Water-resistance finishing paint for pleasure boats, and preparation method thereof

A technology for boating and painting, applied in coatings, polyester coatings, polyamide coatings, etc., can solve the problems of water resistance, gloss retention, and insufficient wear resistance, and achieve excellent gloss retention, durability, and bright and full color. Effect

Active Publication Date: 2015-07-01
苏州靖羽新材料有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Technical issues solved: Aiming at the disadvantages of insufficient water resistance, gloss retention and wear resistance of existing paints for pleasure boats, the present invention provides a water resistance and gloss retention paint for pleasure boats and a preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] This embodiment provides a water-resistant and gloss-retaining paint for pleasure boats, which contains the following components in parts by mass:

[0039] Acrylic modified alkyd resin 15 parts

[0040] 20 parts epoxy resin

[0041] Perchlorinated polyethylene 10 parts

[0042] Acrylic monomer 5 parts

[0043] Titanium dioxide 10 parts

[0044] Carbon black 5 parts

[0045] Wollastonite 20 parts

[0046] Polyamide 12 parts

[0047] Benzoyl peroxide 0.3 parts

[0048] 0.5 parts of 2,4-dihydroxybenzophenone

[0049] Cyclohexanone 7 parts

[0050] 3 parts benzoic acid

[0051] Butanol 6 parts.

[0052] The preparation steps of water-resistant and gloss-retaining paint for pleasure boats are as follows:

[0053] Step 1: Add acrylic modified alkyd resin, epoxy resin, cyclohexanone, benzoic acid and butanol into a three-necked flask, add and stir in a water bath at 60-70°C to dissolve the resin, and then use a 254 mesh Number / cm (100 mesh) standard sieve to remove...

Embodiment 2

[0057] This embodiment provides a water-resistant and gloss-retaining paint for pleasure boats, which contains the following components in parts by mass:

[0058] Acrylic modified alkyd resin 18 parts

[0059] 25 parts epoxy resin

[0060] Perchlorinated polyethylene 13 parts

[0061] Acrylic monomer 6 parts

[0062] Titanium dioxide 15 parts

[0063] Carbon black 7 parts

[0064] Wollastonite 25 parts

[0065] Polyamide 15 parts

[0066] Benzoyl peroxide 0.5 parts

[0067] 0.7 parts of 2,4-dihydroxybenzophenone

[0068] Cyclohexanone 8.5 parts

[0069] 4.5 parts of benzoic acid

[0070] Butanol 8 parts.

[0071] The preparation steps of water-resistant and gloss-retaining paint for pleasure boats are as follows:

[0072] Step 1: Add acrylic modified alkyd resin, epoxy resin, cyclohexanone, benzoic acid and butanol into a three-necked flask, add and stir in a water bath at 60-70°C to dissolve the resin, and then use a 254 mesh Number / cm (100 mesh) standard sieve to...

Embodiment 3

[0076] This embodiment provides a water-resistant and gloss-retaining paint for pleasure boats, which contains the following components in parts by mass:

[0077] Acrylic modified alkyd resin 25 parts

[0078] 32 parts epoxy resin

[0079] Perchlorinated polyethylene 20 parts

[0080] Acrylic monomer 11 parts

[0081] Titanium dioxide 20 parts

[0082] Carbon black 12 parts

[0083] Wollastonite 35 parts

[0084] Polyamide 25 parts

[0085] Benzoyl peroxide 0.7 parts

[0086] 1 part of 2,4-dihydroxybenzophenone

[0087] Cyclohexanone 11 parts

[0088] 7 parts of benzoic acid

[0089] Butanol 12 parts.

[0090] The preparation steps of water-resistant and gloss-retaining paint for pleasure boats are as follows:

[0091] Step 1: Add acrylic modified alkyd resin, epoxy resin, cyclohexanone, benzoic acid and butanol into a three-necked flask, add and stir in a water bath at 60-70°C to dissolve the resin, and then use a 254 mesh Number / cm (100 mesh) standard sieve to re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a water-resistance finishing paint for pleasure boats, and a preparation method thereof. The finishing paint consists of the following components in parts by mass: 15-30 parts of an acrylic modified alkyd resin, 20-35 parts of an epoxy resin, 10-25 parts of high chlorinated polyethylene, 5-13 parts of an acrylic acid monomer, 10-20 parts of titanium dioxide, 5-13 parts of carbon black, 20-40 parts of wollastonite, 12-30 parts of polyamide, 0.3-0.72 part of benzoyl peroxide, 0.5-1.2 parts of 2, 4-dihydroxy benaophenonel, 7-13 parts of cyclohexanone, 3-8 parts of benzoic acid and 6-13 parts of butanols. The water-resistance finishing paint provided by the invention has bright and rich color, excellent performances of gloss retention, water resistance, ultraviolet resistance, wear resistant and durability, and excellent decorative and protective effects on the pleasure boats.

Description

technical field [0001] The invention relates to a paint and a preparation method thereof, in particular to a water-resistant and gloss-retaining paint for pleasure boats and a preparation method thereof. Background technique [0002] There are cruise ships in many parks and tourist attractions for tourists to play and enjoy the scenery. The part above the waterline of the cruise ship is under salt spray and ultraviolet radiation for a long time, and the part below the waterline is in the water for a long time. Due to the unique purpose of the cruise ship, the paint color on the surface is relatively bright. Therefore, the paint coated on the surface of the cruise ship should have the properties of water resistance, UV resistance, gloss retention and wear resistance. However, the existing coatings for pleasure boats will lose their original luster after the pleasure boats have been used for a period of time, and their water resistance and abrasion resistance are not high. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/00C09D167/08C09D123/28C09D177/00C09D7/12C09D5/00
Inventor 庄亚东
Owner 苏州靖羽新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com