A resilience and transformer technology, which is applied in the field of high resilience transformer gasket and its preparation, can solve the problems that the compression resilience cannot meet the sealing requirements, and achieve the best compression resilience, high mechanical strength, and good low temperature resistance.
Inactive Publication Date: 2014-01-15
ANHUI KELIN ELECTRONICS
View PDF2 Cites 7 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
With the rapid development of science and technology and modern industry, the existing rubber gasket compression resilience is far from meeting the actual sealing requirements
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0012] A high resilience transformer gasket made of the following raw materials by weight (kg): methyl vinyl rubber (N41) 80, polyurethane rubber (AR-200) 20, hexamethyldisilazane 15, gas phase white Carbon black 35, diphenylsilanediol 5, zinc oxide 1.5, stearic acid 2.5, 2,5-dimethyl-2,5-di(tert-butylperoxy)hexane 1, diisoperoxide Propylbenzene 0.5, bis-(γ-triethoxysilylpropyl) tetrasulfide 2, antioxidant RD1, antioxidant TNP2, antioxidant 10101.5, coumarone resin 10, nanopotassium feldspar 8, organic bentonite 6. Mica powder 8. Composite filler 4;
[0013] The preparation method of the composite filler is as follows: a. Weigh wollastonite, pyrophyllite and attapulgite in a weight ratio of 3:3:1 and mix them evenly, calcinate at 505°C for 4 hours, and put in hydrochloric acid with a concentration of 15% after cooling to normal temperature Soak in the solution for 2 hours, filter, wash the above-mentioned ore mixture with distilled water until neutral, dry, pulverize, and pas...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a high-resilience transformer sealing gasket and a preparation method thereof. The high-resilience transformer sealing gasket is prepared from 70-80 weight parts of methyl vinyl silicone rubber, 20-30 weight parts of polyurethane rubber, 15-20 weight parts of hexamethyldisilazane, 30-40 weight parts of fumed silica, 4-6 weight parts of diphenylsilanediol, 1-2 weight parts of zinc oxide, 2-3 weight parts of stearic acid, 1-2 weight parts of 2,5-dimethyl-2,5-di(tert-butylperoxy)hexane, 0.5-1 weight part of dicumyl peroxide, 2-3 weight parts of bis-(gamma-triethoxysilylpropyl)tetrasulfide, 1-2 weight parts of an antiager RD, 2-3 weight parts of an antiager TNP, 1-2 weight parts of an antioxidant 1010, 10-15 weight parts of coumarone resin, 5-10 weight parts of nanometer potassium feldspar, 4-8 weight parts of organobentonite, 6-12 weight parts of mica powder and 3-5 weight parts of a composite filling material. The high-resilience transformer sealing gasket is soft and smooth, has no toxicity and smell, has excellent high temperature and low temperature resistance, excellent compression resilience and high mechanical strength, can be used at a temperature of -70-250 DEG C for a long time, and does not age, deform and crack.
Description
technical field [0001] The invention relates to a high resilience transformer sealing gasket and a preparation method thereof, belonging to the technical field of sealing materials. Background technique [0002] The gasket is an important part of the transformer, which plays the role of sealing and preventing oil leakage of the transformer. With the rapid development of science and technology and modern industry, the compression resilience of existing rubber gaskets is far from meeting the actual sealing requirements. Therefore research and develop a kind of highly elastic rubber gasket has become the task of top priority. Contents of the invention [0003] The object of the present invention is to provide a high-resilience transformer gasket and a preparation method thereof, so as to improve the compression resilience of the transformer gasket. [0004] The technical scheme that the present invention adopts is as follows: [0005] A high resilience transformer gasket, ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.