Novel metal magnetic lubricating oil additive and preparation method thereof

A technology of lubricating oil additives and additives, applied in the direction of additives, lubricating compositions, petroleum industry, etc., can solve the problems of environmental pollution, discharge of a large amount of waste water, waste gas and pollutants, and achieve the effect of avoiding corrosion

Inactive Publication Date: 2013-10-02
LIAONING QIZHONG LUBRICATING OIL MFG
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Especially lubricating oil additives containing elements such as sulfur, phosphorus or chlorine will discharge a larg

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] 1. Synthesis of mixed amides

[0025] Put tall oil and diethanolamine in a container, react at 100°C under vacuum (pressure=0.10MPa) for 4 hours, then add oleic acid methyl ester, adjust pH=10, and continue the reaction at 100°C under nitrogen protection 3 hours, obtain mixed amide;

[0026] Tall oil: diethanolamine: methyl oleate = 2.5: 3.5: 1.5 (molar ratio).

[0027] 2. Synthesis of metal magnetic additives

[0028] Mix 50 grams of the mixed amide prepared above with 4.5 grams of molybdenum oxide and 4.5 grams of tungsten oxide, stir evenly, add 6 grams of hydroxyethylethylenediamine, add 6 grams of ammonia water, and react for 4 hours at a temperature of 90 ° C and a pressure of 0.15 MPa ; Increase the temperature to 180°C and continue the reaction for 3 hours under the same pressure. Then lower the temperature to 100°C, vacuumize to a pressure of 0.1MPa, and extract low-boiling substances; finally filter to obtain a brown-red metallic magnetic additive product. ...

Embodiment 2

[0031] 1. Synthesis of mixed amides

[0032] Put tall oil and diethanolamine in a container, react at 100°C under vacuum (pressure=0.10MPa) for 4 hours, then add oleic acid methyl ester, adjust pH=10, and continue at 100°C under nitrogen protection Reacted for 3 hours to obtain mixed amides;

[0033] Tall oil: diethanolamine: methyl oleate = 2:3:1 (molar ratio).

[0034] 2. Synthesis of metal magnetic additives

[0035] Mix 100 grams of the mixed amide prepared above with 9.5 grams of molybdenum oxide and 9.5 grams of tungsten oxide, stir evenly, add 15 grams of hydroxyethylethylenediamine, add 15 grams of ammonia water, and react at a temperature of 90 ° C and a pressure of 0.15 MPa for 5 hours; increase the temperature to 180° C., and continue the reaction for 4 hours under the condition of constant pressure. Then lower the temperature to 100°C, vacuumize for 2 hours until the pressure reaches 0.1MPa, and extract low-boiling substances; finally filter to obtain a brown-re...

Embodiment 3

[0038] 1. Synthesis of mixed amides

[0039] Put tall oil and diethanolamine in a container, react at 100°C under vacuum (pressure=0.10MPa) for 4.5 hours, then add oleic acid methyl ester, adjust pH=10, and continue to react at 100°C under nitrogen protection conditions for 3 Hour, obtain mixed amide;

[0040] Tall oil: diethanolamine: methyl oleate = 2:3.5:1 (molar ratio).

[0041] 2. Synthesis of metal magnetic additives

[0042] Mix 70 grams of the mixed amide prepared above with 6 grams of molybdenum oxide and 6 grams of tungsten oxide, stir evenly, add 9 grams of hydroxyethylethylenediamine, add 10 grams of ammonia water, and react at a temperature of 90 ° C and a pressure of 0.15 Mpa for 4 hours; increase the temperature to 180° C., and continue the reaction for 4 hours under the condition of constant pressure. Then lower the temperature to 100°C, vacuumize to a pressure of 0.1MPa, and extract low-boiling substances; finally filter to obtain a brown-red metallic magne...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Wear scar diameteraaaaaaaaaa
Wear scar diameteraaaaaaaaaa
Login to view more

Abstract

A purpose of the present invention is to provide a novel environmental protection non-sulfur-phosphorus metal magnetic lubricating oil additive with characteristics of simple production method, low cost, good oil solubility and high yield, and a preparation method thereof. The novel metal magnetic lubricating oil additive is characterized in that the additive is prepared from mixed amide, molybdenum oxide, tungsten oxide, hydroxyethyl ethylene diamine and ammonia water according to a weight ratio of 100:8.5-10:8.5-10:10-15:10-15, wherein the mixed amide is prepared through carrying out a reaction of tall oil, diethanolamine and methyl oleate. The additive is an oil-soluble metal magnetic tungsten-molybdenum-nitrogen complex, is a friction modifier, an anti-wear agent and an antioxidant for internal combustion engine motor lubricating oil, has a significant oil saving effect, and does not contain sulfur and phosphorus so as to further provide advantages of energy saving and environmental protection.

Description

technical field [0001] The invention belongs to the field of chemical synthesis, and in particular relates to the synthesis of oil-soluble metal magnetic tungsten and molybdenum lubricating oil additive compounds. Background technique [0002] In order to increase the anti-friction and anti-wear effect of lubricating oil, a small amount of lubricating oil additives are usually added to the lubricating oil. The traditional lubricating oil additives are sulfur, phosphorus or chlorine type anti-wear agents, which are corrosive to friction pair materials. selective. In particular, lubricating oil additives containing elements such as sulfur, phosphorus or chlorine will discharge a large amount of waste water, waste gas and pollutants during production and use, thereby causing pollution to the environment. [0003] In recent years, with the rapid development of the automobile industry, especially the growing demand for energy saving, emission reduction, low-carbon and environmen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M141/06C10N30/06
Inventor 陈永强罗兰·菲舍尔加里胡·伦佩尔李浩印王严绪周彦国
Owner LIAONING QIZHONG LUBRICATING OIL MFG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap