-0.75 part of coupling agent and 1.5-3.5 parts of stearic acid. The thermoplastic powder is mixed with the wood meal and bran powder, and the formula and processing technique are adjusted, thereby preparing the wood-plastic material with stable quality and beautiful appearance; the plastic powder, wood meal and bran powder can adopt tailings or waste, thereby saving the energy and reducing the environmental pollution; and the wood-plastic material has the advantages of favorable dimensional stability and high aging resistance, and can resist the high temperature of 200 DEG C, and the shock strength is 80 kJ / m<2>.

Description

technical field [0001] The invention relates to a novel material, in particular to a wood-plastic material compounded with wood powder and thermoplastic powder and a production method thereof. Background technique [0002] Cement products are often used as building materials for outdoor use. This material is heavy and needs to be constructed in situ. It requires high proficiency of the construction personnel. If the processing is not good, it will be difficult to repair later, and for some high-end products such as tourist attractions. The use of cement materials for gazebos or plank roads is very unsightly. [0003] Wooden materials are very beautiful due to the natural growth of wood grain, but when used outdoors, because the wood has a loose internal structure, it will absorb water and moisture. If it is in a humid environment for a long time, it will rot and require frequent maintenance. . Contents of the invention [0004] In order to solve the problem that cement m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/12C08L27/06C08L25/06C08L59/00C08L69/00C08L77/00C08L33/00C08L81/06C08L71/12C08L71/00C08L97/02C08K5/00
Inventor 仇兆阳
Owner QINGDAO ENVIRONMENTAL PROTECTION MATERIAL WOOD RHINE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com