A high-solid, high-volume, environment-friendly bright white finish paint for woodware

A high solid content, environmentally friendly technology, applied in the field of paint, can solve the problems of high substrate treatment requirements, general fullness, and low solid content in construction, and achieve the effects of saving labor costs, shortening working hours, and improving poor yellowing resistance

Active Publication Date: 2016-02-24
CHENGDU ZHANCHEN PAINT
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a high-solid-content, high-volume, environmentally-friendly bright white topcoat for wood, which solves the problem of low solid content in the construction of ordinary high-fullness PU bright white topcoats on the market, serious environmental pollution, and high requirements for substrate treatment. Relatively general disadvantages of fullness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Component A: 15 parts of bisphenol A epoxy resin with epoxy equivalent of 180-190ep / g, 35 parts of hydrogenated bisphenol A epoxy resin with epoxy equivalent of 235-260ep / g, active solvent butyl glycidol 8 parts of ether, 10 parts of titanium dioxide, 25 parts of inorganic filler barium sulfate, 0.5 parts of anti-sedimentation agent silicon dioxide, 1 part of mixture of electrically neutral polycarboxylate ammonium salt and modified polysiloxane as dispersant, defoamer 0.1 part of foam-breaking polysiloxane liquid, the leveling agent is polyacrylate compound and modified polysiloxane compound, wherein, 1 part of polyacrylate compound, 0.5 part of modified polysiloxane compound, anti-yellowing The variable aids are ultraviolet absorbers and composite antioxidants, wherein, 0.5 parts of ultraviolet absorbers and 0.5 parts of composite antioxidants;

[0027] B component: modified alicyclic amine curing agent;

[0028] Component C: 50 parts each of acetone and butanone.

...

Embodiment 2

[0032] Component A: 25 parts of bisphenol A epoxy resin with epoxy equivalent of 180-190ep / g, 25 parts of hydrogenated bisphenol A epoxy resin with epoxy equivalent of 235-260ep / g, active solvent butyl glycidol 12 parts of ether, 5 parts of titanium dioxide, 35 parts of inorganic filler barium sulfate, 1 part of anti-sedimentation agent silicon dioxide, 0.5 parts of mixture of electrically neutral polycarboxylate ammonium salt and modified polysiloxane as dispersant, defoamer 0.5 parts of polysiloxane liquid for breaking bubbles, the leveling agent is polyacrylate compound and modified polysiloxane compound, wherein, 0.5 part of polyacrylate compound, 0.1 part of modified polysiloxane compound, anti-yellowing The variable aid is an ultraviolet absorber and a composite antioxidant, wherein, 1 part of the ultraviolet absorber and 1 part of the composite antioxidant;

[0033] B component: modified alicyclic amine curing agent;

[0034] Component C: 50 parts each of diluent aceto...

Embodiment 3

[0039] Component A: 20 parts of bisphenol A epoxy resin, 30 parts of hydrogenated bisphenol A epoxy resin, 10 parts of active solvent butyl glycidyl ether, 8 parts of titanium dioxide, 30 parts of inorganic filler barium sulfate, anti-settling agent II 0.8 parts of silicon oxide, 0.8 parts of a mixture of electrically neutral polycarboxylate ammonium salt and modified polysiloxane as a dispersant, 0.3 parts of a foam-breaking polysiloxane liquid as a defoamer, and a leveling agent of polyacrylate compounds and Modified polysiloxane compound, wherein, 0.8 parts of polyacrylate compounds, 0.3 parts of modified polysiloxane compounds, anti-yellowing additives are ultraviolet absorbers and composite antioxidants, wherein, ultraviolet absorbers 0.8 part, 0.7 part of compound antioxidant;

[0040] B component: modified alicyclic amine curing agent;

[0041] Component C: 50 parts each of diluent acetone and butanone.

[0042] Production process: put the resin in → add butyl glycidy...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tack-free timeaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses environment-friendly type bright white finish with high solid content and high fullness for woodware. The environment-friendly type bright white finish comprises the following components in parts by weight: components A: 15-25 parts of bisphenol A epoxy resin, 25-35 parts of hydrogenated bisphenol A epoxy resin, 8-12 parts of active flux butyl glycidyl ether, 5-10 parts of titanium dioxide, 25-35 parts of inorganic fillers, 0.5-1 part of an anti-settling agent, 0.5-1 part of a dispersing agent, 0.1-0.5 part of an antifoaming agent, 0.6-1.5 parts of a flatting agent, 1-2 parts of anti-yellowing auxiliaries; component B: modified alicyclic amine curing agent; component C: ketones solvent, wherein the weight ratio of the components A:component B:component C is 100:(30-35):(5-8). The environment-friendly type bright white finish with high solid content and high fullness for woodware, disclosed by the invention, saves labor cost and shortens working hours; moreover, construction solid content (greater than 90%) is far higher than that (50%-55%) of the common polyurethane bright white finish. Moreover, requirements of paint with ultrahigh solid content are achieved, and pollution to environment caused by volatilization of an organic solvent is reduced.

Description

technical field [0001] The invention belongs to the field of paints, and in particular relates to a high-solid-content, high-volume, environment-friendly bright white finish for woodware. Background technique [0002] For a long time, in the furniture market, polyurethane bright white finish occupies a large market share. The painting process of general furniture factories is to spray the PU white topcoat after the PE white primer is dried and polished. Through market research, it is found that the traditional high-fullness PU bright white finish paint has low solid content (generally between 50% and 55%), and has high requirements for the treatment of PE substrates. At least 600 mesh sandpaper can barely cover the sand. marks, still unsatisfactory. Contents of the invention [0003] The purpose of the present invention is to provide a high-solid-content, high-volume, environmentally-friendly bright white topcoat for wood, which solves the problem of low solid content in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/02C09D7/12
Inventor 陈建群雷利
Owner CHENGDU ZHANCHEN PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com