Thermal insulation waterproof daub and preparation method thereof

A technology of waterproof glue and antifungal agent, which is applied in the field of architectural coatings, can solve the problems of large amount of cementing materials, etc., and achieve the effects of short construction period, good flexibility, and good thermal insulation performance

Active Publication Date: 2014-02-05
MAANSHAN TIANJINYUN PAINT IND
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this way, the amount of cementing material should be large enough, otherwise its

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermal insulation waterproof daub and preparation method thereof
  • Thermal insulation waterproof daub and preparation method thereof
  • Thermal insulation waterproof daub and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Add 40% of sodium silicate aqueous solution, 0.1% of antifungal agent, 0.8% of dispersant, 0.5% of ester alcohol and 0.2% of functional fiber into the formula with 13% of styrene-acrylic emulsion, 0.1% of coupling agent and 0.1% of wetting agent In the mixing tank of the mixed liquid, start the agitator, and add thickener 0.2% after mixing for 2 hours at a stirring speed of 120r / min;

[0019] Add 15% of hollow vitrified microspheres, 5% of aluminum silicate, 10.5% of pottery sand, 10% of building glue and 4.5% of polyphenylene particles at a stirring speed of 50r / min and stir for 1 hour to obtain a mixture, which is thermal insulation and waterproof Clay, PH value is 8.5.

Embodiment 2

[0021] Add 25.2% of sodium silicate aqueous solution, 0.5% of antifungal agent, 0.6% of dispersant, 0.8% of ester alcohol and 0.5% of functional fiber into the formula with 14% of styrene-acrylic emulsion, 0.4% of coupling agent and 0.6% of wetting agent In the mixing tank of the mixed solution, start the agitator, and add thickener 0.4% after mixing for 2.5 hours at a stirring speed of 130r / min;

[0022] Add 5% of hollow vitrified microspheres, 10% of aluminum silicate, 32% of pottery sand, 5% of construction glue and 5% of polyphenylene particles at a stirring speed of 55 r / min and stir for 1.5 hours to obtain a mixture, namely Thermal insulation and waterproof cement, PH value is 9.

Embodiment 3

[0024] Add 20% of sodium silicate aqueous solution, 0.9% of antifungal agent, 0.2% of dispersant, 1% of ester alcohol and 0.9% of functional fiber into the formula with 19% of styrene-acrylic emulsion, 0.7% of coupling agent and 0.9% of wetting agent In the mixing tank of the mixed liquid, start the agitator, at the stirring speed of 125r / min, add 0.8% thickener after mixing for 3 hours.

[0025] Add 20% hollow vitrified microspheres, 15% aluminum silicate, 13.1% pottery sand, 6.0% construction glue and 1.5% polyphenylene particles into the mixture at a stirring speed of 60 r / min and stir for 2 hours to obtain a mixture, that is, heat preservation Waterproof cement, PH value is 10.

[0026] 1. The effect of the amount of styrene-acrylic emulsion on the performance of thermal insulation and waterproof cement.

[0027] Styrene-acrylic emulsion is the basic cementing substance of thermal insulation and waterproof mastic, and it is the source of the strength of thermal insulation...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Compressive shear bond strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a thermal insulation waterproof daub and a preparation method thereof. The preparation method comprises the following steps of putting sodium silicate aqueous solution, a mildew preventive, a dispersing agent, an ester alcohol and functional fiber into a mixing tank with mixed liquor of styrene-acrylic emulsion, a coupling reagent and a wetting agent; starting a stirrer, wherein the stirring speed is 120-130r/min; after mixing for 2-3 hours, adding a thickener; adding hollow vitrified microbeads or hollow glass microbeads, aluminium silicate, ceramic sand, glue for building and polyphenyl granule while stirring at 50-60r/min, and stirring for 1-2 hours to obtain the thermal insulation waterproof daub. The thermal insulation waterproof daub has low density and good heat insulation performance, is paste, and can be directly used in site construction without any pretreatment measures such as adding water and stirring; the daub can form an integral thermal insulation layer on the surface of a wall and can be firmly combined with the surface of the wall, and no cavities exist between the thermal insulation layer and a wall body base layer; the formed external thermal insulation system of an exterior wall has a simple structure, is convenient to construct, and has short construction period and low expenses of labor.

Description

technical field [0001] The invention belongs to the field of architectural coatings, more specifically, the invention relates to a thermal insulation and waterproof cement and a preparation method thereof. Background technique [0002] In recent years, architectural reflective and heat-insulating coatings have been widely used as a new type of functional architectural coating in hot summer and warm winter, hot summer and cold winter regions. In hot summer and cold winter regions, on the exterior walls of some special buildings, such as energy-saving blocks (such as concrete blocks with core-hole insulation boards, aerated concrete blocks, etc.) that do not require external wall insulation systems, their matching The application of thermal insulation putty forms a building reflective thermal insulation coating-thermal insulation putty system, which can not only meet the requirements of building energy-saving design, but also play the role of reducing wall surface temperature...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/26
Inventor 蒋字平唐翠红
Owner MAANSHAN TIANJINYUN PAINT IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap