Architectural SBS (styrene-butadiene-styrene) modified asphalt waterproof paint

A technology of modified bitumen and waterproof coating, which is used in construction asphalt-based waterproof coating and various construction waterproof engineering fields, can solve the problems of low elongation, poor flexibility of bitumen, easy cracking, etc., so as to improve corrosion resistance and aging resistance. Performance, mechanical strength improvement, good thixotropic creep effect

Inactive Publication Date: 2013-09-11
SHANDONG INNOWIT CHEM
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the disadvantages of poor flexibility, low elongation, easy cracking at low temperature, especially hot flow and brittleness of asphalt, the above two modified asphalt coatings have defects to varying degrees during use.
Among them, the production method of water-emulsified asphalt paint is cumbersome, and the biggest disadvantage is that because the paint is water-based, the film-forming compactness is poor, so the water resistance and aging resistance are poor; solvent-based asphalt paint cannot be used indoors due to the presence of a large amount of organic matter.
Especially in poorly ventilated kitchens and bathrooms and buildings, one is to prolong the period of construction work, and the other is to cause health effects on workers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Architectural SBS (styrene-butadiene-styrene) modified asphalt waterproof paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A kind of SBS modified asphalt waterproof paint for construction, its raw material composition is: asphalt: 40 weight parts, waste engine oil: 20 weight parts, talcum powder: 10 weight parts, SBS: 4 weight parts, zinc-aluminum alloy powder: 1 weight part , Phytate: 3 parts by weight, Isopropanol: 1 part by weight, Sodium hypophosphite: 3 parts by weight, Cerium nitrate: 0.2 parts by weight, Lanthanum nitrate: 1.5 parts by weight, C16 alcohol: 0.2 parts by weight, Glycerin : 0.5 parts by weight, polydimethylsiloxane: 0.05 parts by weight, benzalkonium chloride: 0.1 parts by weight;

[0031] Wherein, the asphalt is a mixture of 10# asphalt and 100# asphalt in a ratio of 1:7;

[0032] The talcum powder fineness is 80 orders;

[0033] The mass percentage of each component of the zinc-aluminum alloy powder is: Zn: 50%, the balance is Al and unavoidable impurities.

[0034] Above-mentioned SBS modified asphalt waterproof paint for building, its preparation method is:

[00...

Embodiment 2

[0042]A kind of SBS modified asphalt waterproof paint for construction, its raw material composition is: asphalt: 50 weight parts, waste engine oil: 15 weight parts, talcum powder: 15 weight parts, SBS: 2 weight parts, zinc-aluminum alloy powder: 5 weight parts , Phytate: 1 part by weight, Isopropanol: 3 parts by weight, Sodium hypophosphite: 1 part by weight, Cerium nitrate: 0.5 parts by weight, Lanthanum nitrate: 0.5 parts by weight, C16 alcohol: 1.5 parts by weight, Glycerin : 0.2 parts by weight, polydimethylsiloxane: 0.2 parts by weight, benzalkonium chloride: 0.01 parts by weight;

[0043] Wherein, the asphalt is a mixture of 10# asphalt and 100# asphalt in a ratio of 1:7;

[0044] The talcum powder fineness is 100 orders;

[0045] The mass percentage of each component of the zinc-aluminum alloy powder is: Zn: 60%, the balance is Al and unavoidable impurities.

[0046] The above-mentioned SBS modified asphalt waterproof paint for construction, its preparation method is...

Embodiment 3

[0048] A kind of SBS modified asphalt waterproof paint for construction, its raw material composition is: asphalt: 45 parts by weight, waste engine oil: 18 parts by weight, talcum powder: 13 parts by weight, SBS: 3 parts by weight, zinc-aluminum alloy powder: 3 parts by weight , Phytate: 2 parts by weight, Isopropanol: 2 parts by weight, Sodium hypophosphite: 2 parts by weight, Cerium nitrate: 0.35 parts by weight, Lanthanum nitrate: 1 part by weight, C16 alcohol: 0.8 parts by weight, Glycerin : 0.35 parts by weight, polydimethylsiloxane: 0.1 parts by weight, benzalkonium chloride: 0.05 parts by weight;

[0049] Wherein, the asphalt is a mixture of 10# asphalt and 100# asphalt in a ratio of 1:7;

[0050] The talcum powder fineness is 90 orders;

[0051] The mass percentage of each component of the zinc-aluminum alloy powder is: Zn: 55%, the balance is Al and unavoidable impurities.

[0052] The above-mentioned SBS modified asphalt waterproof paint for construction, its prepa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an architectural SBS (styrene-butadiene-styrene) modified asphalt waterproof paint which is prepared from asphalt, used machine oil, talcum powder, SBS, zinc-aluminum alloy powder, phytate, isopropanol, sodium hypophosphite, cerium nitrate, lanthanum nitrate, C16 alcohol, glycerol, polydimethylsiloxane, benzalkonium chloride. The modified asphalt waterproof paint disclosed by the invention is suitable for various industrial and civil buildings, has the characteristics of water resistance, corrosion resistance, moisture resistance, mold resistance and long service life, is convenient for construction, and is easy for construction for any part with a complex shape and crossed pipelines.

Description

technical field [0001] The invention relates to the field of chemical coatings, in particular to an asphalt-based waterproof coating for construction, which is mainly used in various construction waterproofing projects. Background technique [0002] Asphalt has a long history of being used for waterproofing. This is because asphalt has good waterproofness and durability, and it is still an important material for building waterproofing. It has cheap and abundant raw materials, easy construction, strong waterproof function, and long waterproofing period. Salient features. Domestic modified asphalt coatings are mainly solvent-based and water-emulsion modified asphalt waterproof coatings. However, due to the disadvantages of poor flexibility, low elongation, easy cracking at low temperature, and especially hot flow and brittleness in asphalt, the above two modified asphalt coatings have defects in varying degrees during use. Among them, the production method of water-emulsifie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D195/00C09D153/02C09D183/04C09D7/12
Inventor 邵昌元
Owner SHANDONG INNOWIT CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com