Aqueous metal antirust agent and preparation method thereof

A metal rust inhibitor, water-based technology, applied in the direction of metal material coating process, etc., can solve the problems of metal rust inhibitor not easy to dissolve, environmental pollution, etc., and achieve the effect of good dispersion and low volatile content.

Inactive Publication Date: 2013-11-27
JIANGXI GRESS TECH CORP
View PDF1 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] But the metal antirust agent of prior art is not easy to dissolve, easily causes pollution to environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] A water-based metal rust inhibitor, made of the following raw materials in parts by weight: 10 parts of dodecylbenzenesulfonic acid, 20 parts of pentaerythritol tetraoleate, 40 parts of butyl oleate, 10 parts of o-toluidine, sulfuric acid 7 parts of sodium, 10 parts of sodium hydroxide, 10 parts of sodium silicate, 40 parts of water.

[0012] The preparation method of water-based metal antirust agent comprises the following steps: mixing dodecylbenzenesulfonic acid, pentaerythritol tetraoleate, butyl oleate, o-toluidine, sodium sulfate, water, then adding sodium hydroxide and Sodium silicate, you can.

Embodiment 2

[0014] A water-based metal rust inhibitor, made from the following raw materials in parts by weight: 20 parts of dodecylbenzenesulfonic acid, 30 parts of pentaerythritol tetraoleate, 45 parts of butyl oleate, 15 parts of o-toluidine, sulfuric acid 15 parts of sodium, 20 parts of sodium hydroxide, 15 parts of sodium silicate, 50 parts of water.

[0015] The preparation method of water-based metal antirust agent comprises the following steps: mixing dodecylbenzenesulfonic acid, pentaerythritol tetraoleate, butyl oleate, o-toluidine, sodium sulfate, water, then adding sodium hydroxide and Sodium silicate, you can.

Embodiment 3

[0017] A water-based metal rust inhibitor, made of the following raw materials in parts by weight: 15 parts of dodecylbenzenesulfonic acid, 25 parts of pentaerythritol tetraoleate, 43 parts of butyl oleate, 12 parts of o-toluidine, sulfuric acid 10 parts of sodium, 15 parts of sodium hydroxide, 13 parts of sodium silicate, 45 parts of water.

[0018] The preparation method of water-based metal antirust agent comprises the following steps: mixing dodecylbenzenesulfonic acid, pentaerythritol tetraoleate, butyl oleate, o-toluidine, sodium sulfate, water, then adding sodium hydroxide and Sodium silicate, you can.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an aqueous metal antirust agent and a preparation method thereof. The aqueous metal antirust agent is prepared from following raw materials by weight: 10-20 parts of dodecylbenzenesulfonic acid, 20-30 parts of pentaerythritol tetraoleate, 40-45 parts of butyl oleate, 10-15 parts of o-toluidine, 7-15 parts of sodium sulfate, 10-20 parts of sodium hydroxide, 10-15 parts of sodium silicate and 40-50 parts of water. The aqueous metal antirust agent can be uniformly dispersed in water without impurities such as suspended solids, etc. and has good dispersity. The content of volatile organic compounds is 0.3-0.5 ppm. The content of harmful volatile compounds is low, thus having no harm to human health, and therefore the aqueous metal antirust agent is environment friendly and healthy.

Description

technical field [0001] The invention relates to a metal antirust agent, in particular to a water-based metal antirust agent and a preparation method thereof. Background technique [0002] Metal surface treatment agent refers to the general term for various chemical agents for metal surface treatment. Metal surface treatment includes degreasing, rust removal, phosphating, antirust and other substrate pretreatments, which are prepared for metal coating technology and metal protection technology. The quality of substrate pretreatment has a great influence on subsequent coating preparation and metal use. big impact. It mainly includes three categories: cleaning agent, antirust agent and phosphating solution. Metal surface treatment technology is divided into two categories: mechanical treatment (such as sandblasting, polishing, high-pressure water washing, etc.) and chemical treatment. As for coating, electroplating and other technologies, which have independently developed ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/60
Inventor 徐志坚
Owner JIANGXI GRESS TECH CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com