Hydroxyl-terminated phenyl amino polyether modified silicone oil

A technology of phenylamino-terminated polyether and polyether modification, which is used in textiles, papermaking, fiber processing and other directions to achieve good smoothness and good stability.

Inactive Publication Date: 2013-10-02
黄山市强力化工有限公司
View PDF7 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, there is no silicone polymer that provides heat resistance while maintaining softness and anti-yellowing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydroxyl-terminated phenyl amino polyether modified silicone oil
  • Hydroxyl-terminated phenyl amino polyether modified silicone oil
  • Hydroxyl-terminated phenyl amino polyether modified silicone oil

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Example 1: Preparation of a hydroxyl-terminated phenylamino polyether modified silicone oil

[0025] Step 1) Preparation of polyether-modified aminosilane: Add 150g of 3-piperazinylpropylmethyldimethoxysilane and 175g of alkyl epoxy polyether into a fully dried reaction kettle, seal it and raise the temperature After reaching 60°C, stirring and reacting for 60 minutes; adding catalyst tetramethylammonium hydroxide accounting for 1% of the total weight of the reactants, and continuing to keep warm for 5 hours to obtain the product; the structural formula of the alkyl epoxy polyether is as follows:

[0026]

[0027] In the formula: a and b are both positive integers, and: a=2~8, b=2~15, 0≤n≤4 (integer).

[0028] Step 2) Preparation of hydroxy-terminated phenylamino polyether-modified silicone oil: Take 100g of polyether-modified aminosilane, 200g of dimethoxydiphenylsilane, and 20g of octamethylcyclotetrasiloxane prepared above to react In the kettle, the temperature ...

Embodiment 2

[0030] Example 2: Preparation of a hydroxyl-terminated phenylamino polyether modified silicone oil

[0031] Step 1) Preparation of polyether-modified aminosilane: Add 250g of 3-cyclohexyl-aminopropylmethyldimethoxysilane and 85g of alkyl epoxy polyether into a fully dried reaction kettle, seal it and raise the temperature to 95°C, stirred and reacted for 30 minutes; added a catalyst tetrabutylphosphine hydroxide accounting for 5% of the total weight of the reactants, and continued the heat preservation reaction for 1 hour to obtain final product; the structural formula of the alkyl epoxy polyether is as follows:

[0032]

[0033] In the formula: a and b are both positive integers, and: a=2~8, b=2~15, 0≤n≤4 (integer).

[0034] Step 2) Preparation of hydroxyl-terminated phenylamino polyether-modified silicone oil: add 100 g of polyether-modified aminosilane, 50 g of diphenyldimethoxysilane, and 200 g of octamethylcyclotetrasiloxane prepared above to the reaction In the kettl...

Embodiment 3

[0037] Example 3: Preparation of a hydroxyl-terminated phenylamino polyether modified silicone oil

[0038] Step 1) Preparation of polyether-modified aminosilane: Add 20g of 3-(N,N-dimethylaminopropyl)-aminopropylmethyldimethoxysilane and 120g of alkyl epoxy polyether to In a well-dried reactor, seal the temperature up to 85°C, and stir and react for 45 minutes; add catalyst tetramethylammonium hydroxide accounting for 3% of the total weight of the reactants, and continue to keep warm for 3 hours to obtain; the alkyl ring The structural formula of oxypolyether is as follows:

[0039]

[0040] In the formula: a and b are both positive integers, and: a=2~8, b=2~15, 0≤n≤4 (integer).

[0041]Step 2) Preparation of hydroxyl-terminated phenylamino polyether-modified silicone oil: add 200 g of polyether-modified aminosilane, 150 g of diphenyldimethoxysilane, and 100 g of octamethylcyclotetrasiloxane prepared above to the reaction In the still, heat up to 100°C; add catalyst tetr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a hydroxyl-terminated phenyl amino polyether modified silicone oil. According to the invention, polyether modified amino silane is firstly prepared from amino silane and alkyl epoxy polyether, and then the hydroxyl-terminated phenyl amino polyether modified silicone oil is prepared from polyether modified amino silane, phenylsilane and octamethylcyclotetrasiloxane in the presence of a catalyst. Compared with the prior art, alkyl phenyl silane, polyether modified amino silane and octamethylcyclotetrasiloxane are synthesized into a brand-new hydroxyl-terminated phenyl polyether modified silicone oil through a polymerization balanced reaction. The microemulsion type softener emulsified by the silicone oil is soft and smooth in hand feel and excellent in yellowing resistance and temperature resistance when used for finishing textiles; the product is good in stability of shear force, centrifugal force, electrolyte, hard water and the like, and is particularly suitable for surface treatment of polyester fibers.

Description

technical field [0001] The invention relates to a silicone polymer, in particular to a hydroxyl-terminated phenylamino polyether modified silicone oil. Background technique [0002] Amino-modified silicone oil is widely used in textile printing and dyeing, leather, papermaking, and daily necessities care due to its excellent and outstanding soft and smooth feel. However, because the contained amino groups, especially the primary amino groups, are easily oxidized, the white and light-colored fabrics after finishing are yellowed, and the temperature resistance of the amino groups is poor, which affects the finishing effect of the fabric and the aesthetics of clothing. There are many ways to modify amino groups to inhibit or reduce yellowing. Such as modification with epoxy group, epoxy group and acrylate co-modification; modification with polyether isocyanate and epoxy; modification with polyether carboxylic acid containing amide group; modification with acylating agent (such...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G77/46D06M15/647
Inventor 邱万军叶光华
Owner 黄山市强力化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com