Environment-friendly aqueous nano transparent UV shielding coating for highlight furniture and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
An environmentally friendly, external shielding technology, applied in the field of coatings, can solve the problems of easy aging, brittleness and peeling off of coatings
Inactive Publication Date: 2014-01-15
FORTUNE WOODEN PROD
View PDF0 Cites 6 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0007] The technical problem to be solved by the present invention is to provide a paint that solves the problem that the paint is easy to age, become brittle and falls off under the sun's ultravioletradiation, improves the surface hardness of the paint, and does not pollute the environment.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0029] The environment-friendly water-based nano-transparent UV-shielding paint for high-gloss furniture of the present invention comprises the following components:
[0030] 100 parts of deionized water, 3 parts of dispersant, nano TiO 2 5 parts, nano 3 parts, nano ZnO2 parts, nano Fe 2 o 3 5 parts, 3 parts of titanium dioxide, 4 parts of thickener, 65 parts of acrylic modified water-based polyurethane, 2 parts of preservative, 1 part of pH regulator, 5 parts of sodium hexametaphosphate.
Embodiment 2
[0032] The environment-friendly water-based nano-transparent UV-shielding paint for high-gloss furniture of the present invention comprises the following components:
[0033] 120 parts of deionized water, 4 parts of dispersant, nano TiO 2 3 parts, nano 4 parts, nano ZnO6 parts, nano Fe 2 o 3 2 parts, 4 parts of titanium dioxide, 5 parts of thickener, 70 parts of acrylic modified water-based polyurethane, 1 part of preservative, 1 part of pH regulator, 3 parts of sodium hexametaphosphate.
Embodiment 3
[0035] The environment-friendly water-based nano-transparent UV-shielding paint for high-gloss furniture of the present invention comprises the following components:
[0036] 150 parts of deionized water, 5 parts of dispersant, nano TiO 2 5 parts, nano 3 parts, nano ZnO 4 parts, nano Fe 2 o 3 3 parts, 5 parts of titanium dioxide, 5 parts of thickener, 60 parts of acrylic modified water-based polyurethane, 2 parts of preservative, 1 part of pH regulator, 5 parts of sodium hexametaphosphate.
[0037] A preparation method of environment-friendly water-based nano-transparent ultraviolet shielding paint for high-gloss furniture, comprising the following steps:
[0038] The environment-friendly water-based nano transparent UV shielding coating was prepared by blending method. Take a certain amount of polyacrylic acid modified water-based polyurethane emulsion E-106 and add 0.1% nano-TiO 2 Mix the water dispersion, stir with a high-speed mixer at a speed of 1000r / min for 1 hour a...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention relates to an environment-friendly aqueous nano transparent UV shielding coating for highlight furniture. The coating comprises the following components: deionized water, a dispersing agent, a nano inorganic slurry, titanium dioxide, a thickener, acrylic modified waterborne polyurethane, a preservative, a pH regulator and sodium hexametaphosphate. A blending method is employed to prepare the environment-friendly aqueous nano transparent UV shielding coating. The method is as below: taking a certain amount of an acrylic modified aqueous polyurethaneemulsion E-106 and adding 0.1% of nano TiO2 mixed aqueous dispersion with stirring; stirring evenly with a high speed mixer with a stirring speed of 1000 r / min for 1 h; adding a nano antibacterial powder during the stirring process; then adding an appropriate amount of aqueous additives including a defoaming agent and a leveling agent; and mixing evenly to obtain the environment-friendly aqueous nano transparent heat insulation coating. The invention has the following advantages: improvement of the surface hardness of the UV coating, improvement of aging resistance of the UV coating, prevention from yellowing and no environmental pollution.
Description
technical field [0001] The invention relates to a coating, in particular to an environment-friendly water-based nano transparent ultraviolet shielding coating for high-gloss furniture, and also relates to a preparation method of the coating. Background technique [0002] Nanoparticles are favored by countries all over the world because of their novel and unique properties. It has developed rapidly in the past ten years. A series of multi-functional and high-performance nano-composite coatings can be prepared through proper matching of nanomaterials with different functions and a wide variety of polymers. It is widely used in many fields such as construction, wood and automotive coatings. [0003] UV coatings have little environmental pollution, fast curing speed and energy saving. Unlike traditional coatings, which are volatile and slow to cure, UV coatings have become a major substitute for traditional coatings in recent years. Our company through the nanomaterials ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More