Double-component ceramic tile interface agent as well as preparation method and using method thereof

An interface agent, two-component technology, used in the field of building materials, can solve the problems of smooth interface, low water absorption, tile falling off, etc., to achieve the effect of improving consistency and mixing, improving compactness and improving construction performance

Active Publication Date: 2014-01-08
湖北鲁邦建材股份有限公司
View PDF3 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For this reason, the object of the present invention is to overcome the problem that existing ceramic tiles, especially vitrified tiles, are caused by low water absorption and smooth interface, and provide a two-component ceramic tile interface agent that improves the interface performance and construction performance of ceramic tiles, including A component and B component, the A component includes: cement, quartz sand, metakaolin, thickener; the B component includes: water reducing agent, toughening agent, penetrating agent, dispersant, defoaming agent Agents, fungicides, accelerators, season regulators, water

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A two-component tile interface agent, its components and weight content are: 200 parts of cement, 400 parts of quartz sand, 50 parts of metakaolin, 1 part of thickener, 1 part of water reducer, 150 parts of toughening agent, 3 parts of penetrant, 1 part of dispersant, 1 part of defoamer, 1 part of fungicide, 5 parts of accelerator, 10 parts of seasoning agent, 100 parts of water. Among them, cement is ordinary Portland cement; quartz sand is construction sand with a SiO2 weight content of 90%-99% and a particle size of 60-120 mesh; metakaolin is kaolin calcined at 600-900 ° C. %, Al2O3 weight content of 40%, average particle size of 2.179μm commercially available powder; thickener is methyl cellulose ether; water reducer is naphthalene water reducer; toughening agent is acrylic emulsion; penetrating agent is fat Alcohol polyoxyethylene ether; dispersant is triethylhexyl phosphoric acid; defoamer is organosiloxane; bactericide is commercially available water-based antise...

Embodiment 2

[0037]A two-component tile interface agent, its components and weight content are: 400 parts of cement, 400 parts of quartz sand, 10 parts of metakaolin, 0.2 parts of thickener, 1 part of water reducer, 50 parts of toughening agent, 3 parts of penetrant, 0.1 part of dispersant, 0.3 part of defoamer, 0.1 part of fungicide, 1 part of accelerator, 2 parts of seasoning agent, 100 parts of water. Among them, cement is ordinary Portland cement; quartz sand is construction sand with a SiO2 weight content of 90%-99% and a particle size of 60-120 mesh; metakaolin is kaolin calcined at 600-900 ° C. %, Al2O3 weight content is 50%, the average particle size is 2.179 μ m commercially available powder; thickener is carboxymethyl cellulose ether; water reducer is polycarboxylate water reducer; The penetrating agent is fatty alcohol polyoxyethylene ether; the dispersant is sodium lauryl sulfate; the defoamer is polyether defoamer; the bactericide is a commercially available water-based antise...

Embodiment 3

[0041] A two-component tile interface agent, its components and weight content are: 300 parts of cement, 300 parts of quartz sand, 40 parts of metakaolin, 0.5 parts of thickener, 5 parts of water reducer, 95 parts of toughening agent, 4 parts of penetrant, 0.5 part of dispersant, 2 parts of defoamer, 0.5 part of bactericide, 2 parts of accelerator, 4 parts of seasoning agent, 100 parts of water. Among them, cement is a mixture composed of ordinary Portland cement with a weight content of 90% and sulphoaluminate cement with a weight content of 10%; quartz sand is construction sand with a weight content of 90% SiO2 and a particle size of 60-120 mesh; metakaolin is kaolin Calcined at 600-900°C, the commercially available powder with SiO2 weight content of 48%, Al2O3 weight content of 46%, and average particle size of 2.179 μm is formed; the thickener is starch ether; the water reducer is naphthalene-based water reducer, A mixture of polycarboxylate water reducers in a weight rati...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
The average particle sizeaaaaaaaaaa
Bond strengthaaaaaaaaaa
Login to View More

Abstract

The invention aims at solving a ceramic tile dropping problem caused by low water absorption and a smooth interface of the existing ceramic file, especially a vitrified porcelain tile, and provides a double-component ceramic tile interface agent for improving interface performance and construction performance of a ceramic tile. The double-component ceramic tile interface agent comprises a component A and a component B, wherein the component A comprises cement, quartz sand, metakaolin and a thickener; the component B comprises a water reducing agent, a flexibilizer, a penetrating agent, a dispersing agent, an antifoaming agent, a bactericide, an accelerator, a season regulator and water. According to the invention, two strength forming materials of multiple polymers and cement are used at the same time, so that possibility of forming an interface for a second time is reduced, and bonding strength of the interface agent and the ceramic tile is improved. Besides, while construction time is ensured, setting time is shortened, construction performance is effectively improved, and long-term aesthetic sense of the ceramic tile is ensured.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a two-component ceramic tile interface agent and its preparation and use methods. Background technique [0002] Ceramic tiles are widely used as facing materials for walls and floors. They have the advantages of low water absorption, high wear resistance, uniform size, acid resistance, and no radiation. Especially in the process of home decoration, ceramic tiles are economical, beautiful, and durable. At the same time, there are various varieties, which can meet the needs of different levels and styles. People are used to using ceramic tiles as decorative materials for bathrooms and kitchens. However, after the traditional decoration construction, the tiles are prone to loosening or even falling off, which not only causes serious economic losses, but also brings troubles for re-construction. [0003] There are three main reasons for the tiles to fall off: ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/04C04B28/06C04B28/34
Inventor 陈乐舟蹇守卫张良军
Owner 湖北鲁邦建材股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com